Easy-stripping type room temperature vulcanizing silicone rubber and preparation method thereof
A room temperature vulcanization, silicone rubber technology, applied in the field of silicone rubber, can solve the problem of difficult cleaning after secondary maintenance, and achieve the effects of cost saving, convenient use and good sealing performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example 1
[0032] 100 parts by weight of hydroxy-terminated polydimethylsiloxane with a viscosity of 200 Pa·s at 25°C, 50 parts by weight of polybutene, and 5 parts by weight of titanium dioxide are stirred in a closed reactor under vacuum, and then 1 Parts by weight of methyl tributyl ketoxime silane, 20 parts by weight and a specific surface area of 50m 2 / g of hydrophobic fumed silica, 0.05 parts by weight of dibutyltin dilaurate, 1 part by weight of lead octoate, and 5 parts by weight. The kinematic viscosity at 40°C is 26mm 2 / s industrial-grade white oil is stirred for 30-60 minutes under vacuum, then released by nitrogen and put into a closed packaging container. The tensile strength is 1.1MPa, the elongation is 425%, the peeling strength is less than 1.0N / cm, 25℃ Easily peelable room temperature vulcanized silicone rubber with sealing pressure greater than 8.0MPa.
Example Embodiment
[0033] Example 2
[0034] Put 100 parts by weight of hydroxy-terminated polymethylphenylsiloxane with a viscosity of 30 Pa·s at 25°C, 100 parts by weight of MDT-type polymethylsiloxane and 300 parts by weight of diatomaceous earth in a closed reactor. Stir uniformly, and then add 25 parts by weight of tetrakis (methyl isobutyl ketoxime) silane and 3 parts by weight with a specific surface area of 300m 2 / g of hydrophobic fumed silica, 2 parts by weight of dibutyltin diacetate and 10 parts by weight of kinematic viscosity at 40°C is 10mm 2 / s cosmetic-grade white oil is stirred for 30-60 minutes under vacuum, then release the vacuum with nitrogen and put it into a closed packaging container. The tensile strength is 1.8MPa, the elongation is 205%, the peeling strength is less than 1.0N / cm, and 25℃. Easily peelable room temperature vulcanized silicone rubber with sealing pressure greater than 8.0MPa.
Example Embodiment
[0035] Example 3
[0036] 60 parts by weight of hydroxy-terminated polydimethylsiloxane with a viscosity of 80 Pa·s at 25°C, and 40 parts by weight of hydroxy-terminated polymethylphenylsiloxane with a viscosity of 1 Pa·s at 25°C, 5 parts by weight of dimethyl silicone oil and 50 parts by weight of silicon micropowder are uniformly stirred in a closed reactor under vacuum, and then 20 parts by weight of methyl tris(methyl isobutyl ketoxime) silane and 3 parts by weight of specific surface area are added in sequence. 200m 2 / g of hydrophilic fumed silica, 0.05 parts by weight of dibutyl tin diphenoxide, 30 parts by weight of kinematic viscosity at 40°C is 60mm 2 / s industrial grade white oil and 5 parts by weight, the kinematic viscosity at 40°C is 26mm 2 / s cosmetic-grade white oil is stirred for 30-60 minutes under vacuum, then release the vacuum with nitrogen and put it into a closed packaging container. The tensile strength is 1.3MPa, the elongation is 185%, the peeling strengt...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Kinematic viscosity | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap