A technology of hot-dip galvanizing and products, applied in hot-dip galvanizing process, coating, metal material coating process, etc., can solve the problems of excessive consumption of zinc and low efficiency of heating system, so as to reduce zinc consumption and stabilize heat. Loss and effect of reducing the amount of dross
Active Publication Date: 2010-09-15
SHANGHAI YONGFENG HOT DIP GALVANIZING
View PDF2 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The technical problem to be solved by the present invention is to provide a hot-dip galvanizing method for iron and steel products that is applied to defects such as excessive consumption of zinc and low efficiency of the heating system in the conventional process of hot-dip galvanizing
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] Zinc pot volume: 16.2×2.5×3.6m 3 , Heating method: electric heating on both sides Steel products: 80kg / piece
[0026] 1) Cleaning of black parts: degrease steel products and remove pollutants;
[0027] 2) pickling: immerse the cleaned iron and steel products into the pickling tank, the pickling solution is hydrochloric acid aqueous solution, the working concentration is 10%, the working temperature is room temperature, and the weight ratio of ferric chloride in the pickling solution is controlled to be 150 grams per liter , pickled for 35 minutes, rinsed into ready-made products;
[0028] 3) Helper treatment: the helper solution is an aqueous solution of ammonium chloride and zinc chloride, and its mass ratio is
[0029] Ammonium Chloride 15%
[0030] Zinc Chloride 11%
[0031] Aqueous solution 74%
[0032] The working temperature is 65°C, the pH value is 5, and the content of ferric chloride in the plating flux is controlled at 2.5 g / L.
[0033] Immerse the produ...
Embodiment 2
[0037] Zinc pot volume: 16.2×2.5×3.6m 3 , Heating method: Gas heating on both sides Steel products: 400kg / piece
[0038] 1) Cleaning of black parts: degrease steel products and remove pollutants;
[0039] 2) pickling: immerse the cleaned iron and steel products into the pickling tank, the pickling solution is hydrochloric acid aqueous solution, the working concentration is 12%, the working temperature is room temperature, and the weight ratio of ferric chloride in the pickling solution is controlled to be 180 grams per liter , pickled for 50 minutes, rinsed into ready-made products;
[0040] 3) Helper treatment: the helper solution is an aqueous solution of ammonium chloride and zinc chloride, and its mass ratio is
[0041] Ammonium Chloride 18%
[0042] Zinc Chloride 13%
[0043] Aqueous solution 69%
[0044] The working temperature is 75°C, the pH value is 4.5, and the content of ferric chloride in the plating flux is controlled at 4 g / L.
[0045] Immerse the product t...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a hot dip galvanizing method for the steel product, which belongs to the hot dip galvanizing engineering in the metallurgy field. The invention mainly solves the technical problem that the hot dip galvanizing method which is utilized for the steel product for directly aiming at the faults of excessive consumption of the zinc and low efficiency utilization of the heating system in the normal hot dip galvanizing process is provided. The heating way of the dip galvanizing kettle of the invention is side surface heating, thus, the temperature of the liquid zinc can be conveniently controlled, the deposition of the zinc dross can be accelerated, and the zinc quantity taken away by the galvanizing piece can be reduced; because the ferric salt content inside the assistant galvanizing tank is controlled, the zinc dross quantity inside the zinc kettle is reduced; simultaneously, the output per hour is controlled to stabilize the heat loss and reduce the increased zinc consumption caused by temperature variation. Through the progress of the process, the zinc consumption is reduced, the heat energy is fully utilized, the faults of excessive zinc consumption and low efficiency utilization coefficient of the heating system caused by normal process are overcome, the quality is ensured, simultaneously, the resources are saved.
Description
technical field [0001] The invention relates to hot-dip galvanizing in the field of metallurgy, in particular to a hot-dip galvanizing method for iron and steel products. Background technique [0002] The anti-corrosion coating of steel products includes electroplating, hot-dip galvanizing and other methods. The hot-dip galvanizing process of steel products has been a conventional and commonly used method. The energy consumption in the process has also been paid attention to. Because the conventional process is too old, it has caused defects such as excessive consumption of zinc and low efficiency of the heating system. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a hot-dip galvanizing method for iron and steel products that is applied to defects such as excessive consumption of zinc and low utilization of heating systems caused by conventional hot-dip galvanizing processes. [0004] The technical solution pr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more