Method for producing rubber matrix Chinese medicine plaster based on Mooney viscosity

A technology of Mooney viscosity and production method, which is applied in the direction of pharmaceutical formulations, medical preparations with no active ingredients, medical preparations containing active ingredients, etc., and can solve the problems of lack of quantitative monitoring indicators, unstable adhesion performance, rubber paste coating, etc. Problems such as poor cloth, to achieve the effect of ensuring product qualification rate and quality stability, saving parking time, and convenient detection and operation

Inactive Publication Date: 2010-03-17
SOUTH CHINA UNIV OF TECH +1
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, only based on experience and lack of quantitative monitoring indicators, it is easy to cause defects such as poor coating of rubber paste, unstable adhesion performance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Weigh the following raw materials:

[0028] Matrix components: natural rubber 10kg

[0029] Terpene resin 4kg

[0030] Low molecular weight polyisobutylene 3kg

[0031] White Vaseline 0.2kg

[0032] lithopone 4kg

[0033] Traditional Chinese medicine extract: bruises analgesic drug extract 2.5kg

[0034] The weight-average molecular weight of the low-molecular-weight polyisobutylene is 2600; for the specific ingredients and preparation of the traumatic analgesic drug extract, please refer to the Chinese invention patent with application number 00130813.0.

[0035] The preparation process is as follows:

[0036] (1) Mixing: According to the amount of raw material prescription, put the natural rubber that has been masticated into flakes into an internal mixer, add terpene resin, white vaseline, polyisobutylene, lithopone and Dieda analgesic extract , start mixing, and control the mixing time for 20 minutes; stop samp...

Embodiment 2

[0041] Weigh the following raw materials:

[0042] Matrix components: natural rubber 10kg

[0043] Hydrogenated Rosin 3kg

[0044] Low molecular weight polyisobutylene 4kg

[0045]Yellow Vaseline 0.1kg

[0046] Lanolin 0.1kg

[0047] Lithopone 1kg

[0048] Calcium carbonate 3kg

[0049] Traditional Chinese Medicine Extract: Dieda Analgesic Drug Extract 5kg

[0050] The weight-average molecular weight of the low-molecular-weight polyisobutylene is 2600; for the specific ingredients and preparation of the traumatic analgesic drug extract, please refer to the Chinese invention patent with application number 00130813.0.

[0051] The preparation process is as follows:

[0052] (1) Mixing: According to the prescription amount, put the natural rubber that has been masticated into thin flakes into an internal mixer, add hydrogenated rosin, low molecular weight polyisobutylene, yellow vaseline, lanolin, lithopone, calci...

Embodiment 3

[0057] Weigh the following raw materials:

[0058] Matrix components: natural rubber 10kg

[0059] Terpene resin 5kg

[0060] Petroleum resin 2kg

[0061] Lanolin 0.2kg

[0062] White carbon black 1.5Kg

[0063] Talc powder 2.5kg

[0064] Traditional Chinese Medicine Extract: Dieda Analgesic Drug Extract 1.2kg

[0065] The weight-average molecular weight of the low-molecular-weight polyisobutylene is 5,500; for the specific ingredients and preparation of the bone-relief analgesic drug extract, please refer to the Chinese invention patent with application number 00130813.0.

[0066] The preparation process is as follows:

[0067] (1) Mixing: According to the prescription amount, put the natural rubber that has been masticated into flakes into an internal mixer, add terpene resin, petroleum resin, lanolin, white carbon black, talcum powder and medicinal extract, and start mixing. Refining; control the mixing time...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for producing a rubber matrix Chinese medicine plaster based on Mooney viscosity. The method comprises the steps that: natural rubber or synthetic rubber plasticated into slice is placed in an internal mixer, a filler, a viscosifier, a softener and a Chinese medicine extract are added in accordance with the formulation of the rubber matrix Chinese medicine plaster for mixing, the internal mixer is shut off and samples are taken for analyzing the value of Mooney viscosity of the mixed plaster, the mixing time is controlled in a range from 4 to 25 minutes so thatthe Mooney viscosity of the mixed plaster, measured by a Mooney viscosity apparatus, is from 3 to 9; refining is then implemented, the mixed plaster is rolled 1 to 6 times on a mixing mill or milled for 1 to 5 minutes in the internal mixer, and the Mooney viscosity of the sampled plaster after the refining, measured by the Mooney viscosity apparatus, is from 2 to 7 by controlling the rolling timesor the milling time. According to the method, the Mooney viscosity of the rubber plaster in different production steps is regarded as quantitative indicators in order to monitor the production of therubber plaster on the scene, thus ensuring the coating and adhesive performance of the rubber plaster article.

Description

technical field [0001] The invention relates to a production method of a traditional Chinese medicine plaster, in particular to a production method of a rubber matrix traditional Chinese medicine plaster based on Mooney viscosity. Background technique [0002] At present, the production process of traditional Chinese medicine rubber ointment is divided into two kinds: traditional process (solvent method) and new process (hot pressing method). The production process of the solvent method needs to use a large amount of solvent-gasoline, the production cost is high, the requirements for explosion-proof and fire-proof measures are strict, the safety hazard is large, and the residue of gasoline is easy to cause skin allergies. Cause more loss of volatile components. The hot pressing method overcomes the shortcomings of the solvent-based rubber paste, does not require solvents, is safe in production, meets environmental protection requirements, has low production costs, and has a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K36/00A61K9/70A61K47/32A61K47/02A61K47/04A61K47/36A61K47/44
Inventor 卢珣梁艳茹罗权焜林淑明陈云鹄钱碧坤
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap