The technology of a curable composition and a manufacturing method, which is applied in the field of curable compositions, can solve the problems of unsuitable curing, expensive equipment and high reactivity in manufacturing, and achieve the effects of excellent rapid curing and high safety.

Active Publication Date: 2009-07-22
CEMEDAINE CO LTD
View PDF18 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In addition, there is a growing demand for fast-curing products in the market, but currently manufacturers' fast-curing products are not suitable for curing during production.
For example, Patent Document 5 discloses a curable composition containing a crosslinkable silyl group-containing organic polymer, a dialkyltin oxide, and an ester compound in the reactant, and the crosslinkable silyl group-containing of organic polymers containing -SiX 3 The cross-linkable silyl group shown, but due to high reactivity, there is a problem of curing the product during production
In addition, when considering manufacturing stability and using a low-activity organotin-based curing catalyst, rapid curing cannot be obtained. When considering rapid curing and using a highly active organotin-based curing catalyst, it is the same as dialkyltin oxide. Reactants with ester compounds will not be able to obtain manufacturing stability
[0007] The recently developed equipment that can produce catalysts in a completely closed system is well received by manufacturers of room temperature curing products, but the number of additives is limited and the equipment is very expensive, so it is not suitable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Curing composition and method for producing curing composition
  • Curing composition and method for producing curing composition
  • Curing composition and method for producing curing composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0164] The present invention will be specifically described below with examples, but these examples are only for illustration and not limitation.

Synthetic example 1

[0166] 43 parts by weight of xylene, 80 parts by weight of methyl methacrylate, 20 parts by weight of stearyl methacrylate, 20 parts by weight of γ-methacryloxypropyl trimethoxysilane, and ruthenocene for metal catalysts 0.1 parts by weight of the dichloride was put into a flask equipped with a stirring device, a nitrogen gas introduction pipe, a thermometer, and a reflux cooling pipe, and the contents of the flask were heated to 80° C. under nitrogen gas introduction.

[0167] Next, stir and add 20 parts by weight of 3-mercaptopropyltrimethoxysilane fully replaced with nitrogen gas next time, after adding 20 parts by weight of 3-mercaptopropyltrimethoxysilane, heat and cool for 4 hours to make the stirring flask The temperature of the contents was maintained at 80°C. Thereafter, 20 parts by weight of 3-mercaptopropyltrimethoxysilane fully substituted with nitrogen was added to the flask over 5 minutes while stirring. After adding the total amount of 20 parts by weight of 3-m...

Synthetic example 2

[0171] In addition to replacing 80 parts by weight of methyl methacrylate in the contents of the flask with 10 parts by weight of n-butyl acrylate and 70 parts by weight of methyl methacrylate, the others were synthesized with Synthesis Example 1 to obtain a crosslinkable silane containing A mixture 2 of a polyoxyalkylene-based polymer (A) and a (meth)acrylic polymer (B).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
number average molecular weightaaaaaaaaaa
number average molecular weightaaaaaaaaaa
molecular weightaaaaaaaaaa
Login to View More

Abstract

A curing composition is disclosed which is excellent in workability, adhesiveness, rubber properties, shelf life stability, and fast curing properties. The curing composition contains (A) a crosslinkable silyl group-containing organic polymer and (B) a (meth)acrylic polymer which is obtained by polymerizing a (meth)acrylic monomer having a polymerizable unsaturated bond in the presence of a metallocene compound and a crosslinkable silyl group-containing thiol compound, and at least one end of which is bonded with a residue -S-R (wherein R is a group having a crosslinkable silyl group) which is left when a hydrogen atom is removed from the crosslinkable silyl group-containing thiol compound.

Description

[0001] This application is a divisional application, the application number of its parent application: 200480020303.4, the filing date: 2004.7.30, the title of the invention: curable composition and the manufacturing method of the curable composition technical field [0002] The present invention relates to a curable composition, and more specifically relates to a curable composition having excellent adhesiveness, rubber physical properties, rapid curing and production stability. Background technique [0003] Patent Document 1 discloses a propylene-based polymer polymerized using a specific polymerization catalyst. In addition, Patent Document 1 discloses a curable composition comprising this special propylene-based polymer and a silane coupling agent, but the curable composition is not sufficient in adhesiveness, rubber physical properties, and the like. [0004] In addition, industrially produced room temperature curable compositions containing organic polymers containing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/02C08L33/04C08L33/20C08L23/22C08L71/02C08K5/57
Inventor 斋藤敦斋藤知纪冈村直实
Owner CEMEDAINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com