Corrosion resistance coating for steel and preparation method thereof

A coating and anti-corrosion technology, which is applied in the field of anti-corrosion coatings for steel and its preparation, can solve the problems of complex coating process configuration, and achieve the effects of improving heat dissipation function, improving activity and good thermal conductivity.

Inactive Publication Date: 2010-11-24
NANJING UNIV OF INFORMATION SCI & TECH
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating process configuration of the above invention is too complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion resistance coating for steel and preparation method thereof
  • Corrosion resistance coating for steel and preparation method thereof
  • Corrosion resistance coating for steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation process of corrosion-resistant paint for steel of the present invention is as follows:

[0025] Preparation of alloy powder: according to weight percentage: Zn is 35%, Mn is 0.01%, Cd is 0.2%, Sr is 0.2%, Si is 0.02%, Pr is 0.03%, Gd is 0.05%, and the rest is Al For batching, pure metal ingots are used for Zn and Al, pure cadmium grains are used for Cd, pure manganese flakes are used for Mn, silicon blocks are used for Si, and Pr, Gd, and Sr are all added in the form of master alloys, respectively with Pr15% The praseodymium-aluminum master alloy, the gadolinium-aluminum master alloy containing Gd15% and the strontium-aluminum master alloy containing Sr25%; put the raw materials into a crucible with a bottom hole with an external induction coil, the diameter of the bottom hole is 1-2mm, and the bottom hole of the crucible The lower part is equipped with a rotating molybdenum alloy runner, and the upper part of the crucible is connected to a nitrogen pres...

Embodiment 2

[0028] Preparation of alloy powder: The weight percentage of the chemical composition of alloy powder is: Zn is 40%, Mn is 0.1%, Cd is 0.4%, Sr is 0.4%, Si is 0.05%, Pr is 0.09%, Gd is 0.2% %, the rest is Al.

[0029] The percentage by weight of each component in the paint preparation is: 45% alloy powder, 3.0% boron nitride powder, 3% silicon carbide powder, 7.0% butanol, and the rest is epoxy resin liquid;

[0030] The preparation process is the same as in Example 1.

Embodiment 3

[0032] Preparation of alloy powder: The weight percentage of the chemical composition of the alloy powder is: 37% for Zn, 0.09% for Mn, 0.3% for Cd, 0.3% for Sr, 0.03% for Si, 0.06% for Pr, and 0.09% for Gd %, the rest is Al.

[0033]The percentage by weight of each component in the paint preparation is: 42.5% alloy powder, 4% boron nitride powder, 4% silicon carbide powder, 7.5% butanol, and the rest is epoxy resin liquid;

[0034] The preparation process is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a corrosion resistance coating for steel and a preparation method thereof. The coating has the advantages of excellent performance and good wear resistance. The preparation method has the advantages of simple process and low production cost and is suitable for industrial production. The corrosion resistance coating for steel comprises the following compositions in percentage by weight: 40-45 percent of alloy powder, 3.0-6.0 percent of boron nitride powder, 3-6 percent of silicon carbide powder, 7.0-8.0 percent of butanol powder and the balance of epoxy resin liquid, wherein the particle size of the alloy powder, the particle size of the boron nitride powder and the particle size of the silicon carbide powder are all 270-800 meshes. The alloy powder comprises the following compositions in percentage by weight: 35-40 percent of Zn, 0.01-0.1 percent of Mn, 0.2-0.4 percent of Cd, 0.2-0.4 percent of Sr, 0.02-0.05 percent of Si, 0.03-0.09 percent of Prm 0.05-0.2 percent of Gd and the balance of Al.

Description

1. Technical field [0001] The invention belongs to the field of metal materials, and relates to a corrosion-resistant coating for steel and a preparation method thereof. 2. Technical Background [0002] At present, in the field of coating materials, the corrosion protection of steel has been paid attention to. [0003] Application No. CN200710113712.4 discloses a corrosion-resistant and wear-resistant powder coating, which is composed of a base material, a filler and a coupling agent. The base material is selected from thermoplastic polyamide resin, and the filler is carbon fiber and molybdenum disulfide. In order to disperse evenly and improve the compatibility between the filler and the base material, this invention also adds a small amount of γ-glycidyl ether propyl trimethoxysilane as a coupling agent. The preparation method of anti-corrosion and wear-resistant powder coating, weighing 100 parts of thermoplastic polyamide resin, 0.2-1 part of carbon fiber, 1-3 parts of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/14C04B14/34
Inventor 赵浩峰王玲张禄
Owner NANJING UNIV OF INFORMATION SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap