Anticorrosive inner coating film for inner layer of steel drum

A technology of inner coating and inner layer, applied in anti-corrosion coatings, coatings, epoxy resin coatings, etc., can solve the problems of accelerating water absorption of water-based coatings, reducing corrosion resistance, and affecting the safety of transportation of material purity in barrels. , to achieve the effect of eliminating phase interface, inhibiting penetration, and good physical shielding effect

Inactive Publication Date: 2022-01-18
荆州市先隆包装制品有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the particle coalescence stage, molecular rearrangement occurs, and polymer particles with similar polar groups tend to aggregate (while waterborne epoxy coatings must contain polar groups or hydrophilic groups), resulting in Polar groups form polar channels for water penetration, which accelerates water absorption in water-based coatings and reduces corrosion resistance. In order to increase the hardness of steel drums during the coating preparation process, various pigments and fillers are added. Pigments and fillers are generally difficult Uniform dispersion in water makes it easy to form a phase interface between coatings, giving an intrusion channel for intruding substances, making the metal substrate more prone to corrosion reactions, and steel drums often need to contain various acid-base salts and highly corrosive substances. The anti-corrosion performance of the inner wall of the steel drum is not well done, which has a great impact on the purity of the material in the drum and the safety of transportation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Embodiment 1: A kind of preparation method for the anticorrosion inner film of inner layer of steel drum is as follows: 60% of modified epoxy resin emulsion and water are added in the stirring vessel and stirred, stirred for 40-50min, then film-forming auxiliary Add 2% surfactant, 2% surfactant, 4% coupling agent, 10% curing agent, 0.1% defoamer, 0.2% leveling agent and water into a stirring container and stir for 70-80min, cool to room temperature, and obtain an anti-corrosion inner coating membrane.

Embodiment 2

[0036] Embodiment 2: A kind of preparation method for the anti-corrosion inner coating film of inner layer of steel drum is as follows: Add 65% of modified epoxy resin emulsion and water into the stirring container and stir, stir for 40-50min, then add film-forming auxiliary Add 2% anti-corrosion pigments and fillers, 4% surfactants, 5% coupling agents, 12% curing agents, 0.2% defoamers, 0.5% leveling agents and water into the stirring container and stir for 70-80min, cool room temperature to obtain an anti-corrosion inner coating. The anti-corrosion pigments and fillers are prepared from talcum powder and 3-aminopropyltriethoxysilane.

Embodiment 3

[0037] Embodiment 3: A kind of preparation method for the anticorrosion inner coating film of inner layer of steel drum is as follows: 66% of modified epoxy resin emulsion and water are added in the stirring vessel and stirred, stirred for 40-50min, then film-forming auxiliary Add 4% anticorrosion agent, 3.5% anticorrosion pigment and filler, 5% surfactant, 5% coupling agent, 12% curing agent, 0.2% defoamer, 0.5% leveling agent and water into the stirring container and stir for 70-80min, cool room temperature to obtain an anti-corrosion inner coating. The anti-corrosion pigments and fillers are prepared from modified aluminum tripolyphosphate and N-aminoethyl-γ-aminopropyltrimethoxysilane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of anticorrosive coatings, and relates to an anticorrosive inner coating film for an inner layer of a steel drum. The anticorrosive inner coating film mainly comprises the following components in percentage by weight: 60-70% of modified epoxy resin emulsion; 1-5% of a coalescing agent; 3-15% of anticorrosive pigment and filler; 2-8% of a surfactant; 4-10% of a coupling agent; 10-15% of a curing agent; 0.1-2% of a defoaming agent; 0.1-2% of a leveling agent; 0.1%-0.6% of a corrosion inhibitor; and 10-50% of water. The modified epoxy resin emulsion is adopted, so that a formed coating plays a role in physically shielding various corrosive media; the corrosion inhibitor is added, so that the corrosion rate of steel is greatly reduced; and a pigment and filler are modified to form the anticorrosive pigment and filler, the dispersity of the pigment and filler in epoxy resin is improved, and a phase interface between the pigment and filler and the resin is eliminated, so that the shielding property and the corrosion resistance of a colored paint film are improved on the premise of ensuring high hardness and high adhesive force of the paint.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, in particular to an anti-corrosion inner film used for the inner layer of a steel drum. Background technique [0002] Steel drums are one of the traditional containers and play an important role in traditional containers. The steel drum has evolved from the function of temporarily storing the contents to today's industrial packaging, sales packaging, transportation packaging, etc.; from production to circulation and consumption, it has formed a consistent flow container and has become a means of long-term preservation of the contents. It can be said that steel drums are the best for mankind. Work and life have brought great changes and progress. [0003] Although the application of steel drums has only a history of more than one hundred years, it has developed rapidly and has a wide variety. It is widely used in industrial product packaging, transportation packaging and sales pac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08C09D7/61C09D7/62C09D7/63
CPCC09D163/00C09D5/08C09D7/61C09D7/62C09D7/63C08K9/02C08K9/04C08K3/042C08K5/544C08K5/18C08K5/521
Inventor 胡文明邹雅俊邹乐新凡亮亮覃方王海邹雅丽
Owner 荆州市先隆包装制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products