A pollution-repellent and anti-corrosion steel wrist arm positioning device and processing method for catenary

A positioning device and processing method technology, applied in anti-corrosion coatings, hot-dip coating process, metal material coating process, etc., can solve the problems of no coating technology and products, affecting the electrical conductivity of catenary, and achieve excellent salt spray resistance Corrosion, improved corrosion resistance and service life, high hardness effect

Active Publication Date: 2022-03-08
CHINA RAILWAY SIYUAN SURVEY & DESIGN GRP
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, conventional dirt-repellent coatings are mainly organic silicon, organic fluorosilicon and fluorocarbon coatings, which have certain insulation properties. The use of these coatings in catenary components will affect the electrical conductivity of the catenary, and are suitable for high-speed rail contact The dirt-repellent coating required for the use of grid components must also have electrical conductivity, and there is no related coating technology and product at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A pollution-repellent and anti-corrosion steel wrist arm positioning device and processing method for catenary
  • A pollution-repellent and anti-corrosion steel wrist arm positioning device and processing method for catenary

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] Formula components by mass, take by weighing 10 parts of film-forming resin (organosilicon modified bisphenol A epoxy resin SM-60), 55 parts of organosilicon monomer (methyltriethoxysilane), crosslinking agent ( Tetraethyl silicate) 0.5 parts, interface adhesive (aminopropyltriethoxysilane) 5 parts, catalyst (dibutyltin dilaurate) 0.1 part, conductive filler (1 μm flake aluminum powder) 30 parts, 1 part of corrosion inhibitor passivation agent (sodium molybdate), 0.2 part of orientation agent (polyvinylpyrrolidone), 3-6 parts of anti-sedimentation agent (organic bentonite), 10 parts of solvent (6 parts of ethanol, 4 parts of propylene glycol methyl ether) 0.3 part, 0.3 part of defoamer (Defom 8700), 5 parts of pigment and filler (iron oxide red), after mixing and stirring evenly, grind in a sand mill until the fineness is about 25 μm, that is, to obtain the contact net component Anti-corrosion conductive and foul-repellent coating.

Embodiment 2

[0079] Formula components by mass, weigh 20 parts of film-forming resin (organosilicon modified bisphenol A epoxy resin SM-60), silicone monomer (40 parts of methyltriethoxysilane, methyltrichlorosilane 25 parts) 65 parts, crosslinking agent (methyl orthosilicate) 2.5 parts, interface adhesive (aminopropyltriethoxysilane) 10 parts, catalyst (organobismuth catalyst) 0.3 parts, conductive filler (1μm sheet aluminum powder) 60 parts, corrosion inhibitor passivation agent (cerium nitrate) 3 parts, orientation agent (polyvinylpyrrolidone) 0.4 parts, anti-settling agent (organic bentonite) 6 parts, solvent (12 parts ethanol, propylene glycol methyl ether 8 parts) 20 parts, 0.8 parts of defoamer (Defom 8700), 20 parts of pigments and fillers (red iron oxide), after mixing and stirring evenly, grind in a sand mill until the fineness is about 25 μm, that is, the described Corrosion-resistant, conductive, and foul-repellent coatings for catenary components.

Embodiment 3

[0081] Formula components by mass, weigh 15 parts of film-forming resin (organosilicon modified bisphenol A epoxy resin SM-60), silicone monomer (40 parts of methyl triethoxysilane, dimethyl dichloride 15 parts of silane) 55 parts, 1.5 parts of crosslinking agent (tetraethyl orthosilicate), 8 parts of interface adhesive (aminopropyltriethoxysilane), 0.2 parts of catalyst (dibutyltin dilaurate), conductive 50 parts of filler (1μm flake aluminum powder), 2 parts of corrosion inhibitor and passivation agent (cerium nitrate), 0.3 parts of orientation agent (polyvinylpyrrolidone), 4 parts of anti-settling agent (organic bentonite), solvent (8 parts of ethanol , 7 parts of propylene glycol methyl ether) 15 parts, defoamer (Defom 8700) 0.6 part, pigment and filler (iron oxide red) 15 parts, after mixing and stirring evenly, grind in a sand mill until the fineness is about 25 μm, that is The anti-corrosion conductive dirt-repellent paint for the catenary assembly is obtained.

[0082...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dirt-repellent and anti-corrosion-type steel wrist arm positioning device and a processing method for contact nets. The surface is coated with a dirt-repelling composite coating, and the dirt-repelling composite coating is an anti-corrosion conductive dirt-repelling paint. On the premise of not affecting the surface conductivity of catenary components, a coating with fouling function is prepared on hot-dip galvanized or GalFan alloy anti-corrosion coating, which reduces the deposition of corrosive pollutants on the surface of catenary components in the tunnel and improves The overall anti-corrosion performance and service life of the steel wrist arm positioning device are guaranteed.

Description

technical field [0001] The invention belongs to the field of steel wrist arms of electrified railway catenary, and in particular relates to a positioning device and a processing method for a dirt-repellent and anti-corrosion steel wrist arm of an catenary. Background technique [0002] Rail transit High-speed railway is an important part of my country's transportation hub, most of which pass through eastern coastal cities, and harsh environmental conditions such as offshore ocean salt spray, heavily polluted industrial atmosphere, dust, etc. higher requirements. In particular, the steel wrist arm positioning device is a very important component in the electrification facilities of the high-speed rail. The corrosion of salt spray and adhered dirt directly affects the operation safety and operating cost of the high-speed rail. [0003] Traditional steel wrist arm positioning devices often use anodic oxidation and hot-dip galvanizing to prepare anti-corrosion coatings on the su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/02C09D5/10C09D5/24C09D7/61C09D7/62C09D7/63C09D7/65C09D7/20C23C2/04C23C2/06
CPCC09D163/00C09D5/103C09D5/24C09D7/61C09D7/62C09D7/63C09D7/65C09D7/20C23C2/04C23C2/06C08K2003/0812C08K2201/001C08K13/06C08K7/00C08K3/08C08K5/5419C08K5/544C08K3/346
Inventor 石瑞霞李红梅陈同舟汪洋方志国戚广枫吕青松冯增辉耿肖
Owner CHINA RAILWAY SIYUAN SURVEY & DESIGN GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com