Manufacturing process of negative ion far infrared multifunctional ceramic decorative ground and wall brick

A kind of negative ion far-infrared, production process technology, applied in the field of building ceramic bricks, to achieve the effect of eliminating fatigue, promoting human bones, and activating human cells

Inactive Publication Date: 2008-12-24
牛崇光
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, no such floor tiles have been found at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Add the prepared ceramic glaze additive (the additive includes Sogo stone and tourmaline) to the floor and wall tile ceramic glaze in a proportion of 10% by mass to make a functional glaze, and then put the functional glaze into the system. Grind in the glaze ball mill for 72 hours, pass through the high-strength iron removal and filtration process before use;

[0013] After drying the prepared floor and wall bricks, spray glaze on the surface of the floor and wall bricks with functional glaze, and then put them into a tunnel kiln for firing at a high temperature of 1000°C, and then make finished products out of the kiln. The produced functional floor and wall tiles release 506-1000 negative ions per square centimeter per second. The production of the functional floor and wall tiles does not need to change the original production process, and does not need to change the composition and formula of the original glaze. The production process is simple, the cost is low, an...

Embodiment 2

[0015] Compared with Example 1, in this example, the mass percentage of the ceramic glaze additive is 18%, the time for the functional glaze to be put into the glaze ball mill for grinding is 50 hours, and the temperature of the tunnel kiln is 1100°C.

Embodiment 3

[0017] Compared with Example 1, in this example, the mass percentage of the ceramic glaze additive is 30%, the time for the functional glaze to be put into the glaze ball mill for grinding is 24 hours, and the temperature of the tunnel kiln is 1200°C.

[0018] The sogo stone of the present invention is a paleontological fossil. Its surface is microporous, its Mohs hardness is 3.4-4, and its density is about 3.7g / cm 3 , produced in the Qinghai-Tibet Plateau region of my country. In Tibet and other areas, it is also commonly known as heaven stone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fabrication technology of a negative ion far infrared multifunctional ceramic decorative ground-wall tile belonging to the ceramic field, which comprises the following steps: (1) adding a 10%-30% of prepared ceramic glaze additive according to the weight percentage into the ground-wall tile ceramic glaze to prepare a functional glaze, milling the functional glaze in a glaze-making ball mill for 24-72 hours, high-intensively removing iron and filtering the glaze for standby; (2) spraying glaze on surface of the ground-wall green tile using functional glaze after drying the prepared ground-wall green tile, then sintering the ground-wall green tile in a tunnel kiln at a high temperature of 1000-1200 DEG C, preparing the finished product after taking the ground-wall tile out of the kiln. The ceramic product of the invention has multiple functions such as permanent release of anion, emission of far infrared, deodorization, self-cleaning, antibacterial and air purification. At the same time the ceramic glaze surface contains a plurality of minerals and microelements germanium and strontium.

Description

technical field [0001] The invention belongs to the field of ceramics, and in particular relates to a building ceramic brick. Background technique [0002] In modern society, indoor pollution has seriously threatened human health. Indoor pollution mainly refers to formaldehyde, benzene, ammonia, and radon produced by building decoration materials; electromagnetic waves and radiation from indoor household appliances; combustion of coal, liquefied petroleum gas, and natural gas; smoke generated during high-temperature cooking processes such as frying and baking ; Pollutants such as viruses and bacteria on pets destroy the family's daily life environment and affect people's health. With the improvement of people's living standards and living tastes, people pay more and more attention to the environment optimization and purification of public places, living spaces, daily life and medical facilities. Ceramic products, especially building ceramic products such as floor tiles and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 牛崇光牛振
Owner 牛崇光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com