Environment-protecting flame-retardant composite filling reinforced polyamide 66 resin composition

A technology of resin composition and flame retardant composite, which is applied in the field of environmentally friendly flame retardant composite filled reinforced polyamide 66 resin composition and polyamide modified materials. Effects on human health and excellent flame retardancy

Inactive Publication Date: 2009-05-27
SHANGHAI SUNNY
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in recent years, brominated flame retardants have been troubled by the problem of dioxins. At the same time, the flame-retardant polymer materials using it (bromine-antimony system) will generate a large amount of smoke and corrosive gases during thermal cracking and combustion. At present, the EU and Japan has successively issued laws and regulations to ban the use of such flame retardants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 and 2

[0024] Examples 1 and 2: Polyamide 66 is used as the matrix resin, the red phosphorus masterbatch is used as a flame retardant, the compatibilizer is PP-g-MAH; the antioxidant is 1098 / 168 (1:1); the lubricant is MB -4.

[0025] Proportioning 1-2 (weight %) (table 1)

[0026] raw material name Matching ratio 1 Matching 2 Polyamide 66 55 46 Red phosphorus masterbatch 20 18 PP-g-MAH 4 5 E-glass fiber 10 15 talcum powder 10 15 lubricant 0.5 0.5 Antioxidant is 1010 / 168(1:1) 0.5 0.5

[0027] Put the above-mentioned components into the high mixer in proportion except glass fiber and mix for 4 minutes, then add glass fiber and extrude granulation with a screw extruder, the screw speed is at 450 rpm, and the processing temperature in each zone is: ( Unit ℃)

[0028] a district Second District Third District Four districts five districts District six District Seven eight districts District 9 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an environment-friendly flame retardant composite filling reinforced polyamide 66 resin composition, which consists of a mixture. The mixture consists of the following compositions by weight percentage: 40 to 67 percent of nylon 66, 12 to 25 percent of red phosphorus master batch, 1 to 10 percent of compatilizer, 10 to 20 percent of glass fiber, 10 to 20 percent of talcum powder, 0.1 to 1 percent of antioxidant, and 0.1 to 1 percent of lubricant. The flame retardant polyamide composition has high-efficiency flame retardant performance with flame retardant rating reaching V0 grade of UL94 standard, greatly improves rigidity and heat resistance of nylon with good dimension stability, and belongs to an environment-friendly product. The environment-friendly flame retardant composite filling reinforced polyamide 66 resin composition is applicable to injection molding of electronic equipment and household appliances with various environment-friendly and flame retardant requirements.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant composite filled reinforced polyamide 66 resin composition, in particular to an engineering material product suitable for injection molding with high electrical insulation performance requirements and flame-retardant enhancement requirements, suitable for low-voltage vacuum contactors, circuit breakers The invention relates to polyamide modified materials for devices, low-voltage switches, thin-walled electronic and electrical components, etc., and belongs to the technical field of modified polyamides. technical background [0002] Nylon 66 is a homogeneous thermoplastic polymer with six symmetrical methylene groups in its molecular structure. It has the advantages of high strength, wear resistance, solvent resistance, good self-lubrication and wide temperature range. It is the most widely used One of engineering plastics, widely used in various electronic and electrical equipment and hom...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/06C08K9/06C08K7/14C08K5/524C08L51/06
Inventor 杨涛孟成铭项军宋董强柴振东
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products