Preparation of synthetic rutile

An artificial rutile, oxidation roasting technology, applied in the direction of titanium dioxide, titanium oxide/hydroxide, etc., can solve the problems of ineffective removal, low grade of artificial rutile, unsuitable for titanium tetrachloride, etc., and achieve easy control and reduce energy consumption , to avoid the effect of local overheating

Inactive Publication Date: 2009-04-22
PANGANG GROUP VANADIUM TITANIUM & RESOURCES +2
View PDF1 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The tailings of vanadium-titanium magnetite (raw ore) after selecting iron concentrate can be used to recycle titanium concentrate, which can be used to produce artificial rutile. However, the existing methods use electric furnace smelting or reduction corrosion to process titanium concentrate. Due to the inability to effectively remove calcium, magnesium and other impurity elements in titanium concentrate, the grade of artificial rutile obtained (that is, the content of titanium dioxide in artificial rutile) is all low, and it is not suitable for boiling chlorination to produce titanium tetrachloride. raw material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation of synthetic rutile
  • Preparation of synthetic rutile

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0008] The invention provides a method for preparing artificial rutile. The method comprises: oxidative roasting and reduction roasting of titanium concentrate, removal of impurities in the product of reduction roasting, and calcining of the product after removal of impurities. The reduction roasting is carried out under a reducing gas; wherein, the oxidation roasting and reduction roasting are carried out in a fluidized bed reactor.

[0009] The titanium concentrate recovered from the tailings after extracting iron concentrate from the vanadium-titanium magnetite (raw ore) in the Panxi area mainly contains iron metatitanate (FeO·TiO 2 ) crystals, and solid solutions of oxide impurities such as magnesium, manganese, aluminum, vanadium, and silicon. There are generally two methods for recovering titanium concentrate from the above tailings, namely gravity separation and gravity separation plus flotation. The TiO in the titanium concentrate obtained by gravity separation from th...

Embodiment 1

[0031] a. Oxidation roasting: get 20 kilograms of fine-grained titanium concentrates (purchased from Panzhihua Iron and Steel Group's fine-grained titanium concentrates (20# ore), see Table 1 for chemical composition analysis, and see Table 2 for particle size analysis), first at 650 After preheating in the preheater at ℃, it enters the fluidized oxidation furnace (that is, the fluidized bed reactor during oxidation, including the separation section, the settling section and the reaction section interconnected from top to bottom) for oxidation and roasting. Among them, the titanium concentrate enters the reaction section from the feed pipe at the bottom of the fluidized bed reactor, the air enters the reaction section from the reaction gas inlet at the bottom of the fluidized oxidation furnace, and the oxidized roasted product enters the reaction section from the fluidized oxidation furnace. The discharge pipe of the settling section of the furnace is output, and the oxidizing ...

Embodiment 2

[0043] Prepare artificial rutile according to the method described in embodiment 1, the difference is,

[0044] a, in oxidation roasting, the flow velocity of regulating air is 1 cubic meter / hour, the feeding speed of titanium concentrate is 20 kilograms / hour, makes the ratio of the flow velocity of titanium concentrate and the flow velocity of air be 20 kilograms / cubic meter, air The linear velocity in the fluidized oxidation furnace is 0.65 m / s, the temperature of oxidation roasting is 850 DEG C, the pressure of oxidation roasting is 20 kPa, and the oxidation roasting time is 90 minutes;

[0045] In the reduction roasting, the flow rate of the coke oven gas is adjusted to be 1 cubic meter per hour, and the feed rate of the product of the oxidation roasting is 20 kg per hour, so that the ratio of the flow rate of the product of the oxidation roasting to the flow rate of the coke oven gas is 20 kg / hour cubic meter, the linear velocity of coke oven gas in the fluidized reductio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method for preparing artificial rutile. The method comprises the following steps: titanium concentrate is subjected to oxidizing roasting and reducing roasting for removing impurities in oxidizing roasting products; and the products of which the impurities are removed are calcined, wherein the oxidizing roasting is performed in the presence of oxidizing gas, the reducing roasting is performed in the presence of reducing gas, and the oxidizing roasting and the reducing roasting are performed in a fluidized bed reactor. By adoption of the method, the high-grade artificial rutile can be prepared by adopting coarse fraction titanium concentrate as a raw material and can also be prepared by adopting micron-sized fraction titanium concentrate as the raw material.

Description

technical field [0001] The invention relates to a method for preparing artificial rutile. Background technique [0002] Vanadium-titanium magnetite is a multi-element paragenetic ore, and its composition varies with the place of origin. Vanadium-titanium magnetite contains 30-34% iron (existing in the form of iron oxide in the ore) by weight, and is mainly used as a raw material for extracting iron, vanadium and titanium. The tailings of vanadium-titanium magnetite (raw ore) after selecting iron concentrate can be used to recycle titanium concentrate, which can be used to produce artificial rutile. However, the existing methods use electric furnace smelting or reduction corrosion to process titanium concentrate. Due to the inability to effectively remove calcium, magnesium and other impurity elements in titanium concentrate, the grade of artificial rutile obtained (that is, the content of titanium dioxide in artificial rutile) is all low, and it is not suitable for boiling ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G23/07
Inventor 叶恩东程晓哲税必刚陈述罗建林彭卫星张天播
Owner PANGANG GROUP VANADIUM TITANIUM & RESOURCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com