A kind of method for making leather without tanning agent

A technology of tanning agent and polar organic solvent, applied in the field of leather making, can solve the problems of non-recyclability, unfavorable industrialization, solvent discharge, etc., and achieve the effects of improving the efficiency of tanning, reducing the cost of tanning, and shortening the tanning time.

Active Publication Date: 2022-03-01
SICHUAN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, polar organic solvents after dehydration have a high water content and cannot be reused for dehydration of pelts, thus causing problems of low solvent utilization and solvent emissions
On the other hand, the existing tanning agent-free tanning technology uses in-situ hydrolysis to enhance the surface roughness of dehydrated hides to achieve hydrophobic treatment. This technology requires accurate control of the degree of in-situ hydrolysis, which is not conducive to industrialization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for making leather without tanning agent
  • A kind of method for making leather without tanning agent
  • A kind of method for making leather without tanning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Tanning-free tanning:

[0046] Dehydrate the bare hide (cowhide) in absolute ethanol (6.0 times the weight of the bare hide) for 90 minutes, add molecular sieve activation powder (3A) (3.5 times the weight of the bare hide) and dehydrate for 120 minutes to obtain the dehydrated hide. Adopt Karl Fischer method to measure its moisture content to be 2.95%;

[0047] Dry the dehydrated skin to obtain the skin base, and the softness of the skin base measured according to GB / T 39371-2020 is 4.69 mm, as shown in Table 3;

[0048] Weigh silicon dioxide (10% of the weight of the skin) and disperse it in absolute ethanol (10 times the weight of the skin) to form a suspension, then filter the above suspension onto the surface of the skin, dry it and place Soak in 10 wt% PDMS solution (8.0 times the weight of the skin) for 5.0 min to complete the hydrophobic treatment;

[0049] Tanning agent-free leather is obtained after drying the above-mentioned skin base that has completed the...

Embodiment 2

[0061] The molecular sieve recovered in Example 1 and ethanol are used to form a molecular sieve-polar organic solvent composite dehydration medium for reuse in the tanning agent-free tanning of this embodiment:

[0062] Put the bare hide (cowhide) into recovered ethanol (6.0 times the weight of the bare hide) for dehydration for 90 minutes, add the recovered molecular sieve activation powder (3A) (3.5 times the weight of the bare hide) and dehydrate for 120 minutes to obtain dehydrated Skin, adopting Karl Fischer method to measure its water content is 3.24%;

[0063] Dry the dehydrated skin to obtain the skin base, and measure the softness of the skin base to be 4.52 mm, as shown in Table 3;

[0064] Weigh silicon dioxide (10% of the weight of the skin) and disperse it in absolute ethanol (10 times the weight of the skin) to form a suspension, then filter the above suspension onto the surface of the skin, dry it and place Soak in 10 wt% PDMS solution (8.0 times the weight of...

Embodiment 3

[0069] Dehydrate the bare hide (cowhide) in absolute ethanol (4.0 times the weight of the bare hide) for 60 minutes, add molecular sieve activation powder (3A) (2.0 times the weight of the bare hide) and dehydrate for 60 minutes to obtain the dehydrated hide. Adopt Karl Fischer method to measure its moisture content to be 3.48%;

[0070] Drying the dehydrated skin to obtain the skin base;

[0071] Weigh titanium dioxide (8.0% of the weight of the skin) and disperse it in absolute ethanol (12 times the weight of the skin) to form a suspension, then filter the above suspension onto the surface of the skin, dry it and place it at 10 Soak in wt% PDMS solution (5.0 times the weight of the skin) for 30 minutes to complete the hydrophobic treatment;

[0072] The leather without tanning agent was dried after the hydrophobic treatment was completed. The mechanical performance parameters of the tanning agent-free leather prepared in this example are shown in Table 2, the tear force is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softnessaaaaaaaaaa
pore sizeaaaaaaaaaa
tear loadaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of leather making and discloses a method for making leather without tanning agents. First, the bare hide is dehydrated in a controlled manner using a molecular sieve-polar organic solvent composite dehydration medium. Subsequently, tanning agent-free leather is produced by increasing the surface roughness of the hide and reducing its surface energy. The present invention does not use any metal or non-metallic tanning agent, and has the advantage of being environmentally friendly; the present invention breaks the distribution balance of moisture between the bare hide and the polar organic solvent, and realizes the "from raw hide to polar organic solvent" for the moisture in the bare hide. Solvents, and then from polar organic solvents to molecular sieves" multi-media self-driven directional controllable dehydration, promotes continuous and controllable removal of moisture in raw hides, effectively solves the problem of low dehydration efficiency when pure polar organic solvents dehydrate bare hides, Many bath changes are required for dehydration, organic waste liquid is difficult to reuse, etc., and the molecular sieve-polar organic solvent dehydration system is easy to recover and can be used for multiple cycles for controllable dehydration of bare leather, providing a new clean system leather technology.

Description

technical field [0001] The invention relates to the technical field of leather making, in particular to a method for making leather without tanning agents. Background technique [0002] Chrome tanning has always been dominant in the tanning industry (Yao Q, Chen H, Jiao Q, et al. Hydroxyl‐Terminated Dendrimer Acting as a High Exhaustion Agent for ChromeTanning[J]. ChemistrySelect, 2018, 3(4): 1032-1039. Ding W, Cheng Y, Wang Y, et al. Chrome-reduced combination tanning for cleaner dyed sheep furprocessing[J]. Journal of the American Leather Chemists Association, 2015,110(11): 363-371.) . However, chrome tanning requires the use of large amounts of chromium salts, sulfates, and chlorides. At the same time, trivalent chromium Cr(Ⅲ) has the risk of being oxidized to hexavalent chromium Cr(Ⅵ) during neutralization, fatliquoring, dyeing and other post-tanning processes and storage (Tang Y, Zhou J, Zeng Y, et al. Effect of leather chemicals on Cr(III) removal from post tanning ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C14C1/00C14B1/58C14C9/00
CPCC14C1/00C14B1/58C14C9/00C14C11/003C14C13/00C14C9/02C09D183/04
Inventor 黄鑫黄亚文石碧
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap