High shock-resistant, wear-resistant sport shoe sole material and manufacturing method thereof
A technology of sole material and manufacturing method, applied in the direction of sole, footwear, application, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0039] Example 1:
[0040] The composition (mass ratio) is: BIIR 100 parts, white carbon black 50 parts, PEG 5.0 parts, paraffin oil 5.0 parts, sulfur 2.0 parts, magnesium oxide (MgO) 8.0 parts, DM 1.5 parts, M 0.5 parts, TMTM 0.5 parts, 4.0 parts of zinc oxide and 1.0 part of zinc stearate.
[0041] Weigh the material according to the above-mentioned ratio, mix according to the above-mentioned process, and measure the engineering positive vulcanization time of the mixed rubber by a rotorless rheometer at 150℃ t 90 Is 1127s. Then it is compression molded at 150°C. Place the sample at room temperature 22.0℃ for more than 24h to test its hardness (ShoreA) 59, the relative density is 1.19g / cm 3 ; According to the QB / T2884-2007 standard test DIN abrasion of 246mm 3 ; According to GB1040 standard test tensile strength 13.1MPa, elongation at break 743%; according to GB / T 3903.12-2005 standard test right angle tear strength 35N / mm. The dynamic viscoelasticity test shows that the materia...
Example Embodiment
[0042] Example 2:
[0043] The composition (mass ratio) is: BR 100 parts, white carbon black 50 parts, DEG 1.5 parts, PEG 3.0 parts, coupling agent Si-693.0 parts, naphthenic oil 5.0 parts, sulfur 1.5 parts, NS 0.9 parts, oxidation Zinc 3.0 parts, zinc stearate 2.0 parts, tackifier 1.0 part, antioxidant RD 1.0 part, antioxidant 40201.0 part, microcrystalline wax 1.0 part.
[0044] Weigh the material according to the above-mentioned ratio, mix according to the above-mentioned process, and measure the engineering positive vulcanization time of the mixed rubber by a rotorless rheometer at 150℃ t 90 It is 1461s. Then it is compression molded at 150°C. Place the sample at room temperature 22.0℃ for more than 24h to test its hardness (ShoreA) of 65 and relative density of 1.15g / cm 3 ; According to the QB / T2884-2007 standard, its DIN abrasion is 52mm 3 ; According to GB 1040 standard test tensile strength 11.8MPa, elongation at break 692%; according to GB / T 3903.12-2005 standard test rig...
Example Embodiment
[0045] Example 3:
[0046] The composition (mass ratio) is: BIIR 70 parts, BR 30 parts, white carbon black 50 parts, PEG 4.5 parts, coupling agent Si-750.9 parts, sulfur 1.85 parts, NS 0.3 parts, TMTM 0.35 parts, zinc oxide 3.6 parts, 5.6 parts of magnesium oxide, 1.3 parts of zinc stearate, 0.5 parts of tackifier, 0.5 parts of antioxidant 4010A, 0.5 parts of microcrystalline wax.
[0047] Weigh the material according to the above-mentioned proportion and mix according to the above-mentioned process. The engineering positive vulcanization time of the rubber mixture measured by a rotorless rheometer is 694s at 150℃. Then it is compression molded at 150°C. Place the sample at room temperature 22.0℃ for more than 24h to test its hardness (ShoreA) of 63 and relative density of 1.17g / cm 3 ; According to the QB / T2884-2007 standard, its DIN abrasion is 273mm 3 ; According to GB1040 standard test tensile strength 13.4MPa, elongation at break 673%; according to GB / T 3903.12-2005 standard t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap