Concrete water reducing agent of polyacrylic acid and its synthesis process

A concrete water reducer and synthesis process technology, which is applied in the field of polyacrylic acid-based high-efficiency water reducer and synthesis process, can solve the problems of complex production process and high equipment requirements of water reducer, and achieve good appearance quality and good anti-segregation performance , No bleeding line effect

Inactive Publication Date: 2008-01-09
WUHAN UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] From the above three patents, it can be seen that the production process of water reducing agent is very complicated, and the reaction process requires high equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete water reducing agent of polyacrylic acid and its synthesis process
  • Concrete water reducing agent of polyacrylic acid and its synthesis process
  • Concrete water reducing agent of polyacrylic acid and its synthesis process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1: Get the best matching ratio

[0050] Put 40.00g of polyethylene glycol with a molecular weight of 400, 8.4g of acrylic acid, 0.25g of hydroquinone, 1.5g of p-toluenesulfonic acid, and 200g of cyclohexane into a reaction vessel, stir at a temperature of 60°C, and wait for the After hydroquinone and p-toluenesulfonic acid are completely dissolved, then keep the temperature at 80-90°C and react for 8 hours, then filter, vacuumize and remove cyclohexane to obtain polyethylene glycol monoacrylate; add 54.41g of water into a three-necked flask and Control the temperature at 85±5°C, then add 46.80g of the esterification product of the first step, 14g of acrylic acid and 9.16g of sodium 2-acrylamide-2-methylpropenesulfonate, add 54.41g of water to dissolve and mix for dripping, 1.19 g of ammonium persulfate and 1.62 g of mercaptoethanol were dissolved in 54.41 g of water, and the three were added dropwise to the three-necked flask at a controlled rate, so that the...

Embodiment 2

[0052] Put 40.00 g of polyethylene glycol with a molecular weight of 400, 10.5 g of acrylic acid, 0.26 g of hydroquinone, 2.65 g of p-toluenesulfonic acid, and 210 g of cyclohexane into a reaction vessel, and stir at a temperature of 60°C. After hydroquinone and p-toluenesulfonic acid are completely dissolved, then keep the temperature at 80-90°C and react for 8 hours, then filter, vacuumize and remove cyclohexane to obtain polyethylene glycol monoacrylate; add 55.84 g of water into a three-necked flask and Control the temperature at 85±5°C, then add 46.80g of the esterification product of the first step, 14g of acrylic acid and 10.99g of sodium 2-acrylamide-2-methylpropenesulfonate, add 55.84g of water to dissolve and mix until dripping, 1.19 g of ammonium persulfate and 1.62 g of mercaptoethanol were dissolved in 55.84 g of water, and the three were added dropwise to the three-necked flask at a controlled rate, so that the drops were completed within 2±0.5 hours, and the reac...

Embodiment 3

[0054] Put 40.00 g of polyethylene glycol with a molecular weight of 400, 8.4 g of acrylic acid, 0.25 g of hydroquinone, 1.51 g of p-toluenesulfonic acid, and 200 g of cyclohexane into a reaction vessel, and stir at a temperature of 60°C. After hydroquinone and toluenesulfonic acid are completely dissolved, then keep the temperature at 110-115°C and react for 8±0.5 hours, then filter, vacuumize and remove cyclohexane to obtain polyethylene glycol monomethacrylate; add 60.92g of water There is a three-necked flask and the temperature is controlled at 85±5°C, then add 46.80g of the esterification product of the first step, 22.36g of acrylic acid and 9.16g of sodium 2-acrylamide-2-methylpropenesulfonate, and add 60.92g of water to dissolve them Mix, dissolve 1.19 g of ammonium persulfate and 1.62 g of mercaptoethanol in 60.92 g of water, and add the three to the three-necked flask at a controlled rate dropwise, so that the drops are completed within 2±0.5 hours, and the reaction i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
slumpaaaaaaaaaa
Login to view more

Abstract

The concrete water reducing agent of polyacrylic acid is prepared through esterification between polyglycol and acrylic acid to obtain esterified product, and the copolymerization of the esterified product with acrylic acid, 2-acrylamide-2-methyl propenyl sodium sulfonate and other sulfonate with unsaturated double bond. The concrete water reducing agent has weight average molecular weight of 20000-60000, concrete water reducing rate over 35 %, concrete compression strength raised by 100-300 % in 3 days, 40-80 % in 28 days and 30-50 % in 90 days, no loss in 2-hr slump of concrete, raised concrete placeability, etc. and is suitable for matching with flyash, slag and other active admixture to prepare high performance concrete.

Description

technical field [0001] The invention belongs to a polyacrylic acid series high-efficiency water reducer and a synthesis process. Background technique [0002] Acrylic water reducer is the third generation of water reducer. In the past, cement dispersants used to improve fluidity commonly used naphthalene sulfonic acid formaldehyde condensate salt, melamine sulfonic acid formaldehyde high condensate salt, p-aminobenzenesulfonate, water-soluble Cement dispersant such as ethylene copolymer. Concrete mixtures of cement dispersants such as naphthalenesulfonic acid formaldehyde condensate salt, melaminesulfonic acid formaldehyde high condensate salt, p-aminobenzenesulfonate and other cement dispersants have the problems of low water reducing rate and large slump loss; water-soluble ethylene Although the slump loss of the copolymer cement dispersant is small, the setting time is greatly prolonged, resulting in low early strength. At present, my country's concrete superplasticizer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/26C04B103/30
Inventor 廖国胜曾勤
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap