Preparation method of large biological water-based paint

A water-based paint and biological technology, applied in the paint field, can solve the problems of poor salt water corrosion resistance, poor wear resistance, poor adhesion, etc., and achieve good antibacterial effect

Pending Publication Date: 2021-10-15
BYHERB BIGBIO TECH QINGDAO CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The water-based paint of this patent has certain solvent resistance and corrosion resistance, but does not have good impact resistance and adhesion, and does not have antibacterial properties at the same time
[0006] CN110218497A discloses a corrosion-resistant water-based paint and its preparation process, which solves the problem that the overall application effect of the water-based paint is poor due to its poor salt water corrosion resistance, and has good salt water corrosion resistance
[0008] (1) No bacteriostasis;
[0009] (2) poor wear resistance;
[0010] (3) Poor impact resistance;
[0011] (4) poor adhesion;
[0012] (5) Poor salt resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1 A kind of preparation method of large biological water-based paint

[0048] Include the following steps:

[0049] (1) Preparation of Cyclodextrin Solution Containing Plant Extract

[0050] Mix ethylene glycol with water, add cyclodextrin and mix evenly, then add plant extract powder, carry out ultrasonic dispersion at 100Hz for 40min, and stir at 50°C for 30min at 1200r / min after ultrasonic to make it fully combined. Obtain the cyclodextrin solution containing plant extract;

[0051] The plant extract powder is wormwood extract powder;

[0052] The cyclodextrin solution containing plant extracts comprises the following components in parts by mass: 2 parts of ethylene glycol, 5 parts of water, 1 part of cyclodextrin, and 1.5 parts of plant extract powder.

[0053] (2) Preparation of cellulose mixture

[0054] Deionized water was added to triethoxysilane and carboxymethyl cellulose to mix, and then stirred at a stirring speed of 700r / min, a stirring time ...

Embodiment 2

[0073] Embodiment 2 A kind of preparation method of large biological water-based paint

[0074] Include the following steps:

[0075] (1) Preparation of Cyclodextrin Solution Containing Plant Extract

[0076] Mix ethylene glycol with water, add cyclodextrin and mix evenly, then add plant extract powder, carry out ultrasonic dispersion at 80 Hz for 50 min, and then stir at 45°C for 40 min at 1000 r / min to make it fully combined. Obtain the cyclodextrin solution containing plant extract;

[0077] The plant extract powder includes wormwood extract powder and Panax notoginseng extract powder, the mass ratio of which is 1:1;

[0078] The cyclodextrin solution containing plant extracts comprises the following components in parts by mass: 1.5 parts of ethylene glycol, 4 parts of water, 1 part of cyclodextrin, and 1 part of plant extract powder.

[0079] (2) Preparation of cellulose mixture

[0080] Deionized water was added to triethoxysilane and carboxymethyl cellulose to mix, a...

Embodiment 3

[0099] Embodiment 3 A kind of preparation method of large biological water-based paint

[0100] Include the following steps:

[0101] (1) Preparation of Cyclodextrin Solution Containing Plant Extract

[0102] Mix ethylene glycol with water, add cyclodextrin and mix evenly, then add plant extract powder, carry out ultrasonic dispersion at 120Hz for 30min, and stir at 60°C at 1400r / min for 25min after ultrasonication to make it fully combined. Obtain the cyclodextrin solution containing plant extract;

[0103] The plant extract powder includes wormwood extract powder, Panax notoginseng extract powder, tea extract powder, and its mass ratio is 1:1:1;

[0104] The cyclodextrin solution containing plant extracts comprises the following components in parts by mass: 3 parts of ethylene glycol, 6 parts of water, 2 parts of cyclodextrin, and 2 parts of plant extract powder.

[0105] (2) Preparation of cellulose mixture

[0106] Deionized water was added to triethoxysilane and carbo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact resistanceaaaaaaaaaa
Impact resistanceaaaaaaaaaa
Impact resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a large biological water-based paint. The preparation method comprises the following steps: preparing a cyclodextrin solution containing a plant extract, preparing a cellulose mixture, and preparing the water-based paint. According to the large biological water-based paint prepared by the invention, plant active ingredients are added, so that the large biological water-based paint has good antibacterial activity, and the inhibition rate on staphylococcus aureus is 95.7-96.2%, the inhibition rate on escherichia coli is 96.2-96.9%, the inhibition rate on pseudomonas aeruginosa is 92.5-93.1%, and the inhibition rate on candida albicans is 92.9-94.3%; the paint has high wear resistance, and the hardness can reach 2H when the paint is sprayed on a steel plate; and when the paint is sprayed on a steel plate, the impact resistance of the paint is 73-76cm.

Description

technical field [0001] The invention designs a method for preparing a large biological water-based paint, which belongs to the technical field of paint materials. Background technique [0002] Due to its strong hardness, high fullness of paint film, and tolerant construction, paint is the first choice of paint for many people's decoration. With the pressure of environmental protection policies, consumers' awareness of environmental protection is constantly improving. In particular, provinces and cities across the country have introduced VOC emission limit standards to encourage the use of non-solvent-based coatings, which has brought opportunities for the development of water-based paints and other environmentally friendly coatings. Although traditional coatings still occupy a relatively large market share, water-based paints are a green industry and the future development direction of paints. Domestic leading water-based paint companies are on the rise. [0003] It is an i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04C09D5/14C09D7/61C09D7/65C09D7/63
CPCC09D133/04C09D5/14C09D7/61C09D7/65C09D7/63C08K2201/011C08K2003/2227C08L1/286C08L5/16C08K3/22C08K3/36C08K5/00
Inventor 黄效华汪培育王爽原秀燕
Owner BYHERB BIGBIO TECH QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com