A kind of glass fiber cloth reinforced copper clad laminate manufacturing method

A technology of glass fiber cloth and manufacturing method, which is applied in the fields of printed circuit manufacturing, chemical instruments and methods, and the manufacture of printed circuit precursors, etc. It can solve the problem of affecting the dielectric properties of copper clad laminates, high volume fraction of copper clad laminates, and affecting the rigidity of copper clad laminates, etc. problems, achieve the effect of improving peel strength, improving dielectric properties, and reliable production process

Active Publication Date: 2022-07-05
江西倍韬新材料科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most copper-clad laminates use glass fiber cloth as a reinforcing material. However, the dielectric constant of glass fiber cloth is higher than that of resin substrates, and it occupies a higher volume fraction of copper-clad laminates, which directly affects the dielectric properties of copper-clad laminates.
At the same time, the laminated substrate made of alkali-free glass cloth impregnated with polytetrafluoroethylene dispersion emulsion and then hot-pressed has high insulation and high temperature resistance, but its rigidity is relatively poor, which affects the rigidity of the copper clad laminate as a substrate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass fiber cloth reinforced copper clad laminate manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for manufacturing a glass fiber cloth reinforced copper clad laminate, comprising the following specific steps:

[0028] S1. Preparation of reinforcement material: select glass fiber cloth as reinforcement material, and weave glass fiber cloth with E-GLASS alkali-free glass roving, the thickness is 0.01mm, and the gram weight is 15g / m 2 , and then spray 4 parts by weight of polytetrafluoroethylene under the condition of air pressure of 0.3 MPa, after standing for 8 minutes, spray 1 part by weight of epoxy resin, and dry at 35 ° C for 30 minutes, and finally use vinyl The ethoxysilane is surface-treated at 150 °C to obtain a reinforcing material;

[0029] S2. Preparation of modified resin: take epoxy resin as the basic body, carry out a blending reaction with dicyclopentadiene, oligophenylene ether and styrene, and then add a flame retardant and mix evenly to obtain a modified resin. Among them, the weight ratio of epoxy resin to dicyclopentadiene, oligophenyle...

Embodiment 2

[0033] A glass fiber cloth reinforced copper clad laminate manufacturing method, S1. The glass fiber cloth is prepared in the preparation of the reinforcing material, the thickness is 0.1mm, and the gram weight is 90g / m 2 . Others are the same as in Example 1.

Embodiment 3

[0035] A glass fiber cloth reinforced copper clad laminate manufacturing method, S1. The glass fiber cloth is prepared in the preparation of the reinforcing material, the thickness is 0.2mm, and the gram weight is 180g / m 2 . Others are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Basis weightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of copper clad laminates, in particular to a method for manufacturing a glass fiber cloth reinforced copper clad laminate. The prepreg is obtained, and finally the semi-cured and semi-cured copper foils are stacked, combined and pressed into copper clad laminates according to product specifications. By controlling the total integral fraction of the glass fiber cloth in the copper clad laminate, the invention adopts two prepreg treatments, reasonably controls the proportion of prepregs, and uses a silane coupling agent to perform surface treatment on the glass fiber cloth, and at the same time uses a modified ring Oxygen resin impregnated glass fiber cloth can effectively improve the rigidity, dielectric properties and insulation reliability of copper clad laminates, with reliable process and simple operation.

Description

technical field [0001] The invention belongs to the technical field of copper clad laminates, in particular to a manufacturing method of a glass fiber cloth reinforced copper clad laminate. Background technique [0002] Copper clad laminate is a kind of plate-like material formed by dipping the reinforcing material with adhesive, covering one or both sides with copper foil, and hot pressing, called Copper Clad Laminate (CCL), referred to as CCL. copper plate. Its only purpose is to make printed circuit boards (Printed Circuit Board, PCB). Reinforcing materials include cellulose paper, electronic glass fiber woven cloth, electronic glass fiber paper (non-woven fabric), synthetic fiber woven cloth, synthetic fiber non-woven fabric, and the like. The function of the reinforcing material is to make the copper clad laminate have a certain mechanical strength. [0003] With the development of high-performance, high-functionality and networking of computers and information commu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H05K3/02B32B17/02B32B15/20B32B15/14B32B33/00B32B37/06B32B37/10B32B38/08B32B38/16
CPCH05K3/022B32B5/02B32B15/20B32B15/14B32B33/00B32B37/06B32B37/10B32B38/08B32B38/164B32B2260/021B32B2260/046B32B2255/02B32B2255/26B32B2262/101B32B2307/206B32B2307/306B32B2307/20B32B2457/08
Inventor 彭家灯张亲家刘爱新吴允禄
Owner 江西倍韬新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com