Bamboo viscose fibre and its preparing method

A viscose fiber and bamboo technology, applied in the field of fiber production, can solve the problems of uncomfortable wearing, inability to achieve antibacterial, loss and other problems

Inactive Publication Date: 2005-03-23
吉林化纤股份有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of wearing and application, with the influence of physical and chemical effects such as wear and washing, its function will gradually decrease or even be lost, and the real antibacterial purpose will not be achieved. At the same time, the drug will also cause certain allergic reactions, which may affect wearing. wearer's skin, making it uncomfortable to wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Pretreatment: liquid ratio 1:2.5, temperature 160°C, time 180 minutes.

[0033] (2) Cooking: the amount of alkali used is 8% of the absolute dry pulp in terms of NaOH, the liquid ratio is 1:4, the hydrogen peroxide is 1% of the absolute dry pulp, the oxygen pressure is 0.70Mpa, the total heating time is 150 minutes, and the holding temperature is 125°C , holding time 11 hours.

[0034] (3) Chlorination: the amount of chlorine used for chlorination is 1% of absolute dry pulp, the concentration of chlorinated pulp is 3.2%, the chlorination time is 60 minutes, and the chlorination temperature is normal temperature.

[0035] (4) Alkali refining: pulp concentration 5%, NaOH consumption 2% to absolute dry pulp, refining temperature 90°C, hydrogen peroxide to 0.5% absolute dry pulp, oxygen flow to 0.4% absolute dry pulp, time 100 minutes.

[0036] (5) Bleaching:

[0037] The pH of the first stage is 9, the amount of chlorine used is 1% to the amount of absolute dry pulp,...

Embodiment 2

[0062] (1) Pretreatment: liquid ratio 1:3, temperature 170°C, time 150 minutes.

[0063] (2) Cooking: the amount of alkali used is 13% of the absolute dry pulp in terms of NaOH, the liquid ratio is 1:5, the hydrogen peroxide is 2% of the absolute dry pulp, the oxygen pressure is 0.80Mpa, the total heating time is 200 minutes, and the holding temperature is 128°C , holding time 8.5 hours.

[0064] (3) Chlorination: the amount of chlorine used for chlorination is 2.5% to the absolute dry pulp amount, the chlorination pulp is thick 3.0%, the chlorination time is 50 minutes, and the chlorination temperature is normal temperature.

[0065] (4) Alkali refining: pulp concentration 8%, NaOH consumption 4% to absolute dry pulp, refining temperature 80°C, hydrogen peroxide 1% to absolute dry pulp, oxygen flow rate 0.5% to absolute dry pulp, time 80 minutes.

[0066] (5) Bleaching:

[0067] The pH of the first stage is 10, the amount of chlorine used is 2% to the amount of absolute dry...

Embodiment 3

[0092] (1) Pretreatment: liquid ratio 1:3.5, temperature 180°C, time 100 minutes.

[0093] (2) Cooking: the amount of alkali used is 16% of the absolute dry pulp in terms of NaOH, the liquid ratio is 1:6, the hydrogen peroxide is 3% of the absolute dry pulp, the oxygen pressure is 0.90Mpa, the total heating time is 240 minutes, and the holding temperature is 132°C , holding time 6 hours.

[0094] (3) Chlorination: the amount of chlorine used for chlorination is 4% to the absolute dry pulp amount, the thick 2.8% of the chlorinated pulp, the chlorination time is 40 minutes, and the chlorination temperature is normal temperature.

[0095] (4) Alkali refining: pulp concentration 10%, NaOH consumption 6% relative to absolute dry pulp, refining temperature 70°C, hydrogen peroxide relative to absolute dry pulp 1.5%, oxygen flow rate relative to absolute dry pulp 0.6%, time 60 minutes.

[0096] (5) Bleaching:

[0097] The pH of the first stage is 11, the amount of chlorine used is 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The bamboo viscose fiber preparing process includes the steps of preparing bamboo material, cutting, screening, washing, pre-treatment, digestion, eliminating sand, concentration, chlorination, alkali refining, bleaching, acid treatment, eliminating sand and concentration, fishing, soaking, squeezing, crushing, ageing, yellowing, grinding, dissolving, filtering, defoaming, filterin,g spinning, drafting, cutting, post-treatment, drying and packaging. The bamboo viscose fiber thus prepared is antibacterial, cool, smooth, fine and bright, and the present invention creates a new field for developing viscose fiber products.

Description

technical field [0001] The invention relates to the production of fibers from plant fiber raw materials, that is, the preparation of fibers by pulping and papermaking methods, more precisely, bamboo viscose fibers and a preparation method thereof. technical background [0002] At present, viscose fiber is a regenerated cellulose fiber with a wide range of uses, which is made from natural cellulose such as wood and cotton linters through a series of processes such as cooking, acid treatment, and bleaching. Because this fiber and its fabric have good moisture absorption and release properties, soft hand feeling, comfortable wearing, and close to natural cotton properties, it is deeply favored by consumers. Especially in today's return to nature and green consumption, the demand for fabrics made of natural fibers is increasing day by day. However, with the increasing shortage of traditional raw materials such as wood and cotton linters, the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01C1/02D01D5/06D01F2/06D06L4/13D06L4/20
Inventor 姜厚有赵建芬朱长生孙同会薛振军宋志国蔡维义
Owner 吉林化纤股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com