Low-hydrogen alkaline welding rod for 25Cr2Ni4MoV alloy steel manual arc welding

A basic welding rod and manual arc technology, applied in welding medium, welding equipment, metal processing equipment, etc., can solve the problems of lack of welding rods, etc., and achieve the effect of good fluidity of molten pool, fine spatter particles and good arc stability

Active Publication Date: 2010-12-01
SERVICE CENT OF COMMLIZATION OF RES FINDINGS HAIAN COUNTY
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a low-hydrogen alkaline electrode for manual arc welding of 25Cr2N...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-hydrogen alkaline welding rod for 25Cr2Ni4MoV alloy steel manual arc welding
  • Low-hydrogen alkaline welding rod for 25Cr2Ni4MoV alloy steel manual arc welding
  • Low-hydrogen alkaline welding rod for 25Cr2Ni4MoV alloy steel manual arc welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Step 1, making alloy steel welding core

[0033]The preparation weight ratio is 1:1 for professional pure iron and industrial pure iron. Ores containing C, Si, Mo, Cr are placed around and on the upper part of the magnesia crucible in the induction furnace, Ni powder is placed in the middle of the crucible, Re, Mn, B put into the tray. The carbon in the crucible acts as a deoxidizer. Put the pure iron and the contents in the crucible together into the induction furnace for smelting. When the pure iron is completely melted, the temperature of the molten alloy steel reaches 1540°C, and when the molten steel is calm, turn off the power to cool and exhaust for 15 minutes; then turn on the power for refining, and after 20 minutes of refining , When the temperature of the alloy steel liquid drops to 1550°C, add Ti powder, and then tap the steel when the temperature continues to drop to the tapping temperature (the tapping temperature is 1540°C). Fill the furnace with argon ...

Embodiment 2

[0043] Step 1, making alloy steel welding core:

[0044] The preparation weight ratio is 1:1 for professional pure iron and industrial pure iron. Ores containing C, Si, Mo, Cr are placed around and on the upper part of the magnesia crucible in the induction furnace, Ni powder is placed in the middle of the crucible, Re, Mn, B put into the tray. The carbon in the crucible acts as a deoxidizer. Put the pure iron and the contents in the crucible together into the induction furnace for smelting. When the pure iron is completely melted, the temperature of the molten alloy steel reaches 1540°C, and when the molten steel is calm, turn off the power to cool and exhaust for 15 minutes; then turn on the power for refining, and after 20 minutes of refining , When the temperature of the alloy steel liquid drops to 1550°C, add Ti powder, and then tap the steel when the temperature continues to drop to the tapping temperature (the tapping temperature is 1540°C). Fill the furnace with argo...

Embodiment 3

[0053] Step 1, making alloy steel welding core:

[0054] Prepare professional pure iron and industrial pure iron with a weight ratio of 1:1, put ores containing C, Si, Mo, Cr around and on the upper part of the magnesia crucible in the induction furnace, Ni powder in the middle of the crucible, Re, Mn, B Put in the pan. The carbon in the crucible acts as a deoxidizer. Put the pure iron and the contents in the crucible together into the induction furnace for smelting. When the pure iron is completely melted, the temperature of the molten alloy steel reaches 1540°C, and when the molten steel is calm, turn off the power to cool and exhaust for 15 minutes; then turn on the power for refining, and after 20 minutes of refining , When the temperature of the alloy steel liquid drops to 1550°C, add Ti powder, and then tap the steel when the temperature continues to drop to the tapping temperature (the tapping temperature is 1540°C). Fill the furnace with argon 5 minutes before tappin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a low-hydrogen alkaline welding rod for 25Cr2Ni4MoV alloy steel manual arc welding, comprising a core wire and a coating, wherein the core wire is composed of the following components by weight percent: 0.030-0.070% of C, 0.10-0.50% of Si, 1.0-2.0% of Mn, 3.0-5.0% of Ni, 0.10-0.50% of Mo, 0.50-2.0% of Cr, 0.10-0.30% of Ti, 0.002-0.009% of B, 0.10-0.30% of Re, less than 0.005% of S, less than 0.005% of P and the balance of Fe, and the total weight of all components is 100%. The welding rod prepared by the invention has favorable arc stabilizing performance, good weld pool flowability, fine droplet spatters, easy slag detachability after welding, evenly covered slag, delicate and beautiful moulded welding line and controllable content of deposited metals of welding rod diffusible hydrogen.

Description

technical field [0001] The invention belongs to the technical field of welding in material processing, and in particular relates to a low-hydrogen alkaline electrode for manual arc welding of 25Cr2Ni4MoV alloy steel. Background technique [0002] In recent years, the use of large-scale fans in my country's industry has become more and more widely used, and the working conditions have become more and more complicated. In order to improve the overall quality of the fan, the blade material of the core part of the fan is required to have good comprehensive mechanical properties such as high strength, toughness and hardness. . 25Cr2Ni4MoV steel is the steel used for relatively large generator rotors in my country at present. It has the advantages of high strength, high plasticity and toughness, and low brittle transition temperature. In industrial applications, through quenching and tempering (quenching + high temperature tempering) to obtain excellent strength and toughness matc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/30B23K35/365
Inventor 张敏李岩李继红
Owner SERVICE CENT OF COMMLIZATION OF RES FINDINGS HAIAN COUNTY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap