Castor oil modified polyurethane adhesive combination for artificial turf gum
A technology of polyurethane adhesive and artificial turf, applied in the direction of polyurea/polyurethane adhesive, adhesive, adhesive type, etc., can solve the problems of high cost of raw materials, difficult processing, unenvironmental protection, etc., to improve compatibility and cost. Low, improve the effect of bonding
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example 1
[0036] Preparation of the polyurethane adhesive composition for the bottom and back of artificial turf: at room temperature, 100g of modified nano-inorganic fillers were dispersed in 90g of castor oil by means of superoscillation and mechanical stirring to obtain their mixed solution, and 10g of them were quickly reduced to two Ethylene glycol, 2g of nickel diacetylacetonate, 1g of fumed silica, 1g of anionic surfactant and 1g of pigment are put into a stirring tank, and stirred rapidly with a high-speed disperser for 3 minutes at a speed of 500 rpm ; Then add 64.3g of diphenylmethane diisocyanate, stir rapidly for 1 minute to make it evenly mixed, and the viscosity is 5000mPa·s. Use the polyurethane adhesive of the present invention to coat the bottom back of artificial turf, so that its glue amount is 800g / m 2 , then heat-cured at 100°C for 3 minutes, and then left to stand at room temperature for 24 hours. According to the ISO4919 standard, use the univ...
Example Embodiment
[0037] Embodiment 2
[0038] Preparation of the polyurethane adhesive composition for the bottom and back of artificial turf: at room temperature, 200g of modified nano-inorganic fillers were dispersed in 90g of castor oil by supersonic vibration and mechanical stirring to obtain their mixed solution, and 10g of them were quickly reduced to two Ethylene glycol, 2g of nickel diacetylacetonate, 1g of fumed silica, 1g of anionic surfactant and 1g of pigment are put into a stirring tank, and stirred rapidly with a high-speed disperser for 3 minutes at a speed of 500 rpm ; Then add 64.5g of diphenylmethane diisocyanate, stir rapidly for 1 minute to make it evenly mixed, and the viscosity is 12000mPa·s. Use the polyurethane adhesive of the present invention to coat the bottom back of artificial turf, so that its glue amount is 800g / m 2 , then heat-cured at 100°C for 35 minutes, and then left to stand at room temperature for 24 hours. According to the ISO4919 standard, use the univ...
Example Embodiment
[0039] Embodiment 3
[0040] Preparation of the polyurethane adhesive composition for the bottom and back of artificial turf: at room temperature, 200g of modified nano-inorganic fillers were dispersed in 90g of castor oil by supersonic vibration and mechanical stirring to obtain their mixed solution, and 10g of them were quickly reduced to two Ethylene glycol, 2g of nickel diacetylacetonate, 1g of fumed silica, 1g of anionic surfactant and 1g of pigment are put into a stirring tank, and stirred rapidly with a high-speed disperser for 3 minutes at a speed of 500 rpm ; Then add 64.5g of diphenylmethane diisocyanate, stir rapidly for 1 minute to make it evenly mixed, and the viscosity is 12000mPa·s. Use the polyurethane adhesive of the present invention to coat the bottom back of artificial turf, so that its glue amount is 600g / m 2 , then heat-cured at 100°C for 35 minutes, and then left to stand at room temperature for 24 hours. According to the ISO4919 standard, use the univ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap