One-component polyurethane waterproof coating composition and preparation method thereof

A polyurethane waterproof, polyurethane prepolymer technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of slow hydrolysis, base surface peeling, and inability to meet the needs of use

Active Publication Date: 2022-02-18
KESHUN WATERPROOF TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the coating film formed by the current one-component polyurethane waterproof coating will slowly hydrolyze under the action of water vapor in the environment or under the condition of immersion in water, resulting in poor adhesion between the coating film and the substrate, and even bulging, cracking, and contact with the substrate. Peeling, can not meet the needs of underground high humidity or water immersion environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component polyurethane waterproof coating composition and preparation method thereof
  • One-component polyurethane waterproof coating composition and preparation method thereof
  • One-component polyurethane waterproof coating composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0151] Add hydroxyl-terminated polybutadiene acrylonitrile, polyether polyol, and plasticizer into the strong disperser, gradually add pigments and fillers, and disperse evenly;

[0152] Transfer the dispersed slurry to the reactor, stir and heat up to 100~110°C, and dehydrate for 2~3 hours at a relative vacuum of -0.08~-0.1MPa;

[0153] Lower the temperature to 70-80°C, add a dispersant, then gradually add isocyanate, stir, then add the second catalyst, raise the temperature to 75-85°C, and react for 3-4 hours; control the rate of isocyanate addition to 1-2 parts by weight / s;

[0154] Keep warm at 75~85℃, add end-capping agent, and continue stirring for 2~3 hours;

[0155] Cool down to 50~60°C, add the first catalyst, and stir for 0.5~1 hour;

[0156] Cool down to below 50°C, fill with nitrogen for protection, and discharge to obtain a one-component polyurethane waterproof coating composition.

[0157] In the above preparation process, the hydroxyl-terminated polybutadien...

Embodiment 2

[0159] Repeat the preparation process described in Example 1, the change is:

[0160] The hydroxyl-terminated polybutadiene acrylonitrile used is 100 parts by weight, the polyether polyol is 70 parts by weight of polyether polyol EP330N, the dispersant is 40 parts by weight of butyl acetate, and the plasticizer is 26 parts by weight of Trioctyl phosphate, pigments and fillers are 60 parts by weight of nano calcium carbonate and 30 parts by weight of fumed silica, isocyanate is 55 parts by weight of TDI and 7 parts by weight of L-lysine triisocyanate, the second catalyst is 0.5 The amount of stannous octoate in parts by weight, the addition amount of the end-capping agent is 40 parts by weight, and the first catalyst is stannous octoate in 1 part by weight.

Embodiment 3

[0162] Repeat the preparation process described in Example 1, the change is:

[0163] The hydroxyl-terminated polybutadiene acrylonitrile used is 100 parts by weight, the polyether polyol is 50 parts by weight of polyether polyol EP330N, the dispersant is 35 parts by weight of butyl acetate, and the plasticizer is 25 parts by weight of Nonyl ester, pigments and fillers are 65 parts by weight of nano-calcium carbonate and 25 parts by weight of fumed silica, isocyanate is 55 parts by weight of 4,4'-dicyclohexylmethane diisocyanate (HMDI) and 5 parts by weight of L- Lysine triisocyanate, the second catalyst is 0.2 parts by weight of stannous octoate, the addition amount of the blocking agent is 30 parts by weight, and the first catalyst is 0.5 parts by weight of stannous octoate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application belongs to the technical field of waterproof coatings, and provides a one-component polyurethane waterproof coating composition and a preparation method thereof. The one-component polyurethane waterproof coating composition includes polyurethane film-forming resin, dispersant and optional additives; polyurethane film-forming resin Including the molecular chain skeleton of isocyanate-terminated polyurethane prepolymer, which is obtained by the reaction of hydroxyl-terminated polybutadiene acrylonitrile, polyether polyol and isocyanate, and polyurethane film-forming resin. The chain segment structure shown in formula 1, formula 1, wherein R 1 ~R 4 and n, n ’ respectively as defined herein. The coating film formed by the one-component polyurethane waterproof coating composition of the present application has excellent water resistance.

Description

technical field [0001] The application belongs to the technical field of waterproof coatings, and in particular relates to a one-component polyurethane waterproof coating composition and a preparation method thereof. Background technique [0002] The polyurethane coating film has the characteristics of elasticity and good ductility, good adhesion, small volume shrinkage, no seams in the waterproof layer of the coating film, good resistance to expansion and deformation of the base layer, and easy construction. One-component polyurethane waterproof coatings are flourishing due to the advantages of low viscosity, low construction difficulty, long application period and stable performance. [0003] However, the coating film formed by the current one-component polyurethane waterproof coating will slowly hydrolyze under the action of water vapor in the environment or under the condition of immersion in water, resulting in poor adhesion between the coating film and the substrate, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C08G18/69C08G18/48C08G18/12
CPCC09D175/14C08G18/698C08G18/4829C08G18/12
Inventor 何宏林陈立义
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com