Synthetic fiber paper containing basalt fiber and chemical fiber and its preparation method

A technology of basalt fiber and synthetic fiber, which is applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, fiber raw material treatment, inorganic fiber/sheet, etc., which can solve the problems of non-water resistance and poor fatigue of fiber paper, and achieve moisture absorption Low durability, good mechanical properties, and strong UV resistance

Active Publication Date: 2007-04-18
LONGPONT
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the use of plant fibers in the composition of this fiber paper, the fiber paper has disadvantages such as no water resistance, no high temperature resistance, oxidation resistance, corrosion resistance, and poor fatigue.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare the present embodiment 1 synthetic fiber paper in the following proportions:

[0025] Basalt fiber (2-4mm) 5 parts by weight (hereinafter referred to as "parts")

[0026] Aramid 1414 fiber (5 ~ 6mm) 45 parts

[0027] Polyphenylene sulfide fiber (5 ~ 6mm) 50 parts

[0028] The basalt fiber of above-mentioned content is decomposed in the hydraulic disintegrating machine by 1% weight concentration, makes paper pulp A, and above-mentioned content aramid fiber 1414 fiber (wherein contains 0~20% pulp) and polyphenylene sulfide fiber by 0.5% by weight The concentration is decomposed in a hydraulic decomposer to make pulp B, and then the slurry A and slurry B are mixed evenly in the batching tank, and 5 parts of anti-flocculant are added to the pulp stabilization box. Adjust the pressure head of the slurry through the headbox, and the slurry is evenly distributed on the paper forming wire (double circle wire) in the headbox, and then the paper sheet is hot-rolled and ...

Embodiment 2

[0031] Prepare the present embodiment 2 synthetic fiber paper by following parts by weight:

[0032] Basalt fiber (2 ~ 4mm) 5 parts

[0033] Aramid 1313 fiber (5 ~ 6mm) 45 parts

[0034] Polyphenylene sulfide fiber (5 ~ 6mm) 50 parts

[0035] In this embodiment, aramid 1313 fiber (containing 0-20% precipitated fiber) is used to replace aramid 1414 fiber. The preparation method of synthetic fiber paper is the same as that of Example 1, and the results obtained are shown in Table 2:

[0036] Table 2

[0037] project

Embodiment 3

[0039] Prepare the present embodiment 3 synthetic fiber papers by following parts by weight:

[0040] Basalt fiber (6 ~ 8mm) 25 parts

[0041] Aramid 1414 fiber (5 ~ 6mm) 25 parts

[0042] Polyphenylene sulfide fiber (5 ~ 6mm) 50 parts

[0043] In Example 3, without changing the dosage of 50 parts of polyphenylene sulfide fiber, the weight of basalt fiber was increased to 25 parts, the weight of aramid fiber 1414 was reduced to 25 parts, and the remaining steps were carried out according to the same preparation method as in Example 1. The obtained test results are shown in Table 3:

[0044] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of composing fiber paper. It relates to composing non-woven paper, especially relates to a kind of fiber paper made by wet method with basaltic fiber, aramid fiber and polyphenylene sulfide fiber. The composing fiber paper has much strongpoint including well mechanical property, good high-temperature resistance, acid resistance, alkali resistance, strength uvioresistant property, low hygroscopic, better environment bearing property, good insulativity, good high-temperature filterability, radio resistance and good wave-passing property. Therefore, the composing fiber paper is applicable for military engineering and civil fields including aerospace, military engineering, vehicle and ship building and architecture.

Description

technical field [0001] The invention belongs to the field of synthetic fiber paper and relates to a synthetic non-woven paper structure, in particular to a fiber paper made of basalt fiber, aramid fiber and polyphenylene sulfide fiber by wet method. [0002] The present invention also relates to a method for preparing the above-mentioned synthetic fiber paper. Background technique [0003] With the development of material science, the performance requirements of paper are increasing day by day, and synthetic fiber paper has been widely concerned because of its advantages such as higher strength than ordinary plant fiber paper, stable size, not easy to aging, and chemical corrosion resistance. In the prior art, synthetic fiber paper made of non-woven paper structure is known, as disclosed in the Chinese patent of Patent No. ZL99114635.2, a synthetic fiber paper made of polyaramid synthetic fiber as raw material, This patent describes a method for making synthetic paper with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H13/26D21H13/38
Inventor 陶世毅衡沛之王丽萍陈连均
Owner LONGPONT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com