Formula of fragile membrane and preparation method of fragile membrane

A production method and formulation technology, which is applied in the formulation and production of fragile films, can solve problems such as low strength, reduced strength, and reduced strength, and achieve the effects of meeting solvent resistance, meeting use requirements, and improving environmental protection

Pending Publication Date: 2022-07-29
丝艾工业科技(海安)有限公司
0 Cites 0 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0002] There are many kinds of fragile materials, such as fragile paper and fragile film. Fragile materials are widely used in the label industry. They can be used as carrier materials for anti-counterfeiting labels. The label should be damaged. There are many ways to make fragile materials. One is fragile paper. The strength of the paper itself is not high. The fragile paper will further reduce the strength of the paper. The solvent resistance and light resistance of fragile paper are not high. , a kind of fragile film by extrusion method, which adopts multi-layer co-extrusion method to reduce the strength of the core material, and at the same time add more fillers to change the strength of the material itself. The cost of this production method is relatively high, due to If too much filler is added, it is easy to break the membrane during the process of pulling the membrane, which requires high equipment. One is the electric shock method: such as BOPP, PET, etc., which use the electric spar...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses a formula of a fragile film and a manufacturing method thereof, and the formula of the fragile film comprises the following raw materials in parts by weight: 100 parts of water-based resin, 5-60 parts of color paste, 1-10 parts of a thickening agent, 0.1-10 parts of a leveling agent, 1-10 parts of a defoaming agent and 1-20 parts of a curing agent. The color paste is white, the solid content is 30-70%, the filler is one or a mixture of more of mica powder, talcum powder, kaolin, titanium dioxide and calcium carbonate, and the particle size d50 is 10-60 [mu] m. By adopting the water-based resin and a certain amount of the auxiliary agent, the water-based resin composite material can be broken under relatively high tensile strength, has solvent resistance and high-temperature yellowing resistance, can well absorb laser with the wavelength of 1064nm, improves the environmental protection property and meets the use requirements.

Technology Topic

Examples

  • Experimental program(10)

Example Embodiment

[0019] Example 1
[0020] This example proposes a formulation of a fragile film, including the following raw materials by weight: 100 parts of water-based resin, 40 parts of color paste, 0.2 parts of leveling agent, 1 part of defoamer, and 3 parts of curing agent The color of the color paste is white, the solid content is 40%, the filler used is nano-titanium dioxide, and the particle size is d 50 : 20μm, the leveling agent is BYK333, the defoaming agent is BYK018, the curing agent is Rodia WT1000, the water-based resin is a water-based polyurethane modified acrylic resin, the solid content of the water-based resin is 50%, the molecular weight is 4000, and the functionality is 2.
[0021] The present embodiment also proposes a method for making a fragile film, comprising the following steps:
[0022] S1: Select 100 parts of water-based resin, 40 parts of color paste, 0.2 part of leveling agent, 1 part of defoamer, and 3 parts of curing agent, all of them are added into the mixing box for stirring and mixing;
[0023] S2: Use a viscosity measuring instrument to measure the viscosity of the resin mixture to ensure that its viscosity is 1000-10000cPa.s;
[0024] S3: Select a release film with a thickness of 75μm and a release force of 200g/25mm, and use the comma blade coating method to evenly coat the resin mixture with qualified viscosity in S2 on the release film. The thickness of the coating is 40μm ;
[0025] S4: The release film coated with the resin mixture in S3 is placed in a drying box with a temperature of 80° C. for drying, and dried for 20 minutes to obtain a fragile film.

Example Embodiment

[0026] Embodiment 2
[0027] This example proposes a formulation of a fragile film, including the following raw materials by weight: 100 parts of water-based resin, 40 parts of color paste, 4 parts of thickener, 1 part of defoamer, and 3 parts of curing agent agent, 0.2 part of leveling agent, the color of the color paste is white, the solid content is 40%, the filler used is nano-titanium dioxide, the particle size is d 50 : 20μm, the thickener is polyurethane thickening, the defoamer is BYK018, the curing agent is Rodia WT1000, the leveling agent is BYK333, the water-based resin is water-based polyurethane modified acrylic resin, the solid content of the water-based resin is 50%, and the molecular weight is 4000 , with a functionality of 2.
[0028] The present embodiment also proposes a method for making a fragile film, comprising the following steps:
[0029] S1: Select 100 parts of water-based resin, 40 parts of color paste, 2 parts of thickener, 1 part of defoaming agent, 3 parts of curing agent and 0.2 parts of leveling agent, all added to the mixing box for stirring and mixing uniform;
[0030] S2: Use a viscosity measuring instrument to measure the viscosity of the resin mixture to ensure that its viscosity is 1000-10000cPa.s;
[0031] S3: Select a release film with a thickness of 40μm and a release force of 200g/25mm, and use the comma blade coating method to evenly coat the resin mixture with qualified viscosity in S2 on the release film. The thickness of the coating is 75μm ;
[0032] S4: The release film coated with the resin mixture in S3 is placed in a drying oven with a temperature of 90° C. for drying, and dried for 25 minutes to obtain a fragile film.

Example Embodiment

[0033] Embodiment 3
[0034] This example proposes a formulation of a brittle film, which includes the following raw materials by weight: 100 parts of water-based resin, 40 parts of color paste, 1 part of thickener, 0.2 part of leveling agent, 1 part of elimination agent Foaming agent, 3 parts of curing agent, the color of the color paste is white, the solid content is 40%, the filler used is nano-titanium dioxide, the particle size is d 50 : 20μm, the thickener is polyurethane thickener, the leveling agent is BYK333, the defoamer is BYK018, the curing agent is Rodia WT1000, the water-based resin is water-based polyurethane modified acrylic resin, the solid content of the water-based resin is 50%, and the molecular weight is 4000 with a functionality of 2.
[0035] The present embodiment also proposes a method for making a fragile film, comprising the following steps:
[0036] S1: Select 100 parts of water-based resin, 40 parts of color paste, 2 parts of thickener, 0.2 parts of leveling agent, 1 part of defoamer, and 3 parts of curing agent, all of them are added to the stirring box for stirring and mixing uniform;
[0037] S2: Use a viscosity measuring instrument to measure the viscosity of the resin mixture to ensure that its viscosity is 1000-10000cPa.s;
[0038] S3: Select a release film with a thickness of 75μm and a release force of 200g/25mm, and use the comma blade coating method to evenly coat the resin mixture with qualified viscosity in S2 on the release film. The thickness of the coating is 40μm ;
[0039] S4: The release film coated with the resin mixture in S3 is placed in a drying box with a temperature of 100° C. for drying, and dried for 30 minutes to obtain a fragile film.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularity20.0µm
Thickness75.0µm
Release force200.0g/25mm
tensileMPa
Particle sizePa
strength10

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Environmentally-friendly soil remediation equipment with anti-precipitation function

InactiveCN111085534APrevent soil cakingPromote environmental protectionDispersed particle filtrationRotary stirring mixersChemical additionSoil remediation
Owner:深圳市伊乐农产品有限公司

Classification and recommendation of technical efficacy words

Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products