Biodegradable packaging material and preparation method thereof

A technology of biodegradable and packaging materials, applied in the field of biodegradable packaging materials and its preparation, can solve problems such as pollution, endangering human survival and health, and endangering the environment, achieving high decomposition rate, increasing hydrophobicity, and improving environmental protection Effect

Inactive Publication Date: 2021-10-01
YUYAO SUN RAIN SPRAYER
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Synthetic polymer materials have the advantages of light weight, high strength, good chemical stability, and low price. However, while synthetic polymer materials bring convenience to people's lives and improve the quality of life, a large amount of waste after use is also increasing day by day. , becoming a source of white pollution, seriously endangering the environment, causing groundwater and soil pollution, endangering human survival and health, and causing negative impacts that cannot be ignored on the environment on which human beings depend, and biodegradable materials are an effective way to solve this problem , so a biodegradable packaging material and its preparation method are proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A biodegradable packaging material, comprising the following preparation method steps:

[0027] S1, prepare 20-40 parts of starch, 15-25 parts of cellulose, 15-25 parts of chitin, 10-20 parts of protein, 2-6 parts of polyvinyl alcohol, 1-3 parts of polymerizing agent, and 2-4 parts of plasticizer 3-5 parts of biodegradable additives;

[0028] S2, carry out superfine pulverization of starch, blend polyvinyl alcohol with starch, add a small amount of solubilizer, improve the uniformity of starch dispersion; deacetylate chitin under alkaline adjustment to generate chitosan; chitosan Acetic acid aqueous solution, polyvinyl alcohol aqueous solution, and plasticizer are mixed according to a certain ratio to make a mixture;

[0029] S3, the cellulose is chemically modified to make methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose, from methyl cellulose, hydroxypropyl methyl cellulose , cellulose ether film made from water o...

Embodiment 1

[0033] Embodiment 1: Prepare 20 parts of starch, 15 parts of cellulose, 15 parts of chitin, 10 parts of protein, 2 parts of polyvinyl alcohol, 1 part of polymerization agent, 2 parts of plasticizer, 3 parts of biodegradation additive; Micro-grinding, blending polyvinyl alcohol and starch, adding a small amount of solubilizer to improve the uniformity of starch dispersion; deacetylating chitin under alkaline adjustment to generate chitosan; mixing chitosan with acetic acid aqueous solution, polyethylene Alcohol aqueous solution and plasticizer are mixed according to a certain ratio to make a mixture; the cellulose is chemically modified to make methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose, Cellulose ether films prepared from aqueous or hydroalcoholic solutions of methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose; polymerizing the resulting mixture with cellulose ether fil...

Embodiment 2

[0034] Embodiment 2: Prepare 30 parts of starch, 20 parts of cellulose, 20 parts of chitin, 15 parts of protein, 4 parts of polyvinyl alcohol, 2 parts of polymerization agent, 3 parts of plasticizer, 4 parts of biodegradation additive; Micro-grinding, blending polyvinyl alcohol and starch, adding a small amount of solubilizer to improve the uniformity of starch dispersion; deacetylating chitin under alkaline adjustment to generate chitosan; mixing chitosan with acetic acid aqueous solution, polyethylene Alcohol aqueous solution and plasticizer are mixed according to a certain ratio to make a mixture; the cellulose is chemically modified to make methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose, Cellulose ether films prepared from aqueous or hydroalcoholic solutions of methyl cellulose, hydroxypropyl methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose; polymerizing the resulting mixture with cellulose ether fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of packaging materials, in particular to a biodegradable packaging material and a preparation method thereof. The biodegradable packaging material is prepared from starch, cellulose, chitin, protein, polyvinyl alcohol, a polymerizing agent, a plasticizer and a biodegradable additive; the material is prepared from the following components in parts by weight: 20-40 parts of starch, 15-25 parts of cellulose, 15-25 parts of chitin, 10-20 parts of protein, 2-6 parts of polyvinyl alcohol, 1-3 parts of a polymerizing agent, 2-4 parts of a plasticizer and 3-5 parts of a biodegradable additive. The material is good in hydrophobic capacity, oil resistance, water resistance and high temperature resistance, and has the excellent properties of proper strength, grease resistance, flexibility, transparency, odorlessness, odorlessness, easiness in degradation, and has the good film forming characteristic; The biodegradable packaging material is high in decomposition rate, can realize biodegradation, improves environmental protection, and has better biodegradation characteristics.

Description

technical field [0001] The invention relates to the technical field of packaging materials, in particular to a biodegradable packaging material and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of the economy, people's pursuit of material and spirit is getting higher and higher, and there are correspondingly higher requirements for product packaging. When people buy products, they not only look at the aesthetics of the outer packaging, but also Consider other miscellaneous functions. It is precisely because people's pursuit of product packaging continues to improve that many new packaging materials are constantly being applied to product packaging. [0003] Synthetic polymer materials have the advantages of light weight, high strength, good chemical stability, and low price. However, while synthetic polymer materials bring convenience to people's lives and improve the quality of life, a large amount of waste after us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/02C08L1/28C08L5/08C08L89/00C08L29/04C08K5/053C08J5/18
CPCC08J5/18C08J2303/02C08J2401/28C08J2405/08C08J2489/00C08J2429/04C08K5/053
Inventor 毛寅
Owner YUYAO SUN RAIN SPRAYER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products