A technology of waterproof coating and polyurea, applied in the direction of polyurea/polyurethane coating, coating, etc., can solve the problem of low strength of scraping polyurea, and achieve the effect of excellent waterproof performance and excellent mechanical and mechanical properties of the coating
Active Publication Date: 2010-09-01
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD +2
View PDF0 Cites 19 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The scratch-coated polyurea currently on the market has low strength and has
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0022] Example 1:
[0023] 207g polyether glycol and 80g plasticizer were added to a 500mL four-necked reaction flask, heated to 100℃~120℃, vacuum dehydrated for 4h, cooled below 50℃, added 224g diisocyanate, heated slowly, controlled temperature 80 ~85℃, react for 2.5h under vacuum condition, cool down by 50~60℃, add defoamer, stir for 30min, discharge and seal to obtain component A.
[0024] 290g polyether triol was added to a 500mL four-necked reaction flask, heated to 80℃, added 4.5g of titanium dioxide, added 90g of chain extender, stirred well, heated to 100℃~120℃, vacuum dehydrated for 4h, cooled by 50 ~60℃, add 1.5g dibutyltin dilaurate, 0.3g defoamer, 2.3g ultraviolet absorber, 0.2g dispersant, 0.2g anti-separation auxiliary agent and stir for 10min, then add 13.5g molecular sieve water absorbent, stir 20min, add the color paste, mix evenly and then discharge, then B component is obtained. The A and B components are mixed to obtain the waterproof coating of the present i...
Example Embodiment
[0025] Example 2:
[0026] The A component is in accordance with Example 1. The amount of chain extender in component B is 110g.
Example Embodiment
[0027] Example 3:
[0028] The A component is in accordance with Example 1. The amount of chain extender in component B is 130 g.
[0029] Performance Testing:
[0030] The scratch-coated polyurea prepared above was tested for some physical and mechanical properties under specified conditions according to the test method for building waterproof materials GB / T 16777-1997. Table 1 lists some basic performance test results of the knife-coated polyurea.
[0031] Table 1 Performance test results of scratch-coated polyurea waterproof coating
[0032] Performance
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a knife coating type polyurea waterproof coating comprising a main agent and a curing agent with the mass ratio of 1.0-1.5:1, wherein the main agent is an end NCO-based prepolymer obtained by reacting polyether polyol subjected to vacuum dehydration with polyisocyanate and contains 30-40 percent by weight of polyether glycol and 30-45 percent by weight of diisocyanate, the curing agent is formed by mixing an active hydride, a plasticizer and inorganic fillers subjected to vacuum dehydration with a catalyst, a defoamer and a dispersant disperser and contains 70-95 percent by weight of active substances. The knife coating type polyurea waterproof coating has the solid content of 100 percent, has the advantages of tastelessness, nontoxicity and no pollution in the construction process, and is not influenced by environmental dampness and moisture. A formed film layer has the advantages of excellent mechanical property and weatherability as well as favorable high-low temperature resistance, solvent resistance and corrosion resistance and has favorable bond property with materials such as cement products, steel products, wood products, glass fiber products, and the like.
Description
Technical field: [0001] The invention relates to the field of architectural coatings, in particular to a scraping type polyurea waterproof coating and a construction method thereof. Background technique: [0002] Polyurea elastomer is a newest type developed to meet the needs of long-term protection of the surface of concrete, steel structures and their components after the mature application of advanced technologies such as high-solid coatings and light-curing (UV) coatings. protective material. In the mid-1980s, the United States and Europe took the lead in developing and popularizing it on a large scale. After achieving great success, the technology has been rapidly promoted and developed at home and abroad. [0003] In the mid-1980s, Mr. Dudley J Primeaux of the American Texaco Company took the lead in developing the spray polyurea elastomer (SPUA for short), thus fundamentally solving the major technical problems that plagued the construction industry. In 1991, this t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): C09D175/02C09D5/00C09D7/12
Inventor 田凤兰段文锋孙金梅杨红艳王新锋
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Login to view more 
Login to view more