Reinforced nylon material without floating fiber and preparation method thereof

A non-floating fiber and nylon technology, which is applied in the field of non-floating fiber reinforced nylon materials and its manufacturing, can solve the problems of unsolved floating fiber problems, and achieve the effects of high fluidity, high heat resistance, and high processing fluidity

Active Publication Date: 2010-07-21
SUZHOU TAIKAN MACHINERY CO LTD
View PDF4 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent application number CN200510026733.3 provides a glass fiber reinforced nylon composite material with high surface finish and its preparation method, which only involves improving the surface of the material and does not solve the problem of floating fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The non-floating fiber reinforced nylon material of the present invention is made of the following raw materials in mass ratio: polyamide 625%, polyamide 6631%, glass fiber 36%, compatibilizer 1%, paint film agent 1%, toughening agent 4% , 0.3% antioxidant, 0.4% nucleating agent, 0.3% coupling agent and 1% anti-floating fiber agent.

[0028] Among them, the relative density of polyamide 6 is 1.14g / cm3, the melting point is 220°C, and the melt viscosity is 2.4. You can choose PA6TP4208 produced by Taiwan Jisheng Chemical, whose relative density is 1.14g / cm3, and the melting point is 220°C, and The melt viscosity is 2.42; the relative density of polyamide 66 is 1.14g / cm3, the melting point is 260°C, and the melt viscosity is 2.7. Shenma PA66 EPR27 from Pingdingshan, Henan can be used, and its relative density is 1.14g / cm3. is 260°C, and the melt viscosity is 2.67.

[0029] Among them, the glass fiber is alkali-free, twist-free, 10 yarns / 20 strands of long fiber, and its ...

Embodiment 2

[0041] The non-floating fiber reinforced nylon material of the present invention is made of the following raw materials in mass ratio: polyamide 642%, polyamide 6615%, glass fiber 34%, compatibilizer 1%, paint film agent 2%, toughening agent 3% , 0.3% antioxidant, 0.4% nucleating agent, 0.3% coupling agent and 2% anti-floating agent.

[0042] The selection of polyamide 6, polyamide 66, glass fiber, compatibilizer, paint film agent, toughening agent, antioxidant, nucleating agent, coupling agent and the same as the first embodiment.

[0043] The steps for manufacturing the above-mentioned nylon material are the same as those in Example 1.

[0044] The temperature of the screw section is as follows: the temperature of the first zone is 235°C, the temperature of the second zone is 240°C, the temperature of the third zone is 250°C, the temperature of the fourth zone is 255°C, the temperature of the fifth zone is 260°C, the temperature of the sixth zone is 245°C, and the temperatur...

Embodiment 3

[0047] The non-floating fiber reinforced nylon material of the present invention is made of the following raw materials in mass ratio: polyamide 660%, glass fiber 33%, compatibilizer 2%, paint film agent 2%, toughening agent 1%, antioxidant 0.3 %, nucleating agent 0.4%, coupling agent 0.3% and anti-floating fiber agent 1%.

[0048] The selection of polyamide 6, glass fiber, compatibilizer, paint film agent, toughening agent, antioxidant, nucleating agent, coupling agent and the same as the first embodiment.

[0049] The steps for manufacturing the above-mentioned nylon material are the same as in Example 1, and the screw speed is 360 rpm.

[0050] The temperature of the screw section is as follows: the temperature of the first zone is 225°C, the temperature of the second zone is 230°C, the temperature of the third zone is 235°C, the temperature of the fourth zone is 240°C, the temperature of the fifth zone is 240°C, the temperature of the sixth zone is 245°C, and the temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a reinforced nylon material without floating fiber, which is prepared from the following raw materials in percentage by weight: 42% of polyamide 6, 15% of polyamide 66, 34% of glass fiber, 1% of compatibilizer, 2% of film painting agent, 3% of toughening agent, 0.3% of antioxidant, 0.4% of nucleating agent, 0.3% of coupling agent and 2% of floating fiber resisting agent. The invention also discloses a preparation method of nylon material, which comprises the steps of drying the polyamide 6 and the polyamide 66, throwing the raw materials into a high-speed mixer for high-speed mixing, then throwing the mixed the raw materials into a double-screw extruder, and finally granulating and packaging to obtain the product via melting, mixing, extruding, cooling and drying sequentially. The high-performance reinforced nylon material without floating fiber has the characteristics of high rigidity, high toughness, high liquidity, high heat resistance, no floating fiber and the like.

Description

technical field [0001] The invention relates to a non-floating fiber reinforced nylon material and a manufacturing method thereof. Background technique [0002] Because nylon has many characteristics, it is widely used in automobiles, electrical equipment, mechanical parts, transportation equipment, textiles, papermaking machinery, communication supplies, etc. [0003] With the miniaturization of automobiles, the high performance of electronic and electrical equipment, and the acceleration of the lightweight of mechanical equipment, the demand for nylon will be higher and greater. In particular, as a structural material, nylon has high requirements for its strength, heat resistance, and cold resistance. However, the mechanical strength and heat resistance of nylon itself are not very high, and it is difficult to meet the requirements for use as a structural member. Therefore, it is necessary to modify nylon to improve its performance and expand its application field. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08L51/06C08K13/04C08K7/14C08K5/18C08K5/098C08K5/544B29C47/92B29C48/40B29C48/92
CPCB29C48/04B29C48/40
Inventor 张金柱邹仕放韩丽燕
Owner SUZHOU TAIKAN MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com