High-adhesion nano surface paint with low covered thickness for high-grade vehicle and its preparing process

A low-covering, high-strength technology, applied in coatings and other directions, can solve the problems of poor adhesion, material mechanics and covering film thickness, and achieve excellent performance, high hardness, gloss and good image quality.

Inactive Publication Date: 2002-12-25
姜荃
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention discloses a high-strength, low-coverage high-grade automotive nano-top paint and a production method thereof, which solves the problem of poor compatibility of adhesion, material mechanics and cover film thickness in existing metal topcoat coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Put 1 kg of organosilicon coupling agent KH-570 and 2 kg of organotitanium coupling agent KHT-203 into the stirrer while heating up and stir at a speed of 600-1000 rpm, heat up to 50-70 degrees and then stir at a constant temperature 5-10 minutes to make nano metal powder coating agent.

Embodiment 2

[0022] Mix 1 kg of organic titanium coupling agent KHT-203 with 10 kg of organic aluminum coupling agent DL-411, stir in a stirrer while raising the temperature, the speed is 600-1000 rpm, and keep the temperature after heating to 80-90 degrees Stir for 5-10 minutes to make nano carbon powder coating agent.

Embodiment 3

[0024] Take 15kg of cyclohexanone, 15kg of ethyl acetate, 7kg of butyl acetate, 25kg of xylene, 7kg of butanol, 20kg of propylene glycol monomethyl ether, and 15kg of methyl n-amyl ketone, mix and stir evenly to make a diluent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

A high-adhesion and low-thickness nano-class finish paint for high-grade automobile is prepared from nano-class powder of Ti, Ni, Al, or diamond through mixing with amorphous carbon powder, coating with coupling agent, and proportionally adding it to the acrylic-type, polyurethane-type, or acrylic-polyurethane paint of automobile. Its advantages are high hardness, adhesion, weatherability, lustreand antiwear and anti-impact performance.

Description

Technical field: [0001] The invention relates to a metal topcoat, in particular to a high-strength, low-coverage high-grade nano-topcoat for vehicles and a production method thereof, belonging to the technical field of metal coatings. Background technique: [0002] Usually, adding non-melting and insoluble inorganic and organic fillers to the polymer materials in metal topcoat coatings can improve the mechanical properties of the polymer block materials such as rigidity, toughness and wear resistance. It can also improve the adhesion between the polymer coating and the substrate. For example, fine-grained powders such as oxides, calcium carbonate, metals, and carbon black (generally in the micron range) or glass fibers are added to the resin. Although the former can improve the hardness and wear resistance of the polymer material to a certain extent, and improve the adhesion with the inorganic matrix to a certain extent, it makes the polymer material brittle, and even some ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/28C09D7/12
Inventor 姜荃杜良
Owner 姜荃
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap