Polynutrient anti-blocking synergy urea and preparation method

An anti-caking, multi-nutrient technology, applied in the direction of urea compound fertilizer, nitrogen fertilizer, fertilizer mixture, etc., can solve the problems of not using large-scale agricultural production, not matching the law of nitrogen demand, and slow-release too fast. Achieve low cost, prevent contact, and promote plant growth

Inactive Publication Date: 2009-12-02
乔山峰
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main types of coated urea currently formed in China include coated urea, phosphogypsum coated urea and calcium magnesium phosphate coated urea. The amount is small and the cost is low, but most of its slow-release properties are too fast, which cannot match the nitrogen demand of crops. There is still a big gap between the production technology and Europe, the United States, Japan and other countries, and it has not been used on a large scale so far. in agricultural production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: Take by weighing 60kg of magnesium sulfate, 2kg of polyacrylamide, 0.5kg of sodium carboxymethyl cellulose, and 0.5kg of sodium dodecylbenzenesulfonate and mix them uniformly, then add 378kg of water to make an aqueous solution. Add 5 kg of sodium nitrophenolate and 5 kg of sodium α-naphthalene acetate and mix uniformly to make a coating material composition, weigh 1 kg of the coating material composition prepared above and mix it with 100 kg of large-grain urea and then send it into the coating Machine wrapping, screening and packaging.

Embodiment 2

[0015] Embodiment 2: Take by weighing 61kg of magnesium sulfate, 2.5kg of polyacrylamide, 1kg of sodium carboxymethylcellulose, and 1kg of sodium dodecylbenzenesulfonate and mix them uniformly, then add 380kg of water to make an aqueous solution, and in the obtained aqueous solution Add 6 kg of sodium nitrophenolate and 6 kg of sodium α-naphthalene acetate and mix uniformly to make a coating material composition, weigh 1 kg of the coating material composition prepared above and mix it with 100 kg of large-grain urea and then send it to the coating machine Carry out film coating, sieve and pack.

Embodiment 3

[0016] Embodiment 3: take by weighing magnesium sulfate 77kg, polyacrylamide 9kg, sodium carboxymethyl cellulose 2.3kg, sodium dodecylbenzene sulfonate 2.3kg mix uniformly, then add 1074kg water to make aqueous solution, in the aqueous solution obtained Add 10kg of sodium nitrophenolate and 10kg of sodium α-naphthalene acetate to the mixture and mix uniformly to make a coating material composition. Weigh 1 kg of the coating material composition prepared above and mix it with 100 kg of large-grain urea and then send it into the coating Machine wrapping, screening and packaging.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses polynutrient anti-blocking synergy urea which contains large particle urea and a film coating composition, wherein the film coating composition comprises the following components in proportion by weight: 60-95 magnesium sulfate, 2-15 polyacrylamide, 0.5-4 sodium carboxymethyl cellulose, 0.5-4 dodecyl benzene sulphonic acid, 378-1770 water, 5-15 compound sodium nitrophenolate and 5-15 alpha-pimacol; and the weight ratio of the film coating composition to the large particle urea is 1:100-500. The film coating composition forms a coating film on the surface of the large particle urea so as to have good effects of anti-caking and anti-chalking. The components of the polynutrient anti-blocking synergy urea mutually cooperate to ensure that the decomposition velocity of nitrogen is consistent with the demand for nitrogen of crops and can improve the utilization rate of the nitrogen in the urea, promote the growth of plants and meet the requirement on magnesium of the crops, thus the product is polynutrient anti-blocking high-efficiency urea which has simple process and low cost and is suitable for popularization.

Description

technical field [0001] The invention relates to the field of fertilizers, in particular to an anti-caking urea and a preparation method thereof. Background technique [0002] Nitrogen is generally deficient in farmland soil in my country, and the application of nitrogen fertilizer is one of the key measures to ensure high-yield, stable, high-quality, and efficient agriculture. At present, the main variety of nitrogen fertilizer in the world and in my country is urea. Urea has been recognized by consumers for its high concentration of effective nutrients, good performance, easy storage and transportation, and convenient use. However, domestic urea generally has agglomeration problems during transportation, storage and after application, which seriously affects product appearance and utilization rate. On the other hand, the nitrogen utilization rate of urea after application is relatively low. [0003] The agglomeration of urea is caused by the recrystallization process on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/08C05C9/00C05G3/90
Inventor 乔山峰
Owner 乔山峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products