Polyvinyl alcohol hollow container preparation method

A polyvinyl alcohol, hollow technology, applied in the direction of hollow objects, applications, household appliances, etc., can solve the problems of difficult preparation of hollow containers, low decomposition temperature, etc., and achieve the effects of low cost, improved barrier performance, and convenient operation

Active Publication Date: 2007-05-16
SICHUAN UNIV
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This is because polyvinyl alcohol is a crystalline polymer with a large number of hydroxyl groups in the molecule, which can form a large number of intramolecular and intermolecular hydrogen bonds, making its melting point as high as 220-240 ° C, but the decomposition temperature is low, and dehydration begins at 160 ° C. Chemical, starting to decompose at 200°C, and decomposes immediately during the melting process, no thermoplastic processing window, difficult to prepare hollow containers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] 1. Dissolve 1 kg of ethylene glycol and 0.1 kg of aminocaproic acid in 20 kg of deionized water, mix them into a uniform solution, then add 50 kg of polyvinyl alcohol with a degree of polymerization of 1750 and a degree of alcoholysis of 99 mol%, and stir at a temperature of 20 Swells at °C. Melt and plasticize the extruded parison in an extruder at a temperature of 60-125°C, stretch it axially to 1.5, blow it into a container in a mold at a temperature of 10°C, and use a 5% organic titanate solution After cross-linking treatment at a temperature of 80° C. for 1 minute, heat treatment was performed at a temperature of 200° C. for 3 minutes.

[0024] 2. Dissolve 15kg of butanediol and 10kg of triethanolamine salt in 50kg of deionized water, mix to form a uniform solution, then add 80kg of polyvinyl alcohol with a degree of polymerization of 1700 and a degree of alcoholysis of 92mol%, and stir at a temperature of 60°C Swell, then add 3.5kg polyethylene wax, 1kg polyacryl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing polyvinyl alcohol hollow container, wherein it is characterized in that: it dissolves the modifier with compensated structure to the polyvinyl alcohol at 1-25deals into 20-50deals of deionized water, mixing, adding 50-80deals of polyvinyl alcohol, expanding at 20-60Deg. C, adding additives at 0-5deals, mixing, injection molding at injection device whose thermal treatment temperature is 60-170Deg. C and mould temperature is 10-150Deg. C, into hollow container; thermally processing at 40-250Deg. C or infrared drying for 3-120Deg. C, to improve the crystal degree, or at 20-80Deg. C, using crosslink solution whose density is 0.1-5% to treat it for 1-60min; thermally treating or infrared drying, to obtain the product with better insulated, physical and damp-proof properties.

Description

technical field [0001] The invention relates to a polyvinyl alcohol hollow container and a preparation method thereof. More specifically, the invention relates to modifying polyvinyl alcohol with a modifier having a complementary structure to polyvinyl alcohol, and preparing a polyvinyl alcohol hollow container with excellent barrier performance by melt blow molding, which belongs to the field of polymer processing. Background technique [0002] Plastic containers have good mechanical properties, light weight, and are easy to process and shape, and are widely used in the production of hollow containers. However, most plastic containers have poor barrier properties to non-polar solvents. In order to improve their barrier properties, researches have been done both at home and abroad. Mixed material (CN1754908A); Sinopec Group Qilu Petrochemical Company Chen Yongfen etc. disclose a kind of polyethylene / ethylene-vinyl alcohol copolymer high barrier layered hollow container (CN ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C49/78B29C71/02B29C71/04B29C71/00C08L27/06C08K5/3492B29L22/00C08L3/02C08L1/00C08L33/08C08L71/00C08L33/26C08K3/00C08K5/205C08K5/00
Inventor 王琪李莉杨芳熊宪辉
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com