Preparation method of nano grade zirconium oxide crude powder

A zirconia and nano-scale technology, which is applied in the field of preparation of nano-scale zirconia raw powder, can solve the problems of unavoidable water influence, small specific surface area and large particle size of nano-powder, and achieve small particle size and particle size distribution Narrow, large specific surface area effect

Inactive Publication Date: 2005-03-09
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that the impact of water on nanoparticles cannot be avoided in the prior art, and the prepared nano raw powder has a small specific surface area and a large particle size. It provides a new preparation of nano-sized zirconia raw powder method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nano grade zirconium oxide crude powder
  • Preparation method of nano grade zirconium oxide crude powder
  • Preparation method of nano grade zirconium oxide crude powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] At room temperature, in a 500 ml three-necked flask, add 200 ml of 0.5 mol / L ZrOCl 2 Solution, under the condition of rapid stirring, add 0.5 mol / L ammonia water as precipitant, control pH final value 9.5, make ZrO 2 Hydrogels. After washing with water, fully exchange the water with ethanol to make ZrO 2 alcohol gel. Transfer the alcohol gel into an autoclave, add an appropriate amount of ethanol as a drying medium, seal the autoclave, slowly raise the temperature to 260°C, keep it for 1 hour, and release the fluid. use N 2 Fill the reactor to drive off the remaining fluid, and after cooling to room temperature, milky white translucent nano-sized ZrO 2 Original powder. In a muffle furnace, it was baked at 650°C for 4 hours to investigate the thermal stability of nanoparticles at high temperature.

Embodiment 2

[0024] Reaction steps, operating method are the same as embodiment 1, just use ZrO(NO 3 ) 2 solution instead of ZrOCl 2 solution.

Embodiment 3

[0026] Reaction steps, operation method are with embodiment 1, just use Na 2 CO 3 as a precipitant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A process for preparing zirconium oxide nanoparticles includes such steps as using alkali solution as precipitant to precipitate Zr salt to obtain the aqueous gel of zirconium oxide and supercritical drying by low-grade emtrol.

Description

technical field [0001] The invention relates to a method for preparing nano-sized zirconia raw powder, in particular to a method for preparing nano-sized zirconia raw powder by using alcohol solution as a drying medium. Background technique [0002] In recent years, the preparation of nanometer-sized ultrafine particles of inorganic materials has attracted much attention from materials and catalysis scientists. Nanoscale ZrO 2 Because it is a material with high hardness and good toughness, it is widely used in the preparation of various functional ceramic components, such as oxygen sensors, piezoelectric ceramics, pyroelectric ceramics, transparent ferroelectric ceramics and a variety of toughened structural ceramic products, such as Ceramic knives, tools, molds, ceramic valves and advanced ceramic engine parts are the most important raw materials for high-performance special ceramic products. Nanoscale ZrO 2 With the far-infrared emission...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B25/02
Inventor 缪长喜张惠明谢在库陈庆龄
Owner CHINA PETROLEUM & CHEM CORP
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com