Ferrous metal surface fireproof flame resistance paint and production method thereof

Abstract

The invention relates a ferrous metal surface fireproof flame resistance paint and a production method thereof; the paint comprises the following raw materials according to the parts by weight: 25-35 parts of phenolic resin, 20-25 parts of aluminum naphthenate, 5-8 parts of additive, 9-10 parts of each metal of aluminum, tungsten, molybdenum, manganese, gypsum and talcum powder and 0.01-0.05 part of pigment, wherein, the additive comprises glacial acetic acid, phosphorus trichloride and pure water. The production method of the paint comprises the following steps: 1) grinding metal powders to 350-400 meshes of ultrafine powders, then adding additive, aluminum naphthenate and pigment in a the charging basket of a agitator to stir and react to obtain fireproof flame resistance base material; 2) adding the base material in a reaction kettle, gradually dripping phenolic resin while stirring the materials, after fully stirring and discharging the obtained paste; 3) transferring the paste into a three-roll ball mill and finally obtaining the finished paint after performing ball milling 2-3 times. The product can not burn at 800-1200 DEG C, which can not cause fire accident and can eliminate potential safety hazard and environmental pollution. The paint can be widely used as the coating inside and outside buildings, ships, trains, cars, tanks, armored cars and mechanical equipments in civil use, industry, aviation, national defense industry and other fields, and the paint can retard flame and fire.

Description

Technical field: [0001] The invention relates to a fire-resistant and oil-resistant paint for ferrous metal surfaces, and also relates to a production method of the fire-resistant and oil-resistant paint. Background technique: [0002] All inner and outer shells made of ferrous metals need to be painted and painted. Civil, industrial, aviation, national defense industries and other fields, such as mechanical power, engine sets, trains, automobiles, ships, warships, aircraft cannons, guns, construction facilities and equipment, etc., must be painted, but the commonly used paint It is easy to catch fire and burn, which is very unsafe and seriously pollutes the environment. The enamel paint on the market is non-combustible, but the enamel paint is too expensive, and it is not suitable for large-scale spraying. Therefore, conventional paints have been used for a long time, causing hidden dangers to society, personal property, personal safety, and the natural environment. Chin...

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of fire retardant paint for ferrous metal surface, which solves the difficult problem of fire retardant and fire retardant that cannot be solved by the painting process of ferrous metal surface.