Coking additive agent and use thereof
A technology for coal additives and uses, applied in the field of coking additives, can solve the problems of adverse effects of coke blast furnace operation, increased cost, poor cohesion, etc., and achieves the effect of ensuring large-scale long-term use, safe mixing and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] Embodiment 1 The preparation of coke additive of the present invention
[0016] Take SiO with a purity of 99% 2 , using a ball mill to grind into a powder that can pass through a 100-mesh sieve, and wherein 80% by weight can pass through a 200-mesh sieve. Set aside.
Embodiment 2
[0017] Example 2 Preparation of coke using traditional techniques
[0018] Mixed coal ratio: 20% of Pakistan coking coal, 10% of grid coking coal, 10% of Guizhou coal, 5% of Fuyuan coal, 25% of Huaping coal, 10% of suburban coal, 5% of Longchang coal, 5% of Guangrong coal, and 10% of lean coal %, with coal moisture content of 10.3%. Take 400g of mixed coal, put it into a corundum crucible (Φ80mm×110mm), and then use a 3kg weight to compact the mixed coal in the crucible for 5 minutes, remove the counterweight and seal it, and put it into a muffle furnace (400mm×150mm×200mm) Dry distillation, heating rate 18°C / min, heating up to 1100°C, constant temperature for 100min, taking out water to quench the coke, cooling and crushing into particles with a particle size of 5-10mm for thermal reactivity (the thermal reactivity measurement method refers to the national standard GB / T4000-1996, in Put 20g coke sample into the reactor, and when the temperature of the center of the material ...
Embodiment 3
[0019] Example 3 Preparation of coke using the coke additive of the present invention
[0020] Mixed coal ratio: 20% of Pakistan coking coal, 10% of grid coking coal, 10% of Guizhou coal, 5% of Fuyuan coal, 25% of Huaping coal, 10% of suburban coal, 5% of Longchang coal, 5% of Guangrong coal, and 10% of lean coal %, with coal moisture content of 10.3%. Mixed coal 400g, SiO 2 2g(SiO 2 Granularity -200 mesh accounts for 90%, purity 99%) and mix well, put it into a corundum crucible (Φ80mm×110mm), and then use 3kg weight to compact the coal in the crucible for 5min, remove the counterweight and seal, put Dry distillation in a muffle furnace (400mm×150mm×200mm), the heating rate is 18°C / min, the temperature is raised to 1100°C, the temperature is kept constant for 100min, the water is taken out to quench the coke, and after cooling, it is crushed into a particle size of 5-10mm for thermal reactivity (thermal reactivity) The measurement method refers to the national standard GB...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com