Efficient energy-saving kervit microbead insulated sand slurry

A technology of vitrified microbeads and thermal insulation mortar, which is applied in the direction of sustainable waste treatment, solid waste management, and climate sustainability. Efficiency, significant effect, simple operation effect

Inactive Publication Date: 2006-10-25
李珠
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Some thermal insulation mortars are also processed with inorganic substances, such as expanded perlite mortar. Although the physical and chemical properties of this thermal insulation mortar are more stable than those processed with organic substances, their water absorption rate is as high as 200% to 900%. %, the mortar will shrink due to water loss during the setting and hardening process. The stress caused by this shrinkage is the main reason for the hollowing, cracking, cracking and falling off of the mortar. Therefore, the thermal insulation performance will decline during use. From the perspective of heat preservation, this kind of heat preservation mortar has no practical value
[0004] Now some people use vitrified microbeads to process thermal insulation mortar, but due to technical difficulties, its thermal conductivity has been kept at around 0.07W / m.k
Therefore, the insulation performance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Example 1: A high-efficiency and energy-saving vitrified microbead thermal insulation mortar, the components and proportions (weight percentage) of:

[0017] Cement: 32.89%, vitrified beads: 65%, redispersible latex powder: 2%, composite fiber: 0.01%, methyl cellulose ether: 0.1%, air-entraining agent: 0.005%; among them, composite fiber includes The weight percentages of tensile fiber, PP fiber and wood fiber are: tensile fiber 20%, PP fiber 50%, and wood fiber 30%.

[0018] The air-entraining agent is made of acrylic epoxy resin synthetic concrete air-entraining agent, namely SB-G concrete air-entraining agent.

[0019] The redispersible latex powder is ethylene / vinyl acetate / vinyl chloride co-homopolymer powder.

[0020] The preparation process of the above-mentioned composite fiber is as follows: first put the tensile fiber of the above ratio in a stirring device and fully stir it to make it fully puffed, and then add the PP fiber of the above ratio into the stirring de...

Embodiment 2

[0022] Example 2: A high-efficiency and energy-saving vitrified microbead thermal insulation mortar, the components and proportions (weight percentage) are:

[0023] Cement: 65%, vitrified beads: 30%, redispersible latex powder: 5.89%, composite fiber: 0.01%, methyl cellulose ether: 0.1%, air-entraining agent: 0.005%; the composite fiber includes The weight percentages of tensile fiber, PP fiber and wood fiber are: tensile fiber 40%, PP fiber 40%, and wood fiber 20%.

[0024] The air-entraining agent is SK-H air-entraining agent.

[0025] The redispersible latex powder is ethylene / vinyl acetate copolymer powder.

[0026] The preparation process of the above-mentioned composite fiber is as follows: first put the tensile fiber of the above ratio in a stirring device and fully stir it to make it fully puffed, and then add the PP fiber of the above ratio into the stirring device to fully stir it to make it fully puffed Finally, the wood fiber in the above proportion is added to the mi...

Embodiment 3

[0028] Example 3: A high-efficiency and energy-saving vitrified microbead thermal insulation mortar, the components and proportions (weight percentage) are:

[0029] Cement: 50%, vitrified beads: 45.35%, redispersible latex powder: 4%, composite fiber: 0.1%, methyl cellulose ether: 0.5%, air-entraining agent: 0.05%; the composite fiber includes The weight percentages of tensile fiber, PP fiber and wood fiber are: tensile fiber 30%, PP fiber 40%, and wood fiber 30%.

[0030] SJ type air-entraining agent is selected as the air-entraining agent.

[0031] The redispersible latex powder is polyvinyl acetate homopolymer powder.

[0032] The preparation process of the above-mentioned composite fiber is as follows: first put the tensile fiber of the above ratio in a stirring device and fully stir it to make it fully puffed, and then add the PP fiber of the above ratio into the stirring device to fully stir it to make it fully puffed Finally, the wood fiber in the above proportion is added...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention is a high-efficiency, energy-saving, vitrified microball thermal insulation mortar thermal insulation system, comprising: cement, vitrified microballs, re-dispersible latex powder, composite fibers, methyl cellulose ether and air-entraining agent, where the composite fibers include tensile fiber, PP fiber and wood fiber. The invention has antiaging and fireproofing properties, not hollow swelling and cracking, and having high intensity and good binding property, and having heat conductivity coefficient of 0.05W / m.k-0.06W / m.k, saving energy consumption of buildings, applied to new buildings and existing buildings. As constructing, the invention is simple to operate, and the quality is easy to control, able to largely raise construction efficiency and convenient to large-scale spreading and application.

Description

Technical field: [0001] The invention relates to a wall thermal insulation material for buildings, in particular to thermal insulation mortar for wall thermal insulation, in particular to high-efficiency energy-saving vitrified microbead thermal insulation mortar. Background technique: [0002] At present, there are many types of thermal insulation mortars for wall insulation. Among them, most of the thermal insulation mortars are processed by organic materials (such as EPS thermal insulation mortar). This thermal insulation mortar made of organic materials has good thermal insulation properties. , Good chemical resistance and other advantages, but poor workability. In actual construction, there are shortcomings such as low bonding strength and difficult construction. Its physical and chemical properties are also unstable. Moreover, it emits harmful gases and is not resistant to high temperatures. At that time, it becomes a headache of white trash. At the same time, because EPS i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B16/02C04B16/06C04B18/08C04B24/38
CPCY02W30/91
Inventor 李珠刘元珍张泽平
Owner 李珠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap