Ultrathin expansion steel-structure fireproofing coating

A technology for fire-resistant coatings and profiles, applied in fire-resistant coatings, coatings, etc., can solve problems affecting the physical and chemical properties and fire resistance of coatings, negative effects on water resistance and durability of coatings, loss of fire resistance, etc., and achieve fire resistance limit performance. Excellent, strong bonding, efficient fire and heat insulation effect

Inactive Publication Date: 2004-04-14
应急管理部四川消防研究所
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are following problems: (1) its main film-forming substance is a modified acrylate resin emulsion, which is a water-based resin, and the formed coating film still has certain moisture absorption after drying, and powdering, Falling off and so on, thus losing its fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0031] Table 3 lists the raw materials and their contents measured in parts by weight and main technical properties of the ultra-thin intumescent steel structure fireproof coatings of the present invention.

[0032] Example 1

Example 2

Example 3

Example 4

Example 5

Example 6

Chlorinated rubber modified acrylic resin

60

54

50

58

52

56

pentaerythritol

15

13.5

14

16

12

13

Melamine

9.5

9

12

11.5

11

10

Ammonium polyphosphate

20

19

19.5

21.5

20

21

Zinc borate

6.5

7.5

6

8

7

7

Titanium dioxide

10

11

10

9

11.5

9.5

Chlorinated paraffin (70% chlorine content)

12.5

13.5

14

14.5

13

15...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provides a fire-retardant coating capable of forming ultrathin coating layer and having high fire-resisting limit. Its composition comprises (by weight portion) 50-60 portions of modified acrylic resin, 12-16 portions of pentaerythritol, 9-12 portions of trimeric cyanamide, 19-21 portions of polyammonium phosphate, 6-8 portions of zinc borate, 9-11 portions of titanium pigment, 1.25-15 portions of chlorinated paraffin (in which chlorine content is 70%) and 8-15 portions of 200# solvent gasoline. The above-mentioned modified acrylic resin is a chlorinated rubber modified acrylic resin made up by using 1.4-1.8 portions of chlorinated rubber, 2.2-2.7 portions of xylene, 0.9-1.1 portions of hexamethylene-diisocyanate and 1.6-1.8 portions of hydroxyl-bearing acrylic resin. Its coating layer thickness is 1.71-2.69 mm, and its fire-resisting limit can be up to 69-147 min.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to ultra-thin intumescent fireproof coatings for steel structure buildings. Background technique [0002] At present, there are three types of widely used fireproof coatings for steel structures: thick type, thin type and ultra-thin type. The latter two are also called intumescent fire retardant coatings. In addition to the ingredients of general architectural coatings, it mainly contains carbonizing agents, foaming agents, catalysts, etc. of the expansion system. Under the high temperature of the flame, the coating undergoes complex physical and chemical changes and expands and foams, forming a A uniform and dense spongy carbonized layer that is dozens or even hundreds of times thicker than the original coating. This carbonized layer has a very low thermal conductivity, and its thermal conductivity is about 0.02W / (m·K)~0.05W / (m·K), which can effectively isolate the heating of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D5/18C09D133/02
Inventor 覃文清李风戚天游
Owner 应急管理部四川消防研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap