Wear-resistant anti-puncture fabric and processing technology thereof

A processing technology and anti-puncture technology, applied in textiles and papermaking, etc., to achieve the effects of reduced production costs, excellent heat resistance, and high mechanical strength

Inactive Publication Date: 2021-10-22
东台市东驰服装有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Polyester fabrics are widely used, have excellent wrinkle resistance and shape retention, have certain mechanical strength, elastic recovery ability, thermoplasticity and stability, and have low production costs, so they are favored by people. However, polyester fabrics also have certain Therefore, it is particularly important to invent a wear-resistant and puncture-resistant fabric and its processing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wear-resistant anti-puncture fabric and processing technology thereof
  • Wear-resistant anti-puncture fabric and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A wear-resistant and puncture-resistant fabric, comprising a polyester base cloth, the surface of the polyester base cloth is provided with a puncture-resistant layer, and the surface of the puncture-resistant layer is coated with a wear-resistant paint;

[0040] The anti-puncture layer is woven from ultra-high molecular weight polyethylene fibers.

[0041] The wear-resistant coating is made of the following raw materials in parts by weight: 50 parts of modified epoxy resin, 5 parts of curing agent, 6 parts of plasticizer, and 3 parts of diluent.

[0042] The modified epoxy resin is made of E40 epoxy resin, ethyl orthosilicate, ethanol, ethyl acetate and catalyst.

[0043] The curing agent is polyamide resin.

[0044] The plasticizer is made from terephthalic acid, isooctyl alcohol and dodecylbenzenesulfonic acid.

[0045] A processing technology for wear-resistant and puncture-resistant fabrics, the steps are as follows,

[0046] S1, the preparation of plasticizer: ...

Embodiment 2

[0056] A wear-resistant and puncture-resistant fabric, comprising a polyester base cloth, the surface of the polyester base cloth is provided with a puncture-resistant layer, and the surface of the puncture-resistant layer is coated with a wear-resistant paint;

[0057] The anti-puncture layer is woven from ultra-high molecular weight polyethylene fibers.

[0058] The wear-resistant coating is made of the following raw materials in parts by weight: 52 parts of modified epoxy resin, 6 parts of curing agent, 6 parts of plasticizer, and 3.5 parts of diluent.

[0059] The modified epoxy resin is made of E40 epoxy resin, ethyl orthosilicate, ethanol, ethyl acetate and catalyst.

[0060] The curing agent is polyamide resin.

[0061] The plasticizer is made from terephthalic acid, isooctyl alcohol and dodecylbenzenesulfonic acid.

[0062] A processing technology for wear-resistant and puncture-resistant fabrics, the steps are as follows,

[0063] S1, the preparation of plasticizer...

Embodiment 3

[0073] A wear-resistant and puncture-resistant fabric, comprising a polyester base cloth, the surface of the polyester base cloth is provided with a puncture-resistant layer, and the surface of the puncture-resistant layer is coated with a wear-resistant paint;

[0074] The anti-puncture layer is woven from ultra-high molecular weight polyethylene fibers.

[0075] The wear-resistant coating is made of the following raw materials in parts by weight: 60 parts of modified epoxy resin, 7 parts of curing agent, 7 parts of plasticizer, and 4 parts of diluent.

[0076] The modified epoxy resin is made of E40 epoxy resin, ethyl orthosilicate, ethanol, ethyl acetate and catalyst.

[0077] The curing agent is polyamide resin.

[0078] The plasticizer is made from terephthalic acid, isooctyl alcohol and dodecylbenzenesulfonic acid.

[0079] A processing technology for wear-resistant and puncture-resistant fabrics, the steps are as follows,

[0080] S1, the preparation of plasticizer: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant anti-puncture fabric and a processing technology thereof. The wear-resistant anti-puncture fabric comprises a polyester base cloth; an anti-puncture layer is arranged on the surface of the polyester base cloth, and the surface of the anti-puncture layer is coated with a wear-resistant coating; the anti-puncture layer is formed by spinning ultra-high molecular weight polyethylene fibers; and the wear-resistant coating is prepared from the following raw materials in parts by weight of 50-60 parts of modified epoxy resin, 5-7 parts of a curing agent, 6-7 parts of a plasticizer and 3-4 parts of a diluent, and the modified epoxy resin is prepared from E40 epoxy resin, tetraethoxysilane, ethanol, ethyl acetate and a catalyst. Compared with the prior art, the polyester fabric is used as the base cloth of the product, the production cost of the product can be reduced, and polyester has excellent wrinkle resistance and shape retention and has certain mechanical strength, elastic recovery capacity, thermoplasticity and stability, so that the polyester is selected as the base cloth, and the effects of the product in various aspects can be improved.

Description

technical field [0001] The invention relates to the technical field of fabric preparation, in particular to a wear-resistant and puncture-resistant fabric and its processing technology. Background technique [0002] Fabric is a commonly used material in life, used to make clothing, etc. With the improvement of people's living standards, fabrics made of various materials have appeared, among which polyester fabrics have a wide range of applications. [0003] Polyester fabrics are widely used, have excellent wrinkle resistance and shape retention, have certain mechanical strength, elastic recovery ability, thermoplasticity and stability, and have low production costs, so they are favored by people. However, polyester fabrics also have certain Therefore, it is particularly important to invent a wear-resistant and puncture-resistant fabric and its processing technology. Contents of the invention [0004] The object of the present invention is to provide a wear-resistant and p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06N3/00D06N3/12C08G59/14
CPCD06N3/0013D06N3/0088D06N3/12C08G59/1438D06N2209/105D06N2201/0281D06N2201/0254
Inventor 李进东朱敏周克华康灵李楚涵朱灵铃
Owner 东台市东驰服装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com