Efficient energy-saving kervit microbead insulated sand slurry

A technology of vitrified microbeads and thermal insulation mortar, which is applied in the field of thermal insulation mortar for wall insulation and high-efficiency energy-saving vitrified microbead thermal insulation mortar. Simple, improve construction efficiency, and remarkable effect

Inactive Publication Date: 2007-10-31
李珠
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Some thermal insulation mortars are also processed with inorganic substances, such as expanded perlite mortar. Although the physical and chemical properties of this thermal insulation mortar are more stable than those processed with organic substances, their water absorption rate is as high as 200% to 900%. %, the mortar will shrink due to water loss during the setting and hardening process. The stress caused by this shrinkage is the main reason for the hollowing, cracking, cracking and falling off of the mortar. Therefore, the thermal insulation performance will decline during use. From the perspective of heat preservation, this kind of heat preservation mortar has no practical value
[0004] Now some people use vitrified microbeads to process thermal insulation mortar, but due to technical difficulties, its thermal conductivity has been kept at around 0.07W / m.k
Therefore, the insulation performance is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1: A kind of high-efficiency and energy-saving vitrified microbead thermal insulation mortar, its component and proportioning (weight percentage) are:

[0017] Cement: 32.89%, vitrified microspheres: 65%, redispersible latex powder: 2%, composite fiber: 0.01%, methyl cellulose ether: 0.1%, air-entraining agent: 0.005%; among them, composite fiber composition It is tensile fiber, PP fiber and wood fiber, and its weight percentage is: 20% of tensile fiber, 50% of PP fiber, and 30% of wood fiber.

[0018] The air-entraining agent is selected from acrylic epoxy resin synthetic air-entraining agent for concrete, that is, SB-G concrete air-entraining agent.

[0019] The redispersible latex powder is made of ethylene / vinyl acetate / vinyl chloride co-homopolymer powder.

[0020] The preparation process of the above-mentioned composite fiber is as follows: First, put the tensile-resistant fiber in the above proportion in the mixing equipment and stir it fully to make ...

Embodiment 2

[0022] Embodiment 2: A kind of high-efficiency and energy-saving vitrified microbead thermal insulation mortar, its component and proportion (weight percentage) are:

[0023] Cement: 65%, vitrified microspheres: 30%, redispersible latex powder: 5.89%, composite fiber: 0.01%, methyl cellulose ether: 0.1%, air-entraining agent: 0.005%; among them, composite fiber composition It is tensile fiber, PP fiber and wood fiber, and its weight percentage is: 40% of tensile fiber, 40% of PP fiber, and 20% of wood fiber.

[0024] The air-entraining agent is SK-H air-entraining agent.

[0025] The redispersible latex powder is made of ethylene / vinyl acetate copolymer powder.

[0026] The preparation process of the above-mentioned composite fiber is as follows: First, put the tensile-resistant fiber in the above proportion in the mixing equipment and stir it fully to make it fully puffed, then add the PP fiber in the above proportion into the mixing equipment and stir fully to make it fully...

Embodiment 3

[0028] Embodiment 3: A kind of high-efficiency energy-saving vitrified microbead thermal insulation mortar, its component and proportioning (weight percentage) are:

[0029] Cement: 50%, vitrified microbeads: 45.35%, redispersible latex powder: 4%, composite fiber: 0.1%, methyl cellulose ether: 0.5%, air-entraining agent: 0.05%; among them, composite fiber composition It is tensile fiber, PP fiber and wood fiber, and its weight percentage is: 30% of tensile fiber, 40% of PP fiber, and 30% of wood fiber.

[0030] The air-entraining agent is SJ type air-entraining agent.

[0031] The redispersible latex powder is polyvinyl acetate homopolymer powder.

[0032] The preparation process of the above-mentioned composite fiber is as follows: First, put the tensile-resistant fiber in the above proportion in the mixing equipment and stir it fully to make it fully puffed, then add the PP fiber in the above proportion into the mixing equipment and stir fully to make it fully puffed Fina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention is a high-efficiency, energy-saving, vitrified microball thermal insulation mortar thermal insulation system, comprising: cement, vitrified microballs, re-dispersible latex powder, composite fibers, methyl cellulose ether and air-entraining agent, where the composite fibers include tensile fiber, PP fiber and wood fiber. The invention has antiaging and fireproofing properties, not hollow swelling and cracking, and having high intensity and good binding property, and having heat conductivity coefficient of 0.05W / m.k-0.06W / m.k, saving energy consumption of buildings, applied to new buildings and existing buildings. As constructing, the invention is simple to operate, and the quality is easy to control, able to largely raise construction efficiency and convenient to large-scale spreading and application.

Description

Technical field: [0001] The invention relates to a building wall thermal insulation material, in particular to thermal insulation mortar for wall thermal insulation, in particular to high-efficiency energy-saving vitrified bead thermal insulation mortar. Background technique: [0002] At present, there are many types of thermal insulation mortar for wall insulation, and most of them are made of organic matter (such as EPS thermal insulation mortar). This kind of thermal insulation mortar processed by organic matter has good thermal insulation properties. , good chemical corrosion resistance, etc., but poor workability, there are disadvantages such as low bond strength and difficult construction in actual construction, its physical and chemical properties are also unstable, and it will emit harmful gas itself, not resistant to high temperature, and it is not used when it is discarded. When it is time, it becomes a headache of white garbage. At the same time, because EPS is a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B18/08C04B24/38C04B16/06C04B16/02
CPCY02W30/91
Inventor 李珠刘元珍张泽平
Owner 李珠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap