Anodic oxide film scratch repair liquid

A technology of anodic oxidation film and repair fluid, which is applied in the direction of electrolytic coating, surface reaction electrolytic coating, coating, etc., can solve the problems of high cost of processing environment and affecting product size, etc., and achieve stable filling performance, high durability, The effect of reducing the time taken for restoration

Pending Publication Date: 2021-12-03
苏州海伯利安机器人科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the commonly used method is the treatment method of anodizing and re-anodizing, but it has the defect that the scrap rate reaches 70%, which affects the overall product size, and the existing anodizing and re-anodizing treatment environment is very expensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anodic oxide film scratch repair liquid
  • Anodic oxide film scratch repair liquid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A solution for repairing scratches on an anodized film, wherein: by weight, it comprises the following components: 15 parts of aluminum oxide, 15 parts of water, 10 parts of lubricant, 1 part of polyether modified polysiloxane, 7 parts of petroleum spirit 4 parts of polyparaben, 0.5 part of zinc pyrithione, 1 part of ethylene-hydroxyethyl acrylate copolymer, 0.5 part of pentaerythritol triacrylate; lubricants include 4 parts of vegetable wax, 5 parts of synthetic wax and 1 part petroleum wax, vegetable wax is rice bran wax, synthetic wax includes 1 part polyethylene wax and 4 parts hexafluoropropylene-ethylene-vinyl acetate copolymer wax.

Embodiment 2

[0031] A kind of anodized film scratch repair liquid, wherein: by weight, comprises following components:

[0032] 25 parts of alumina, 30 parts of water, 20 parts of lubricant, 3 parts of polyether modified polysiloxane, 10 parts of petroleum spirit, 6 parts of polyparaben, 0.8 parts of zinc pyrithione, ethylene-acrylic acid 2 parts hydroxyethyl ester copolymer, 0.7 parts pentaerythritol triacrylate; lubricant includes 8 parts jojoba oil, 10 parts synthetic wax and 2 parts petroleum wax, synthetic wax includes 3 parts polyethylene wax and 7 parts hexafluoropropylene- Ethylene-vinyl acetate copolymer wax.

Embodiment 3

[0034] A kind of anodized film scratch repair liquid, wherein: by weight, comprises following components:

[0035] 40 parts of alumina, 40 parts of ethanol, 30 parts of lubricant, 5 parts of polyether modified polysiloxane, 13 parts of petroleum spirit, 8 parts of polyparaben, 1 part of zinc pyrithione, ethylene-acrylic acid 3 parts hydroxyethyl ester copolymer, 1 part pentaerythritol triacrylate; lubricants include 10 parts wood wax, 15 parts synthetic wax and 5 parts petroleum wax, synthetic wax includes 5 parts polyethylene wax and 10 parts hexafluoropropylene-ethylene- Vinyl acetate copolymer wax.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anodic oxide film scratch repair liquid. The anodic oxide film scratch repair liquid comprises the following components in parts by weight: 15-40 parts of aluminum oxide, 15-40 parts of a solvent, 10-30 parts of a lubricating agent, 1-5 parts of a thickening agent and 7-13 parts of benzine. The anodic oxide film scratch repair liquid has the advantages of good adhesive force and good gap filling performance through compatibility of multiple components, repair time can be greatly shortened, repair efficiency can be improved, a filled workpiece is high in durability, the filling performance is still stable in a high-temperature, high-pressure and high-humidity environment, the three-damage repair effect is excellent, and the characteristics of a product are not modified.

Description

technical field [0001] The invention relates to the technical field of repairing agents, in particular to an anodized film scratch repairing solution. Background technique [0002] Scratches on aluminum products are traces of lines on the surface of aluminum. After scratches on aluminum products, repairing agents need to be used to repair them, so as to achieve the purpose of repairing scratches, avoid the overall aesthetic problems caused by scratches on aluminum products, and ensure The aesthetics of aluminum products. [0003] At present, the commonly used method is anodizing and re-anodizing, but it has the defect that the scrap rate reaches 70%, which affects the overall product size, and the existing anodizing and re-anodizing treatment environment is very expensive. Contents of the invention [0004] Aiming at the deficiencies in the prior art, the present invention provides an anodized film scratch repair solution, which has high durability of aluminum products af...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25D11/24
CPCC25D11/246
Inventor 刘希舒清元程立
Owner 苏州海伯利安机器人科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com