Production method of carbide slag cement

A production method and technology of carbide slag, applied in cement production and other directions, can solve the problems of consuming large primary natural resources and pollution of carbide slag, and achieve the effects of controlling and controlling dust pollution, protecting the environment and saving resources

Pending Publication Date: 2022-05-13
宁夏金昱元资源循环有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a production method of carbide slag cement, which is used to solve the problems of cement production that consumes a large amount of primary natural resources, solid waste such as carbide slag, and pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of carbide slag cement
  • Production method of carbide slag cement
  • Production method of carbide slag cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] A kind of production method of calcium carbide slag cement, comprises the following steps:

[0066] 1) Raw material pretreatment: crush sandstone, slag, and iron ore and send them to the rectangular combined pre-homogenization yard for storage; desulfurized gypsum is crushed by a gypsum crusher and then sent to a round warehouse for storage. Send the fly ash to the garden warehouse for storage.

[0067] Concentrate the calcium carbide slag with a water content of more than 90% in the concentration tank, and reduce the water content to below 80%, then remove excess water through a filter press, press filter to form a filter cake with a water content of ≤38%, and finally send it to the oven After drying in the dry crusher, it is sent to the calcium carbide slag dry powder warehouse for storage.

[0068] Specifically, the chemical composition analysis table of raw materials used in carbide slag cement is as follows: (%)

[0069] L.O.I. SiO 2

Al 2 o ...

Embodiment 2

[0081] A kind of production method of calcium carbide slag cement, raw material and chemical composition thereof are consistent with embodiment 1, during production, differs from embodiment 1 in the following steps:

[0082] Step 2) In the batching and grinding of auxiliary materials, the extrusion pressure of the grinding treatment is 11 MPa, the number of grinding times is 4 times / rotation, the particle size of the feed is not higher than 55mm, and the comprehensive moisture is less than 3.5%. The particle size of the finished product of the above-mentioned auxiliary materials passes through a 0.08mm square hole sieve, and the sieve residue is ≤8%.

[0083] Step 3) In raw meal batching and homogenization, the components and parts by weight in the raw meal are as follows: 80 parts by weight of carbide slag, 15 parts by weight of fly ash, 76 parts by weight of sandstone, 30 parts by weight of slag, and 20 parts by weight of iron ore share.

[0084] Step 4) In firing the clink...

Embodiment 3

[0087] A kind of production method of calcium carbide slag cement, raw material and chemical composition thereof are consistent with embodiment 1, during production, differs from embodiment 1 in the following steps:

[0088] Step 2) In the batching and grinding of auxiliary materials, the extrusion pressure of the grinding treatment is 10 MPa, the grinding frequency is 3 times / rotation, the particle size of the feed is not higher than 55mm, and the comprehensive moisture is less than 3.5%. The particle size of the above-mentioned finished auxiliary materials passes through a 0.08mm square hole sieve, and the sieve residue is ≤5%.

[0089] Step 3) In raw meal batching and homogenization, the components and parts by weight in the raw meal are as follows: 77 parts by weight of carbide slag, 12 parts by weight of fly ash, 75 parts by weight of sandstone, 28 parts by weight of slag, and 19 parts by weight of iron ore share.

[0090] Step 4) In firing the clinker, the temperature o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a production method of carbide slag cement, and belongs to the technical field of cement production, and the production method comprises the following steps: taking sandstone, iron ore and slag for burdening, feeding into a roller press for grinding, mixing the obtained discharged material with fly ash, and sorting to obtain an auxiliary material finished product; mixing the carbide slag and the auxiliary material finished product, and homogenizing in a raw material homogenizing silo; sequentially preheating and pre-decomposing the homogenized raw material, feeding into a rotary kiln for calcining to obtain clinker, feeding the clinker into a grate cooler for cooling, and feeding into a clinker warehouse for storage for later use; the clinker, the desulfurized gypsum, the slag and the fly ash are mixed and then fed into a combined grinding system to be ground, and a cement finished product is obtained. The method is used for solving the problems of consumption of a large amount of native natural resources in cement production, treatment of carbide slag and other solid wastes and pollution; according to the method, calcium carbide slag is used for replacing limestone to produce cement, the quality of a cement finished product is stable, the consumption of native resources is remarkably reduced, industrial solid waste is recycled, and the production cost is reduced.

Description

technical field [0001] The invention relates to the technical field of cement production, in particular to a production method of carbide slag cement. Background technique [0002] Cement is mainly made of clay, limestone, silica-alumina materials, iron materials and other raw materials mixed and ground in proportion and then calcined at high temperature. It also includes mixed materials, cementitious materials and retarders. It is a powdery hydraulic gelling material that hardens in medium and can harden in water. Therefore, cement is not only widely used in industrial and civil buildings, but also widely used in transportation, urban construction, agriculture, forestry, water conservancy and marine projects, and has a very broad application prospect. [0003] With the continuous development of the construction industry, the demand for cement is also increasing. At present, the production process of cement needs to consume a large amount of primary iron ore, primary silic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/24C04B7/26C04B7/36
CPCC04B7/243C04B7/36C04B7/26Y02P40/10
Inventor 代良云吴红卫梁军曹爱新
Owner 宁夏金昱元资源循环有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com