Fiber-reinforced resin heat-resistant high-speed abrasive cutting wheel and processing method thereof

A fiber-reinforced resin and cutting grinding wheel technology, which is applied in the field of grinding wheels, can solve the problems of poor wear resistance, small cutting ratio, and poor heat resistance, and achieve good wear resistance, high cutting ratio, and good heat resistance.

Active Publication Date: 2011-02-09
山东鲁信四砂泰山磨具有限公司
View PDF0 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the defects of small cutting ratio caused by the fiber reinforced resin grinding wheel with large diameter and sheet structure in the prior art due to poor heat resistanc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-reinforced resin heat-resistant high-speed abrasive cutting wheel and processing method thereof
  • Fiber-reinforced resin heat-resistant high-speed abrasive cutting wheel and processing method thereof
  • Fiber-reinforced resin heat-resistant high-speed abrasive cutting wheel and processing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] The grinding wheel of the present invention includes a central reinforcement part and a cutting use part, and the weight parts of each component of the central reinforcement part are:

[0039] A24# 25 copies

[0040] A36# 65 copies

[0041] A150# 10 copies

[0042] 8 parts of phenolic resin powder

[0043] Phenolic resin wetting agent 4.5 parts

[0044] Silane coupling agent: 0.3 parts

[0045] Hemihydrate gypsum powder: 3.5 parts.

[0046] The weight fraction of each component of the cutting part is:

[0047] ZA16# 18 copies

[0048] ZA20# 12 copies

[0049] A20# 30 copies

[0050] A24# 25 copies

[0051] A36# 15 copies

[0052] Phenolic resin powder 12 parts

[0053] Phenolic resin wetting agent 6.5 parts

[0054] Iron disulfide powder 4.8 parts

[0055] Cryolite powder 4.5 parts

[0056] Ferrous oxide powder 1.2 parts

[0057] Titanium dioxide fine powder 0.8 parts

[0058] Silane coupling agent 0.6 parts

[0059] The present invention is made as figure 1 , figure 2 The pr...

Example Embodiment

[0064] Example 2

[0065] The grinding wheel of the present invention includes a central reinforcement part and a cutting use part, and the weight parts of each component of the central reinforcement part are:

[0066] A24# 30 copies

[0067] A36# 60 copies

[0068] A150# 10 copies

[0069] 8.5 parts of phenolic resin powder

[0070] Phenolic resin wetting agent 4.5 parts

[0071] Silane coupling agent: 0.4 parts

[0072] Hemihydrate gypsum powder: 4 parts.

[0073] The weight fraction of each component of the cutting part is:

[0074] ZA16# 25 copies

[0075] ZA20# 20 copies

[0076] A20# 20 copies

[0077] A24# 30 copies

[0078] A36# 5 copies

[0079] 10 parts of phenolic resin powder

[0080] Phenolic resin wetting agent 5.8 parts

[0081] Iron disulfide powder 5 parts

[0082] 5 parts of cryolite powder

[0083] Ferrous oxide powder 1 part

[0084] Titanium dioxide fine powder 0.8 parts

[0085] Silane coupling agent 0.4 parts

[0086] The main points of the process in this embodiment are the same ...

Example Embodiment

[0088] Example 3

[0089] The grinding wheel of the present invention includes a central reinforcement part and a cutting use part, and the weight parts of each component of the central reinforcement part are:

[0090] A24# 35 copies

[0091] A36# 55 copies

[0092] A150# 10 copies

[0093] 9 parts of phenolic resin powder

[0094] Phenolic resin wetting agent 5 parts

[0095] Silane coupling agent: 0.3 parts

[0096] Hemihydrate gypsum powder: 4.3 parts.

[0097] The weight fraction of each component of the cutting part is:

[0098] ZA16# 20 copies

[0099] ZA20# 15 copies

[0100] A20# 25 copies

[0101] A24# 25 copies

[0102] A36# 15 copies

[0103] 9 parts of phenolic resin powder

[0104] Phenolic resin wetting agent 6 parts

[0105] 6 parts of iron disulfide powder

[0106] 4 parts cryolite powder

[0107] 2 parts of ferrous oxide powder

[0108] Titanium dioxide fine powder 1 part

[0109] Silane coupling agent 0.3 parts

[0110] The main points of the process in this embodiment are the same as ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of abrasive wheels, and in particular relates to a fiber-reinforced resin heat-resistant high-speed abrasive cutting wheel with a large diameter and a flake structure and a processing method thereof. In the invention, the abrasive wheel is divided into a center reinforced part and a cutting part which adopt different formulas, wherein the formula of the center reinforced part has the advantages of high strength and good cohesiveness with a fiber glass reinforced net, and because the center reinforced part does not use zirconia alumina and other materials with a relatively higher price, the cost is saved. By adding iron sulfide powder, cryolite powder and titanium dioxide fine powder to the cutting part, and optimizing the respective proportion, the heat resistance and wear resistance of the cutting part are enhanced and the cutting ratio is improved. The abrasive wheel of the invention has the advantages of good heat-resistant property, good wear-resistant property, high cutting ratio and low cost.

Description

technical field [0001] The invention belongs to the field of grinding wheels, and in particular relates to a fiber-reinforced resin heat-resistant high-speed cutting grinding wheel with a large diameter and a sheet structure and a processing method thereof. Background technique [0002] Fiber-reinforced resin grinding wheel is a type of grinding wheel that uses phenolic resin as a binder for cutting and rough grinding. It has the advantages of high strength, not easy to break, and high removal rate. However, when cutting the shaped round steel, square steel and other steel products just out of the smelting furnace, the cutting wheel with large diameter and thin slice structure is prone to defects such as poor high temperature resistance, high consumption of the grinding wheel and small cutting ratio due to the high temperature of the steel. Even cause the fragmentation of emery wheel, have had a strong impact on the application of resin cutting emery wheel in hot-rolled ste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D18/00B24D3/28
Inventor 刘泉玺翟涵
Owner 山东鲁信四砂泰山磨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap