High-ductility quick-setting quick-hardening concrete repairing material

A repairing material and concrete technology, which is applied in the field of building materials, can solve the problems affecting the durability of buildings, poor mortar density and ion erosion resistance, and inability to obtain adhesion, so as to improve the density and ion erosion resistance. , compactness and ion erosion resistance, high early strength effect

Inactive Publication Date: 2021-11-02
ZHENGZHOU SINO SINA BUILDING MATERIALS CO LTD +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a high-ductility rapid-setting rapid-hardening concrete repair material, which has the advantages of good adhesion, good mortar density and ion erosion resistance, and solves the problem of being wet by rain. If it is used in a humid environment such as a sewer, the required adhesiveness cannot be obtained, and the compactness and ion erosion resistance of the mortar are poor, which affects the durability of the building.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: 30 parts of fly ash, 90 parts of quartz sand, 70 parts of water, 1.6 parts of water reducing agent, 20 parts of Portland cement, 5 parts of aluminate cement, 5 parts of dihydrate gypsum and 20 parts of mineral powder, etc. , the fly ash is class I or class F fly ash, the particle size of the quartz sand is not more than 0.4mm, and the water reducer is naphthalene-based water reducer, sulfamate water reducer or polycarboxylate water reducer. Water agent, the water reducing rate is 15%.

[0021] A preparation method for high-ductility rapid-setting rapid-hardening concrete repair material, comprising the following steps:

[0022] (1) take fly ash part, quartz sand part and portland cement part, aluminate cement part, water part and stir and mix;

[0023] (2) Weigh parts of water reducing agent, part of dihydrate gypsum and mineral powder, add into the mixed cement, stir and mix evenly to obtain concrete repair material.

[0024] The high-ductility rapid-setti...

Embodiment 2

[0025] Example 2: 80 parts of fly ash, 140 parts of quartz sand, 120 parts of water, 2.4 parts of water reducer, 80 parts of Portland cement, 20 parts of aluminate cement, 25 parts of dihydrate gypsum and 80 parts of mineral powder, etc. , the fly ash is class I or class F fly ash, the particle size of the quartz sand is not more than 0.4mm, and the water reducer is naphthalene-based water reducer, sulfamate water reducer or polycarboxylate water reducer. Water agent, the water reducing rate is 35%.

[0026] A preparation method for high-ductility rapid-setting rapid-hardening concrete repair material, comprising the following steps:

[0027] (1) take fly ash part, quartz sand part and portland cement part, aluminate cement part, water part and stir and mix;

[0028] (2) Weigh parts of water reducing agent, part of dihydrate gypsum and mineral powder, add into the mixed cement, stir and mix evenly to obtain concrete repair material.

[0029] The high-ductility rapid-setting ...

Embodiment 3

[0030] Example 3: 55 parts of fly ash, 115 parts of quartz sand, 95 parts of water, 2 parts of water reducer, 50 parts of Portland cement, 12.5 parts of aluminate cement, 15 parts of dihydrate gypsum and 12.5 parts of mineral powder, etc. , the fly ash is class I or class F fly ash, the particle size of the quartz sand is not more than 0.4mm, and the water reducer is naphthalene-based water reducer, sulfamate water reducer or polycarboxylate water reducer. Water agent, the water reducing rate is 25%.

[0031] A preparation method for high-ductility rapid-setting rapid-hardening concrete repair material, comprising the following steps:

[0032] (1) take fly ash part, quartz sand part and portland cement part, aluminate cement part, water part and stir and mix;

[0033] (2) Weigh parts of water reducing agent, part of dihydrate gypsum and mineral powder, add into the mixed cement, stir and mix evenly to obtain concrete repair material.

[0034] The high-ductility fast-setting ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of building materials, and discloses a high-ductility quick-setting quick-hardening concrete repairing material. The material is prepared from the following raw materials in parts by weight: 30 to 80 parts of fly ash, 90 to 140 parts of quartz sand and 70 to 120 parts of water. According to the high-ductility quick-setting quick-hardening concrete repairing material, by adding Portland cement, aluminate cement and dihydrate gypsum, a large amount of ettringite and hydrated calcium aluminate can be generated in the early melting stage of water, so high early strength can be obtained; the ettringite contains a large amount of crystal water and has certain expansion performance for a system, so good adhesion with foundation concrete can be formed, and the purpose of good adhesion is achieved; and by adding a certain amount of mineral powder, a pore structure can be refined, and the mineral powder can react with calcium hydroxide and other substances to generate hydrated calcium silicate gel (volcanic ash effect) so as to further improve the compactness and the ion erosion resistance of mortar, and the purpose of good compactness and ion erosion resistance of the mortar is achieved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-ductility fast-setting rapid-hardening concrete repair material. Background technique [0002] In today's world, structural failures or building function failures caused by various reasons not only affect people's normal life but also cause huge economic losses. Among them, cracks, shedding and leakage of cement concrete structures are the most common maintenance of concrete products. Problem, there are more and more concrete repair materials that have been successfully developed and put into the market, mainly including inorganic and organic repair materials, among which epoxy resin repair materials or (meth)acrylic repair materials have occupied the majority of organic concrete repair materials. Mostly. [0003] Although these concrete repair materials have excellent adhesion to dry concrete, they have the following problems. When they are wet from rain or us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/20C04B111/72
CPCC04B28/06C04B2111/72C04B2111/20C04B18/08C04B14/06C04B7/02C04B22/143C04B18/141C04B24/16C04B2103/302
Inventor 王学振马永胜欧阳宁付勇杨猛
Owner ZHENGZHOU SINO SINA BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap