Scrap rubber powder/vegetable fiber composite foaming material and preparation process thereof

A plant fiber and composite foaming technology, which is applied in the field of waste rubber powder/plant fiber composite foaming material and its preparation, can solve the problems of rubber powder product backlog, little change, and less waste rubber powder application technology, and achieve High elasticity, high strength effect

Inactive Publication Date: 2011-01-19
HUNAN UNIV OF TECH
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the degree of change in this situation is actually not great. One of the very important reasons is that there are few mature application technologies for waste rubber powder, resulting in a backlog of rubber powder products and poor sales.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scrap rubber powder/vegetable fiber composite foaming material and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The present invention will be described in further detail below in conjunction with the embodiments.

[0030] Table 1 lists the formulations of four examples of the waste rubber powder / plant fiber composite foam material of the present invention.

[0031] Preparation: (1) The waste rubber powder and N-(ethyl-methyl-ethyl-nitro)-4-nitrosoaniline equivalent to 5% by weight of the waste rubber powder are placed in a high mixer and mixed evenly, and set aside for use (2) The solution of silane coupling agent KH550 equivalent to 2% of the weight of the plant fiber is sprayed on the surface of the plant fiber, and dried for use; (3) The waste rubber powder processed by step (1), the waste rubber powder processed by step (2) The treated plant fibers are mixed uniformly with high-density polyethylene, benzoyl peroxide, maleic anhydride grafted polyethylene, azodicarbonamide, polyethylene wax and antioxidant 168 in a high-mixer; (4) the The mixed material obtained in step (3) i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a scrap rubber powder/vegetable fiber composite foaming material and a preparation process thereof. The scrap rubber powder/vegetable fiber composite foaming material is prepared from the following components in part by weight: 80 to 120 parts of scrap rubber powder, 80 to 120 parts of vegetable fibers, 20 to 50 parts of high density polyethylene, 2 to 3 parts of benzoyl peroxide, 5 to 20 parts of maleic anhydride grafted polyethylene, 5 to 15 parts of azodicarbonamide, 10 to 30 parts of lubricating agent and 1 to 5 parts of heat stabilizer. The product can be granulated by dynamic extrusion and foamed by die pressing and has a simple preparation process, high cost performance and low cost. The scrap rubber powder/vegetable fiber composite foaming material can be used for manufacturing mute floors, floor tiles, buffer shockproof packaging materials such as inside linear, and the like.

Description

technical field [0001] The invention relates to a waste rubber powder / plant fiber composite foaming material and a preparation process thereof. Background technique [0002] In recent years, oil prices have soared, affecting the increase in synthetic rubber production; while natural rubber production has also stagnated. With the development of the automobile industry, my country has become the largest country in the world in terms of rubber consumption. About 45% of the annual rubber consumption needs to be imported, resulting in the soaring price of raw rubber. [0003] At the same time, waste rubber is increasingly polluting the environment. In 2007, more than 170 million tires were scrapped in my country. Nearly one million tons of waste rubber are not used rationally every year. This is mainly because the way of recycling waste rubber in my country is relatively simple, the recovery rate is very low, and the production of reclaimed rubber is mainly used, supplemented ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L21/00C08L97/02C08L23/06C08L51/06C08K5/14C08K5/23
Inventor 曾广胜许超刘跃军
Owner HUNAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap