High-strength wearable floor rubber and process for preparing same

A wear-resistant floor and rubber technology, which is applied in the field of floor rubber and preparation, can solve the problems of reducing elasticity, anti-skid, cold resistance, wear resistance, increasing product brittleness, slowing down the vulcanization speed, etc., to improve tensile strength and The effect of tear resistance, stable quality and cheap price

Inactive Publication Date: 2006-09-06
恒昌(昆山)精密模具有限公司 +2
View PDF0 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Rubber flooring has become the leading product of floor decoration materials abroad, but the history of domestic rubber flooring is only five or six years, and it is mainly imported, which is expensive
Only a few manufacturers in China are using traditional technology and formula for production. For example, in order to increase the hardness of rubber flooring, the usual method is to increase the proportion of sulfur or use rubber and plastic together. At the same time, it reduces the elasticity, skid resistance, cold resistance and wear resistance of the product, increases the brittleness of the product, slows down the vulcanization speed, and finally makes the quality of the product far from that of foreign countries.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0035] Embodiment: Concrete formula of the present invention is: by mass parts, mainly comprises following composition:

[0036] SBR 60~100 parts

[0037] 40-60 parts of natural rubber

[0038] High styrene content styrene-butadiene rubber 40-60 parts

[0039] 3-8 parts of stearic acid

[0040] Zinc oxide 3~6 parts

[0041] Accelerator 3~7 parts

[0042] Antiaging agent SP-W 0.5~1.5 parts

[0043] Coumarone 3~8 parts

[0044] Chlorinated paraffin 1~2 parts

[0045] Clay 100~200 parts

[0046] White carbon black (gas phase method) 80~120 parts

[0047] Light calcium 100~200 parts

[0048] 3 to 8 parts of coupling agent

[0049] PFM (phenolic resin) 5 to 10 parts

[0050] HMT 0.5~1.0 parts

[0051] Sulfur 5-8 parts

[0052] Decabromodiphenyl ether 5-15 parts

[0053] Antimony trioxide 5-15 parts

[0054] Aluminum hydroxide 30~100 parts.

[0055] Several organic pigments may also be added to the above formulation.

[0056] The preparation process is:

[0057] 1)...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The high-strength flooring rubber mainly comprises (by mass portions) styrene-butadiene rubber 60-100 parts, natural rubber 40-60 parts, butylbenzene rubber with high styrene content 40-60 parts, stearic acid 3-8 parts, zinc oxide 3-6 parts, accelerating agent 3-7 parts, anti-aging agent 0.5-1.5 parts, Coumarone 3-8 parts, paraffin chloride 1-2 parts, pottery clay 100-200 parts, white carbon black 80-120 parts, light calcium 100-200 parts, coupling agent 3-8 parts, phenol resin 5-10 parts, HMT 0.5-1.0 part, sulfur 5-8 parts, decabromodiphenyl oxide 5-15 parts, antimony trioxide 5-15 parts, and aluminum hydroxide 30-100 parts. The preparation consists of plasticization, adaptation, pugging, calendaring, extrusion, modeling and sulfidization.

Description

technical field [0001] The invention relates to floor rubber and a preparation method thereof. Background technique: [0002] Rubber flooring is a kind of ground decoration material in the building materials market, and it is a kind of chemical flooring. It is mainly suitable for public places with high load or super high load, such as hospitals, restaurants, airports, cinemas, supermarkets, shopping malls, beauty salons, entertainment Fields, banks, libraries, computer rooms, gymnasiums, swimming pools, gymnasiums, train and car carriages, office buildings, anti-static workshops, dust-free workshops, etc.; [0003] Rubber flooring has become the leading product of floor decoration materials abroad, but the history of domestic application of rubber flooring is only five or six years, and it is mainly imported and expensive. Only a few manufacturers in China are using traditional technology and formula for production. For example, in order to increase the hardness of rubber ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/08C08L7/02B29C35/02
Inventor 陈正年张荣清
Owner 恒昌(昆山)精密模具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products