Packaging wrapping film and preparation method thereof

A technology of stretch film and thermoplastic elastomer, which is applied in the field of packaging stretch film and its preparation, can solve the problems of further improvement of mechanical properties, easy occurrence of extravasation, poor stability of material properties, etc.

Pending Publication Date: 2021-12-17
泗县绿昂新材料科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the compatibility problem between the various components, the stability of the material properties is not good, and extravasation is prone to occur during long-term use, transportation and storage, and the mechanical properties need to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0037] As a preferred embodiment, the waste polyareneoxadiazole fiber is a waste product of Baodren short fiber; its average diameter is 1-3 μm, and its aspect ratio is 20-30.

[0038] As a preferred embodiment, the vinyl-terminated nitrile rubber is VTBN1300X33LC, a product of CVC Specialty Chemicals Co., Ltd., USA.

[0039] As a preferred embodiment, the rosin polyether sulfonate is a rosin polyether prepared according to the method of Example 1 of the Chinese invention patent of application number 201711335006.4 (this article is incorporated herein by reference as part of the present invention) Sulfonate.

[0040] As a preferred embodiment, the initiator is at least one of cumene hydroperoxide, methyl ethyl ketone peroxide, diisopropyl peroxydicarbonate, and azobisisobutyronitrile.

[0041] As a preferred embodiment, the environmentally friendly plasticizer is at least one of tributyl citrate, trioctyl citrate, and epoxidized soybean oil.

[0042] The invention also discl...

Embodiment 1

[0053] A wrapping stretch film, characterized in that it is prepared from the following components in parts by weight:

[0054] Waste thermoplastic elastomer TPEE 25 parts,

[0055] 4 parts of waste polyarylene oxadiazole fiber,

[0056] Terminal vinyl nitrile rubber 15 parts,

[0057]Rosin polyether sulfonate 4 parts,

[0058] 1.5 parts of pentaerythritol tetra-3-mercapto propionate,

[0059] 1.0 parts of 1-allyl-3-methyl imidazole chloride,

[0060] 0.4 part of initiator,

[0061] 0.2 parts of phosphorus pentoxide,

[0062] Environmentally friendly plasticizer 0.5 parts.

[0063] The waste thermoplastic elastomer TPEE is a waste product of EM550 thermoplastic elastomer TPEE; the waste polyarylene oxadiazole fiber is a waste product of Baodren short fiber; its average diameter is 1 μm, and the aspect ratio for 20.

[0064] The vinyl-terminated nitrile rubber is VTBN1300X33LC, a product of CVC Specialty Chemicals Co., Ltd., USA; the initiator is cumene hydroperoxide; a...

Embodiment 2

[0067] A wrapping stretch film, characterized in that it is prepared from the following components in parts by weight:

[0068] Waste thermoplastic elastomer TPEE 27 parts,

[0069] 5 parts of waste polyarylene oxadiazole fibers,

[0070] Terminal vinyl nitrile rubber 11 parts,

[0071] Rosin polyether sulfonate 2.5 parts,

[0072] 0.7 parts of pentaerythritol tetra-3-mercaptopropionate,

[0073] 0.6 parts of 1-allyl-3-methyl imidazole chloride,

[0074] 0.25 part of initiator,

[0075] 0.12 parts of phosphorus pentoxide,

[0076] Environmentally friendly plasticizer 0.3 parts.

[0077] The waste thermoplastic elastomer TPEE is selected from the waste product of the thermoplastic elastomer TPEE whose brand is EM630; the waste polyarylene oxadiazole fiber is a waste product of Baodren staple fiber; its average diameter is 1.5 μm, and its length is The diameter ratio is 22; the vinyl-terminated nitrile rubber is VTBN1300X33LC, a product of CVC Specialty Chemicals Co., Ltd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a packaging wrapping film, which is characterized by being prepared from the following components as raw materials in parts by weight: 25 to 35 parts of a waste thermoplastic elastomer TPEE, 4 to 7 parts of waste aromatic oxadiazole fibers, 10 to 15 parts of vinyl-terminated nitrile rubber, 2 to 4 parts of rosin polyether sulfonate, 0.5 to 1.5 parts of pentaerythritol tetra-3-mercaptopropionate, 0.5-1.0 part of 1-allyl-3-methyl imidazole chloride, 0.2-0.4 part of an initiator, 0.1-0.2 part of phosphorus pentoxide and 0.2-0.5 part of an environment-friendly plasticizer. The invention further provides a preparation method of the packaging wrapping film. The packaging wrapping film provided by the invention is good in comprehensive performance and performance stability, high in tensile strength and tear strength, and good in penetration resistance and self-adhesion performance.

Description

technical field [0001] The invention relates to the technical field of packaging, in particular to a packaging stretch film and a preparation method thereof. Background technique [0002] Packaging stretch film is a kind of packaging method that uses mechanical stretching device or manual stretching of the film to force the deformation stress at room temperature to wrap the goods tightly for transportation and storage. It is a very common packaging form in the world at present. . It can make the whole stack of goods stable and not loose, thereby reducing damage during transportation, and can also play a role in dust and moisture resistance. Packaging stretching film is widely used in chemical raw materials, chemical fertilizers, Single-piece or tray packaging and other bundled packaging for food, mechanical and electrical products, and textile products. [0003] At present, the packaging stretch film on the market mainly uses PE as the raw material. The production cost of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L79/04C08L93/04C08K5/3445C08J5/18
CPCC08J5/18C08J2367/02C08J2479/04C08J2493/04C08K5/3445
Inventor 王念念高宗华
Owner 泗县绿昂新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com