A kind of super-large diameter steel strand for mine anchor cable and its manufacturing method

A technology of super large diameter and manufacturing method, which is applied in the manufacture of tools, mining equipment, and installation of bolts, etc., to achieve the effect of reducing steel consumption, optimizing temperature and time process parameters, and reducing the risk of steel wire brittle fracture

Active Publication Date: 2022-07-26
天津市新天钢中兴盛达有限公司 +3
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no special industry standard for mining steel strands. The national standard GB / T5224-2014 "Steel Strands for Prestressed Concrete" is applicable to mining steel strands, but in the national standard, 1×19W structural steel strands The maximum diameter of the product is 28.6mm. Products with a diameter above this are not involved in relevant product standards at home and abroad, and are blank products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of super-large diameter steel strand for mine anchor cable and its manufacturing method
  • A kind of super-large diameter steel strand for mine anchor cable and its manufacturing method
  • A kind of super-large diameter steel strand for mine anchor cable and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The structure of the present invention will be further described below with reference to the accompanying drawings and through embodiments. It should be noted that this embodiment is descriptive, not restrictive.

[0026] A super-large diameter steel strand for mining anchor cables, see figure 1 , using 1×19 silk walington (1+6+6 / 6) structure, mainly considering the possible domestic supply of raw materials and the maximum capacity of equipment. Design the size of each layer of steel wire, and appropriately increase the diameter of each layer of steel wire when designing the diameter of each layer (taking into account the current production equipment capacity and tooling allowable conditions, the appropriate increase in the size of the steel wire can improve the quality of the finished steel strand. The maximum force value creates conditions), determine the size of the center wire is 7.74mm, the size of the outer layer thick wire is 8.01mm, the size of the outer layer ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a super-large-diameter steel strand for a mine anchor cable and a manufacturing method thereof. The steel strand adopts a 1×19-wire Waringon structure, 19 wires are twisted at one time, and the twist distance is 13.5 times. The diameter of the wire is 7.74mm, the diameter of the outer thick wire is 8.01mm, the diameter of the outer thin wire is 6.07mm, the diameter of the inner wire is 7.43mm, the nominal diameter of the steel strand is 34.6mm, and the upper deviation of the nominal diameter is +0.40 mm, the lower deviation of the nominal diameter is ‑0.15mm; the manufacturing method includes: selection of wire rods → inspection, testing → pickling, phosphating → inspection → drawing → semi-finished product inspection, testing → stranding → stabilization treatment → layer winding → Finished product inspection and testing → packaging → storage. The invention makes the measured diameter of the twisted steel strand reach 34.8mm through four kinds of diameters of wires, and the structure of the steel strand is tight and not loose, which meets the size requirement of the super-large diameter steel strand.

Description

technical field [0001] The invention belongs to the technical field of mining steel strands, in particular to a super-large diameter steel strand for mining anchor cables and a manufacturing method thereof. Background technique [0002] In recent years, with the continuous exploitation of mine resources, more coal mines have entered the stage of deep mining. The deep mining of mines increases the instability of surrounding rock and the difficulty of supporting, which brings hidden dangers to the safety of mine production. The deep mining also makes the construction environment and other working conditions extremely complicated. , clearly stipulates the requirement to strengthen the roadway support of rockburst mines, and requires the reasonable selection of roadway support forms and parameters, and proposes that "when the roadway with thick coal seams is tunneled along the bottom support and the top coal is selected for anchor bolt and cable support, ... the diameter of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D07B1/06E21D21/00B21C1/02C21D9/52C22C38/02C22C38/04C22C38/42C22C38/46C23C22/73C23G1/04C23G1/08
CPCD07B1/0693E21D21/006B21C1/02C22C38/02C22C38/04C22C38/42C22C38/46C23G1/08C23G1/04C23C22/73C21D9/525D07B2201/1044D07B2201/1036D07B2201/2006D07B2201/2009D07B2205/3057
Inventor 王莉张翔李宝军赵学刚李建富潘捷吕芳王鸿利
Owner 天津市新天钢中兴盛达有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products