Preparation method of water-base epoxy resin sizing agent for carbon fiber

A water-based epoxy resin, epoxy resin curing technology, used in carbon fiber, fiber processing, textiles and papermaking, etc., can solve the problems of poor carbon fiber reinforcement, poor performance of emulsion sizing agent, and high cost, and achieve easy gluing. , low cost, good effect of enhancement

Active Publication Date: 2010-06-16
HARBIN INST OF TECH
View PDF0 Cites 56 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems that the cost of the existing foreign emulsion-type sizing agent is high; the performance of the domestically-researched emulsion-type si...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-base epoxy resin sizing agent for carbon fiber
  • Preparation method of water-base epoxy resin sizing agent for carbon fiber

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0009] Specific embodiment one: the preparation method of carbon fiber water-based epoxy resin sizing agent in this embodiment is realized by the following steps: one, add epoxy resin and water-based epoxy emulsifier by mass ratio 80:20 in the water bath of 70 ℃, then Place in a high-shear dispersing emulsifier, stir at a speed of 1500-16000r / min, and add deionized water dropwise until the phase transfer occurs in the mixed system, and then add deionized water dropwise to the solid content of the mixed system after 20-90 minutes 40% to 50%, continue to stir for 30 minutes to obtain water-based epoxy resin HIT-WE; 2. Add epoxy resin curing agent and water-based epoxy emulsifier in a water bath at 70°C in a mass ratio of 80:20, and then place In the high-shear dispersing emulsifier, stir at a speed of 1500-8000r / min and add deionized water dropwise, and then add deionized water dropwise after 3-5 hours until the solid content of the mixed system is 40%-50%. 3. Dilute the water-b...

specific Embodiment approach 2

[0014] Specific embodiment two: the difference between this embodiment and specific embodiment one is the preparation of water-based epoxy emulsifier in step one: the 250ml four-necked bottle equipped with agitator, reflux condenser and thermometer is placed in 80 ℃ water bath , then add bisphenol A epoxy resin and polyethylene glycol in a molar ratio of 1:1, and stir at a rate of 200 to 500r / min until molten state; heat up to 100°C, add bisphenol A epoxy resin and triphenylphosphine with 0.15% of the total mass of polyethylene glycol, and stirred at a rate of 200-500r / min for 6h, then pour the product into a watch glass to obtain a water-based epoxy emulsifier; put it into a desiccator for preservation . Other steps and parameters are the same as those in Embodiment 1.

specific Embodiment approach 3

[0015] Specific embodiment 3: The difference between this embodiment and specific embodiment 1 is that in step 1, stirring is performed at a rotational speed of 2000-10000 r / min. Other steps and parameters are the same as those in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of water-base epoxy resin sizing agent for carbon fiber, relating to a sizing agent preparation. The invention solves the problems that the cost of existing foreign latex sizing agent and that the performance of domestically researched emulsion sizing agent is not good. The method comprises: 1. preparing water-base epoxy resin; 2. preparing water-base epoxy resin curing agent; 3. diluting water-base epoxy resin with de-ionized water, and dispersing to obtain water-base epoxy resin emulsion; 4. mixing the water-base epoxy resin emulsion with the water-base epoxy resin curing agent to obtain a water-base epoxy resin emulsion system; and 5. mixing the water-base epoxy resin emulsion system with aid to obtain water-base epoxy resin sizing agent for carbon fiber. The water-base epoxy resin sizing agent for carbon fiber in the invention has good performance, good strengthening function to carbon fiber, better clustering property, smoothness and flexibility, and low cost, and the performance indexes such as overall loose degree of filaments of the fiber, fiber opening property and cross-linking degree among signal fibers.

Description

technical field [0001] The invention relates to a preparation method of a sizing agent. Background technique [0002] Carbon fiber is a brittle material. In the process of production and processing, it is easy to produce wool and monofilament breakage through mechanical friction, which reduces the strength of carbon fiber. Moreover, due to the existence of wool, the matrix resin cannot fully wet the carbon fiber, making it It is easy to produce pores in the prepared composite material, which will affect the mechanical properties of the composite material, and the wool will also affect the working environment. Therefore, it is necessary to sizing the carbon fiber. The function of sizing is to form a protective film on the surface of the carbon fiber, which not only protects the surface of the carbon fiber during subsequent processing, reduces the breakage of wool and single filaments, but also makes the carbon fiber easy to be bundled. It acts as a transition layer to improv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/55D06M101/40
Inventor 黄玉东张如良刘丽唐一壬王晓明刘青松景介辉
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap