Method for manufacturing steel plate with high strength and high toughness by using hot-rolling coiled plate
A high-strength, high-toughness technology, applied in the field of hot-rolled coils to manufacture high-strength and high-toughness steel plates, can solve the problems of tough steel plates that cannot be produced, thin gauge, high strength, and low product quality, achieving short heating time and occupying an area The effect of small area and low equipment investment
Active Publication Date: 2009-12-16
武汉武钢实业机电材料工程有限公司
View PDF0 Cites 36 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The production of such products by traditional technology has complicated procedures, high energy consumption,
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0064] The mass percentage of each chemical element is: C: 0.17%, Si: 0.25%, Mn: 1.25%, Ni: 0.05%, Cr: 0.21%, Mo: 0.61%, Cu: 0.01%, Nb: 0.015%, V: 0.038%, Ti: 0.025%, Al: 0.035%, B: 0.0015%, P: 0.018%, S: 0.004%, N: 0.0035%, and the rest are made of iron 12mm thick hot-rolled coils. Yield strength Reh≥1030MPa high For high-strength and high-toughness steel plates, the heat treatment process is as follows: heating to 940°C in induction heating equipment for austenitization, heating time is 100s, quenching cooling rate is 20°C / s, heating to 290°C in induction heating equipment for back Fire, tempering time 120s. A high-strength and high-toughness steel plate with mechanical properties of: Reh: 1080MPa, Rm: 1280MPa, A%: 13%, Akv-40°C: 98J was obtained.
[0065] figure 2 It shows the CCT curve of steel whose Reh is 1030MPa drawn by using Formastor-F thermal dilatometer combined with observation of metallographic structure and hardness test. When the cooling rate is 20°C / s, the...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more Abstract
The invention relates to a manufacture method for manufacturing a steel plate with high strength and high toughness by using a hot-rolling coiled plate. The method comprises the following steps that: firstly, after a hot-rolling coiled plate is leveled on a leveling machine set, refining heat treatment is carried out on the hot-rolling coiled plate, i.e. the hot-rolling coiled plate is heated in induction heating equipment, the heating time is within 60-140s, and the hot-rolling coiled plate is heated to 910DEG C to 960DEG C and austenized; then, the hot-rolling coiled plate enters a water-cooling or steam-cooling quenching machine set to carry out quenching, the quenching and cooling speed of the hot-rolling coiled plate is greater than or equal to 5DEG C/s, and a quenched martensite organization is obtained after quenching; tempering is carried out after quenching, induction heating is carried out by adopting the induction heating equipment in the tempering, the heating temperature of the quenched martensite organization is 220DEG C to 440DEG C, the tempering time is 80 to 180s, and a tempered martensite organization is obtained; and finally, straightening, flaw detection, surface inspection and sampling inspection are carried out to finally obtain the steel plate with excellent performance, high strength and high toughness. The invention has the advantages that as refining treatment adopts an induction heating method, the heating time is short, austenite crystal grains are fine, the mechanical property is superior to that of a similar product produced by the traditional technology, the plate type of the steel plate is good, and the invention has high production efficiency, low equipment investment, little maintenance cost of the equipment, small occupation area and little environmental pollution.
Description
technical field [0001] The invention belongs to the technical field of heat treatment of metallurgical manufacturing mechanical structural parts, in particular to a method for manufacturing high-strength and high-toughness steel plates by using hot-rolled coils. Background technique [0002] High-strength and high-toughness steel plate is an important raw material for the production of equipment manufacturing industry. It can be used in the manufacture of important structural parts such as heavy trucks, automobile booms, and loaders. [0003] The traditional manufacturing method of high-strength and high-toughness steel plate is to use continuous casting billet, roll it into the original flat plate in the medium and heavy plate rolling mill, cut off the four sides, austenitize the steel plate through a heat treatment furnace, and then quench it in the quenching unit to obtain quenched The martensite is heated to the tempering heat temperature in a tempering heat treatment fu...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C21D8/02C22C38/54C21D1/42C21D1/18
CPCY02P10/25
Inventor 马景怡
Owner 武汉武钢实业机电材料工程有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap