Production method of high-strength bamboo pulp viscose glue short fiber

A technology of viscose staple fiber and production method, which is applied in the direction of fiber treatment, chemical post-treatment of fiber, wet spinning method, etc., can solve the problems of weak, low strength, low durability, etc. The effect of strong resistance and high wear resistance

Active Publication Date: 2010-06-16
上海中纺物产发展有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the bamboo pulp viscose staple fiber dry breaking strength 2.5CN/dtex, the wet breaking strength 1.2CN/dtex of producing according

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of high-strength bamboo pulp viscose glue short fiber
  • Production method of high-strength bamboo pulp viscose glue short fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] a. Impregnation: Immerse the bamboo pulp in an impregnation bucket equipped with caustic soda solution, the concentration of the impregnation alkali solution is 255g / L, the temperature of the impregnation alkali solution is 22°C, the impregnation time is 70 minutes, and the amount of denaturant V-388 is methyl fiber 0.8% of prime;

[0025] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeeze ratio is 2.2, and the pulverization degree is 180g / L;

[0026] c. Aging: put the crushed raw materials into the aging drum for aging, the aging temperature is 22°C;

[0027] d. Yellowing: add the aged raw materials into the yellowing machine to react with carbon disulfide. The amount of carbon disulfide added is 35% of the methyl cellulose, the yellowing time is 50 minutes, the temperature is 20°C, and the denaturant V is added during the dissolution. -315, the amount added is 0.6% of ...

Embodiment 2

[0033] a. Impregnation: Immerse the bamboo pulp pulp in an impregnation bucket equipped with caustic soda solution, the concentration of the impregnation alkali solution is 270g / L, the temperature of the impregnation alkali solution is 20°C, the impregnation time is 90 minutes, and the amount of denaturant Lv-3 is methyl fiber 0.6% of prime;

[0034] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeezing multiple is 2.4, and the pulverization degree is 170g / L;

[0035] c. Aging: put the pulverized raw materials into the aging drum for aging, the aging temperature is 24°C;

[0036] d. Yellowing: Add the aged raw materials into the yellowing machine to react with carbon disulfide. The amount of carbon disulfide added is 37% of that of methyl cellulose, the yellowing time is 45 minutes, the temperature is 30°C, and denaturant V is added into the solution. -315, the addition amount i...

Embodiment 3

[0042] a. Impregnation: Immerse the bamboo pulp pulp in an impregnation bucket equipped with caustic soda solution, the concentration of the impregnation alkali solution is 260g / L, the temperature of the impregnation alkali solution is 21°C, the impregnation time is 80 minutes, and the amount of denaturant Lv-3 is methyl fiber 0.7% of prime;

[0043] b. Squeeze and pulverize: squeeze the impregnated raw materials with a squeeze machine, and then pulverize them with a pulverizer, wherein the squeezing multiple is 2.3, and the pulverization degree is 175g / L;

[0044] c. Aging: put the crushed raw materials into the aging drum for aging, the aging temperature is 23°C;

[0045] d. Yellowing: Add the aged raw materials into the yellowing machine to react with carbon disulfide. The amount of carbon disulfide added is 36% of the methyl cellulose, the yellowing time is 48 minutes, the temperature is 25°C, and denaturant V is added during dissolution. -315, the amount added is 0.4% of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Pulverizationaaaaaaaaaa
Pulverizationaaaaaaaaaa
Pulverizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of high-strength bamboo pulp viscose glue short fiber, which adopts the steps of dipping, squeezing, smashing, maturing, yellowing, spinning, drawing, refining, drying and the like to prepare high-strength bamboo pulp viscose glue short fiber. The high-strength bamboo pulp viscose glue short fiber prepared with the method has dry breaking strength of 3.2-3.4 CN/dtex and wet breaking strength of 2.0-2.3 CN/dtex, is firm and has strong spinnability; fabrics and clothes manufactured by the fiber have favourable toughness and high abrasive resistance; other indexes are all superior to the first-rate product index of FZ/ T 52006-2006. The fiber manufactured with the method is ideal material for high-rank clothes and household textiles.

Description

technical field [0001] The invention relates to a production method of viscose fiber, in particular to a production method of high-strength bamboo pulp viscose staple fiber. Background technique [0002] In the textile spinning industry, according to the processing method of bamboo fiber, bamboo fiber can be divided into two types: primary bamboo fiber and regenerated bamboo fiber. Raw bamboo fiber is bamboo fiber made by physical method, and regenerated bamboo fiber is bamboo pulp fiber made by chemical method. [0003] Raw bamboo fiber is made by rolling, twisting and combing bamboo by physical and mechanical methods, and then degumming bamboo fiber, removing sugar, fat, disinfecting and drying. Bamboo fiber has the advantages of coolness, moisture absorption, breathability, and perspiration, and has natural antibacterial properties, which has attracted the attention of the international market. However, due to its natural nature and long processing steps, the fineness a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01C1/00D01D1/02D01D5/06D01F2/06
Inventor 吴会俊熊桐生赵睿哲
Owner 上海中纺物产发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap