Composite powdery calcium sulphate sewage treating agent and preparation method thereof
A sewage treatment agent, calcium sulfate technology, applied in the direction of flocculation/sedimentation water/sewage treatment, sterilization/microdynamic water/sewage treatment, complex/solubilizer treatment, etc., can solve the problem of insufficient polymerization degree and complicated operation process , turbidity of the effluent, etc., to achieve the effects of excellent coagulation performance, low operating cost, and compact alum
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1:
[0027] Mix 5 parts by weight of 80 mesh malic acid and 3 parts by weight of 80 mesh tartaric acid for 40 minutes, then add 60 parts by weight of 80 mesh calcium sulfate, mix for 50 minutes, add 10 parts by weight of 80 mesh magnesium carbonate, mix for 40 minutes, and add 10 80 parts by weight calcium carbonate was mixed for 40 minutes, then 10 parts by weight of 80 mesh ferric chloride were added, mixed for 40 minutes, and 10 parts by weight of 80 mesh calcium oxide were added for 40 minutes, and then 2 parts by weight of 80 mesh polyacrylamide were added. Mix for 120 minutes and it's ready.
Example Embodiment
[0028] Example 2:
[0029] Mix 7 parts by weight of 200 mesh malic acid and 4 parts by weight of 200 mesh tartaric acid for 50 minutes, then add 65 parts by weight of 200 mesh calcium sulfate, mix for 90 minutes, add 12 parts by weight of 200 mesh magnesium carbonate, mix for 50 minutes, and add 15 200 parts by weight calcium carbonate was mixed for 50 minutes, then 15 parts by weight of 200 mesh ferric chloride were added, mixed for 50 minutes, 15 parts by weight of 200 mesh calcium oxide were added, and mixed for 50 minutes, and 2.5 parts by weight of 200 mesh polyacrylamide were added. Mix for 130 minutes, and that's it.
Example Embodiment
[0030] Example 3:
[0031] Mix 10 parts by weight of 400 mesh malic acid and 5 parts by weight of 400 mesh tartaric acid for 60 minutes, then add 70 parts by weight of 400 mesh calcium sulfate, mix for 120 minutes, then add 15 parts by weight of 400 mesh magnesium carbonate, mix for 60 minutes, and add 20 40 parts by weight of 400 mesh calcium carbonate were mixed for 60 minutes, then 20 parts by weight of 400 mesh ferric chloride were added, mixed for 60 minutes, and 20 parts by weight of 400 mesh calcium oxide were added for 60 minutes, and then 3 parts by weight of 400 mesh polyacrylamide were added. Mix for 150 minutes and it's ready.
[0032] The technical indicators of Examples 1-3 are shown in Table 1:
[0033] Table 1:
[0034] Example 1 Example 2 Example 3 Density g / cm 3 (20℃) 1.20 1.25 1.30 Solid content (weight)% 90 91 92 Reducing substances (with Fe 2+ Count)
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap