Calamine viscose fiber and preparation method and application thereof

A viscose fiber, viscose staple fiber technology, applied in the direction of fiber processing, short fiber formation, fiber chemical characteristics, etc., to achieve the effect of good dyeability, spinnability, and good dispersibility

Inactive Publication Date: 2006-12-13
FUJIAN ZHONGHE
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although viscose fiber and calamine have their own characteristics, so far, no one has combined viscose fiber and calamine to make one product have the advantages of both substances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0019] To prepare one ton of viscose filament with a content of 4% calamine, the mother liquor of calamine is first prepared.

[0020] The preparation formula of calamine mother liquor:

[0021] Calamine (average particle size ≤ 1.0 μm): 5%-15%, water: 85%-95%.

[0022] The preparation method of the mother liquor containing 10.0wt% of calamine: in a stainless steel kettle, add 40Kg of calamine and 360Kg of water, stir, mix well, and set aside.

[0023] With above-mentioned mother liquor, continuous blending in injector before spinning with spinning viscose, the weight ratio of blending proportion by the weight of α-Cell (a kind of cellulose) in the fiber gross weight and mother liquor containing calamine powder is 1:0.04, enter the R535A spinning machine (or R535, R535A semi-continuous spinning machine and continuous spinning machine) at the same time for spinning. The doffed silk cake after spinning is processed by pressure washing (or leaching), desulfurization, water wash...

specific Embodiment 2

[0024] To prepare one ton of viscose short fibers with a content of 4% calamine, first prepare a mother liquor of calamine.

[0025] The preparation formula of calamine mother liquor:

[0026] Calamine (≤1.0μm): 5%-15%, water 85%-95%.

[0027] The preparation method of the mother liquor containing 10.0wt% of calamine: in a stainless steel kettle, add 40Kg of calamine and 360Kg of water, stir, mix well, and set aside.

[0028] Above-mentioned mother liquor is blended in dissolving machine with dissolving viscose, and blending ratio is 1: 0.04 by the weight of α-Cell (a kind of cellulose) in the total weight of fiber and the weight ratio containing calamine powder in mother liquor, The blend is stirred, filtered, vacuum defoamed, matured, and then enters the viscose staple fiber spinning machine for spinning. The tow after spinning and forming is desulfurized, washed, pickled, bleached, washed, oiled, cut, dried, and packaged to obtain the required calamine viscose short fiber...

specific Embodiment 3

[0030] To prepare one ton of viscose filament with a content of 2% calamine, first prepare the mother liquor of calamine.

[0031] The preparation formula of calamine mother liquor:

[0032] Calamine (average particle size ≤ 1.0 μm): 5%-15%, water: 85%-95%.

[0033] The preparation method of the mother liquor containing 10.0wt% of calamine: in a stainless steel kettle, add 20Kg of calamine and 180Kg of water, stir, mix well, and set aside.

[0034] With above-mentioned mother liquor, continuous blending in injector before spinning with spinning viscose, the weight ratio of blending proportion by the weight of α-Cell (a kind of cellulose) in the fiber gross weight and mother liquor containing calamine powder is 1:0.02, enter the R535A spinning machine (or R535, R535A semi-continuous spinning machine and continuous spinning machine) at the same time for spinning. The doffed silk cake after spinning is processed by pressure washing (or leaching), desulfurization, water washing,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a calamine cellulose viscose and its process for preparing and application, in which the said fiber contains 1%-6% calamine powder measuring by the gross dry group. The calamine cellulose viscose of this invention not only has the advantages including pure nature, degradability, flexibility and champion dyeing behavior of the cellulose viscose, but also is entitled medicinal and health function, and has multiple physiological activities, which is good for improving the cell vitality and can remove fog and red and can constrict moisture and tumefaction, and simultaneously has distinctive effects including resistance to ultraviolet rays, bacterial inhibition and skin maintenance.

Description

technical field [0001] The invention belongs to the field of textile industry, relates to a calamine viscose fiber, and also relates to a preparation method and application of the calamine viscose fiber. Background technique [0002] Viscose fiber is a regenerated cellulose fiber with the general molecular formula (C 6 h 10 o 5 )n, n is the degree of aggregation. It is made of natural cellulose such as wood, reed, and cotton linters in nature, and is made into soluble cellulose xanthate through alkalization, aging, and yellowing processes, and then dissolved in dilute lye to make viscose. Made by wet spinning. It is one of the first chemical fibers put into industrial production in the world. Viscose fiber is divided into two types: filament and staple fiber. Viscose filament is also called rayon or viscose; and viscose staple fiber has cotton type (also known as artificial cotton), wool type (called artificial wool) and medium and long fibers. Because the properties ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F2/10D01D5/26D01D5/00D02G3/04
CPCD01F1/10D01F2/10
Inventor 刘继涛高炳发许漪许木林
Owner FUJIAN ZHONGHE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com