High-temp alkali-resistant material and use therreof in ceramic filler

A ceramic filler and alkali resistance technology, applied in the field of ceramic filler materials, can solve the problems of high cost, thickening, filler scaling, etc., and achieve the effect of good alkali corrosion resistance

Inactive Publication Date: 2003-05-28
兰州瑞玛化机有限公司 +1
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with this ceramic filler is the high cost
[0011] The object of the present invention is to provide a kind of economical alkali-resistant material and its application in ceramic fillers, to solve the problem of fillers caused by chemical reactions on the surface when ordinary ceramic materials are used in alkaline environments at high temperatures. Scaling, thickening problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] Add the alkali-resistant material composed of the above ratio into a ball mill, and wet crush it until the particle size is less than 50 microns; dehydrate it with a filter press to make the moisture content <= 23%; Extrude the green body into a rectangular saddle ring; dry the green body at 110°C for 2 hours; then sinter it in a drawer kiln at 1350°C and leave the kiln. Performance evaluation: 1. Alkali resistance test

[0023] The φ25 ordinary ceramic saddle ring (produced by Ningde Junjie Porcelain Industry Co., Ltd., the same below), Ty-PakHSM (produced by Norton Chemical Products Company in the United States, with zircon and wood ash as the main components of ceramics, the same below) and the ceramic saddle ring 1 buried K 2 CO 3 (melting point is 891°C), keep it at a high temperature of 950°C for 8 hours, so that the molten K 2 CO 3 Fully contact with the sample in all directions, after cooling, washing and drying, compare the weight changes of each, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A high-temp. alkali-resistant material mainly contains MgO, SiO2 and Al2O3. Its primary crystal phase is forsterite and spinel. Its features are high resistance to alkali corrosion at high temp and use for preparing ceramic filler of heat-accumulating thermal oxidizer to treat organic waste gas in wood industry.

Description

technical field [0001] The invention relates to an industrial ceramic material, in particular to a material for ceramic filler. Background technique [0002] Ceramic fillers for mass transfer or heat transfer used in chemical equipment and heat exchangers are mainly composed of 70-75% SiO 2 , 20-25% Al 2 o 3 , 2~5%K 2 O+Na 2 O, and a small amount of Fe, Ca, Ti, etc. are sintered at high temperature, and its shapes include honeycomb ceramics, porcelain saddle rings, Raschig rings, etc. When the ordinary ceramic filler of the above composition is used in an alkaline environment, the alkaline substance will chemically react with the surface of the filler at high temperature, resulting in the formation of a reaction layer on the surface of the filler, which increases the thickness of the filler. When the thickness of the filler reaches a critical point, only replacement The corroded packing can restore the equipment to normal. This not only increases the cost of replacing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/04C04B35/63C04B41/87
Inventor 曹学仁
Owner 兰州瑞玛化机有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com