Thermosetting water-based coating composition and method of forming coating film

A composition and thermosetting technology, applied in multi-color effect coatings, coatings, devices for coating liquids on surfaces, etc., can solve problems such as difficulty in uniformly distributing colored pigments and obtaining good colors

Inactive Publication Date: 2007-06-27
KANSAI PAINT CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when a large proportion of the emulsion resin is used in a metal coating composition containing the emulsion resin and the water-soluble resin to avoid sagging of the resulting coating film, since the coating film contains a large proportion of the continuous phase derived from the water-soluble resin The resin particles of the emulsion method, the result makes it difficult to uniformly distribute the coloring pigment
So it's hard to get a good color in this case

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting water-based coating composition and method of forming coating film

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0192] Production Example 1 Production of Hydroxyl and Carboxyl Water-Soluble Resin (A)

[0193] Put 35 parts of propylene glycol monopropyl ether in a flask and heat it to 85°C, then add 30 parts of methyl methacrylate, 20 parts of 2-ethylhexyl acrylate, 29 parts of n- A mixture of butyl ester, 15 parts of hydroxyethyl acrylate, 6 parts of acrylic acid, 15 parts of propylene glycol monopropyl ether and 2.3 parts of 2,2'-azobis(2,4-dimethylvaleronitrile). After the addition was complete, the resulting mixture was aged for 1 hour. Next, a mixture of 10 parts of propylene glycol monopropyl ether and 1 part of 2,2'-azobis(2,4-dimethylvaleronitrile) was additionally added dropwise to the flask over 1 hour. After the addition was complete, aging was performed for 1 hour. The aged mixture was neutralized with 7.4 parts of diethanolamine to obtain a 55% solution of water-soluble acrylic resin (A-1) having a weight average molecular weight of 58,000, a hydroxyl value of 72 mg KOH / g ...

manufacture example 4

[0199] Production Example 4 Production of Phthalocyanine Blue Pigment Paste

[0200] In a 225 ml glass bottle, 16.7 parts of phthalocyanine blue pigment (trade name "CYANINEBLUE G-314", product of Sanyo Color Works, Ltd.), 16.7 parts of water-soluble acrylic resin (A -1) solution and 80.8 parts of deionized water. In addition, 130 g of glass beads having a diameter of 1 mm were added as a dispersion medium, followed by dispersion for 1 hour with a paint shaker. The glass beads were then removed to obtain phthalocyanine blue pigment paste (ii).

Embodiment 1

[0201] The manufacture of embodiment 1 thermosetting waterborne metal coating composition

[0202] A solution of 50 parts by solid of the water-soluble acrylic resin (A-1) obtained in Production Example 1, 10 parts by solid of the internally crosslinked acrylic emulsion method resin (D1-1) obtained in Production Example 2 , 30 parts by solids of melamine resin (trade name "Cymel 325", product of Mitsui Cytec, Ltd.) and 10 parts by solids of urethane emulsion method resin (trade name "U-COAT UX8100", product of Sanyo Chemical Industries , Ltd.) mixed together. Next, it was mixed with 15 parts by solid of the aluminum flake dispersion (i) obtained in Production Example 3.

[0203] The resulting mixture was diluted with deionized water to a solid content of 20%, to obtain a thermosetting water-based silver metal coating composition WM-1. The coating composition at 20°C and 1 sec -1 has a viscosity of 220mPa·s at a shear rate of 20°C and 100 seconds -1 It has a viscosity of 12...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

A thermosetting water-based coating composition which comprises (A) 100 parts by weight of a hydroxylated and carboxylated water-soluble resin having a weight-average molecular weight of 500-200,000, a hydroxy value of 1-200 mg-KOH / g, and an acid value of 10-100 mg-KOH / g and (B) 10-100 parts by weight of a brightening pigment and which is to be applied so as to give a cured film having a thickness of 3,000-8,000 nm, characterized in that the viscosity of the coating film applied which has a solid concentration of 40 wt.% is in the range of 4*102 to 1*104 mPa.s as measured at 20 DEG C and a shear rate of 0.1 sec-1. Also provided is a method of coating film formation which comprises using the coating composition.

Description

technical field [0001] The present invention relates to a thermosetting water-based coating composition and a method for forming a coating film. Background technique [0002] When forming an outer coating comprising one or two base coats and one or two clear coats on a substrate such as an automobile body by a two-coat-and-bake method, a three-coat-and-bake method, etc., a thermosetting water-based The coating composition forms a base coat. [0003] In recent years, the thermosetting aqueous coating composition has been required to be capable of forming a coating film with a high-quality appearance. Specifically, when the coating composition has a silver metallic color, the coating composition is required to be capable of forming a coating film having excellent brilliance (brilliance) and excellent flip-flop properties. Angle-dependent light fall refers to the difference in whiteness (brightness) between the surface of the coating film seen from the front (highlighted part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/02B05D1/36B05D5/06B05D7/24C09D5/02C09D5/29C09D7/12C09D133/00
CPCC09D133/02C08J7/047C09D201/06C09D5/29C08L2312/00C08J7/0427
Inventor 桧原笃尚成田信彦
Owner KANSAI PAINT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com