Environment protection type single-component polyurethane binder, production and use method of the same

A polyurethane adhesive, one-component technology, used in polyurea/polyurethane adhesives, adhesive types, adhesives, etc., can solve problems such as irritating odor, less human harm, and respiratory system damage

Active Publication Date: 2008-02-27
SHANDONG INOV POLYURETHANE
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing domestic plastic runway products are basically TDI type. Due to the high vapor pressure of TDI (1.33Pa, 20°C), there is a strong pungent smell, which is easy to damage the human respiratory system during construction and use. deals damage, and MDI has a low vapor pressure (1.5×10 -4 Pa, 20°C), basically odorless and less harmful to the human body, so it is recommended by IST

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] DL-3000: 70; pure MDI: 27; UV-9: 1; BHT: 1, bismorpholine diethyl ether: 1, phosphoric acid: 20ppm by total mass.

[0020] Preparation: Add polyether polyol to the reaction kettle at room temperature, stir at 80°C-100°C, vacuum (-0.09MPa) for dehydration and degassing for 2-3 hours, cool down to 40°C and add diphenylmethane diisocyanate (Pure MDI), UV-9, BHT, phosphoric acid, react at 80-85°C for 2-3 hours, cool down to 40°C, add bismorpholine diethyl ether, and pack into barrels.

[0021] During construction, the adhesive and rubber particles are evenly mixed in a weight ratio of 15:100, paved, and cured (dried) at room temperature.

Embodiment 2

[0023] DL-2000: 60; pure MDI: 20; liquefied MDI: 15, UV-9: 2; BHT: 2, bismorpholine diethyl ether: 1, phosphoric acid: 20PPM according to the total mass

[0024] Preparation: Add polyether polyol to the reaction kettle at room temperature, stir at 80°C-100°C, vacuum (-0.09MPa) dehydration and degassing for 2-3 hours, cool down to 40°C, add pure MDI, liquefy MDI, Add UV-9, BHT, phosphoric acid, react at 80-85°C for 2-3 hours, cool down to 40°C, add bismorpholine diethyl ether, and load into barrels.

[0025] During construction, the adhesive and rubber particles are evenly mixed according to the weight ratio of 20:100, paved and cured (dried).

Embodiment 3

[0027] DL-3000: 40; DL-2000: 30; pure MDI: 27; UV-9: 1; BHT: 1, bismorpholine diethyl ether: 1, benzoyl chloride: 20PPM according to the total mass

[0028] Preparation: Add polyether polyol to the reaction kettle at room temperature, stir at 80°C-100°C, vacuum (-0.09MPa) for dehydration and degassing for 2-3 hours, cool down to 40°C and add diphenylmethane diisocyanate , add UV-9, BHT, benzoyl chloride, react at 80-85°C for 2-3 hours, cool down to 40°C, add bismorpholine diethyl ether, and load into barrels.

[0029] During construction, the adhesive and rubber particles are evenly mixed according to the weight ratio of 18:100, paved and cured (dried).

[0030] The performance of the example is compared with the national standard as follows:

[0031] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elastic recovery rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly type monocomponent polyurethane adhesive to pave gas permeable playground, which comprises the following parts: isocyanate, polyether polyol, age resister, ultraviolet absorbent, dimorpholine ether catalyst and polymerization inhibitor, wherein the polyether polyol is polypropene oxide polyol, which is selected from one or more components of DL-2000, DL-3000, MN-3050 or 330N; the isocyanate is diphenyl methane diisocyanate; the adhesive and rubber particle are blended evenly with weight rate at 15-20: 100 to be paved and solidified (dried). The invention is superior to international index of runway, which is especially for paving indoor playground.

Description

technical field [0001] The present invention relates to an environment-friendly one-component polyurethane adhesive suitable for laying indoor sports grounds and its preparation method, more precisely an environment-friendly one-component polyurethane that does not contain TDI (toluene diisocyanate) and toxic catalysts adhesive. Background technique [0002] Polyurethane rubber sports field (referred to as plastic sports field) has the characteristics of good elasticity, wear resistance, non-slip, and not affected by weather conditions. It is popular with the public and is also the development direction of modern sports field construction. [0003] With the enhancement of people's awareness of environmental protection, the environmental protection requirements for sports venues are also increasingly strong. As early as 1994, IST (International Sports Track Technology Association) proposed "do not accept monomeric TDI components" for the problem of "using polyurethane resin t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/08C09D121/00
Inventor 孙清峰李健栾森鞠伟坦
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com